Investigation on the Effect of Lead (Pb) on the Degradation Behavior of Passive Films on Alloy 800

  • J. UlaganathanEmail author
  • H. Ha
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

Alloy 800 has been demonstrated to be susceptible to Pb-induced degradation such as stress corrosion cracking (SCC) in laboratory experiments. Pb has been proposed to cause such degradation by affecting the formation of protective oxides comprising the passive films on the alloys. To understand the detrimental effects of Pb, Alloy 800 samples pre-passivated under all volatile treatment (AVT) conditions were exposed to alkaline environment of pH280 °C 9.5 at 280 °C in the absence and presence of Pb. The Pb-free and Pb-containing passivated surfaces, along with bare surfaces as control samples, were characterized using electrochemical and surface analytical techniques. The results contrast the susceptibility of Alloy 800 to Pb-induced degradation reported in literature, where experiments are usually performed on bare surfaces with excess Pb, typically as PbO, present in the aqueous solutions; suggesting that the effect of Pb depends on whether it is present in solution or incorporated in the film.

Keywords

Alloy 800 Passive film Pb Cyclic polarization Mott-schottky analysis Atom probe tomography 

Notes

Acknowledgements

Many thanks are due to colleagues at CNL, especially A. Audet and H. Chaudhry for performing the room temperature and high temperature electrochemical measurements; C. Mayhew, H. Rudzinski, and B. Payne for the AES and XPS characterization; and J. Smith for review and technical discussion. APT was performed and analyzed by B. Langelier at the Canadian Center for Electron Microscopy, Hamilton.

References

  1. 1.
    R.L. Tapping, Materials Performance in CANDU Reactors: The First 30 years and the Prognosis for Life Extension and New Designs. J. Nucl. Mater. 383, 1–8 (2008)CrossRefGoogle Scholar
  2. 2.
    D. Gόmez Briceño, M.L. Castaño, M.S. Garcίa, Stress Corrosion Cracking Susceptibility of Steam Generator Tube Materials in AVT (All Volatile Treatment) Chemistry Contaminated with Lead. Nucl. Eng. Des. 165, 161–169 (1996)CrossRefGoogle Scholar
  3. 3.
    H. Takamatsu, T. Matsunaga, B.P. Miglin, J.M. Sarver, P.A. Sherburne, K. Aoki, and T. Sakai, Study on Lead-Induced Stress Corrosion Cracking of Steam Generator Tubing under AVT Water Chemistry Conditions, Proceedings of the Eleventh International Conference on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, American Nuclear Society (ANS), 1997, pp. 216–223Google Scholar
  4. 4.
    B. Capell, R. Wolfe, R. Eaker, J. Lumsden, PbSCC of Alloy 800NG Steam Generator Tubing in Alkaline Conditions, Proceeding of the Seventeenth International Conference on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, Canadian Nuclear Society (CNS), 2016, pp. 713–727Google Scholar
  5. 5.
    C. Marks, C. Anderson, “Steam Generator Management Program: Steam Generator Deposit Characterization for Steam Generator Tube Degradation Prediction and Management”, Technical Report 1018249, Electric Power Research Institute (EPRI), (2008 December)Google Scholar
  6. 6.
    B. Stellwag, The Mechanism of Oxide Film Formation on Austenitic Stainless Steels in High Temperature Water. Corros. Sci. 40(2–3), 337–370 (1998)CrossRefGoogle Scholar
  7. 7.
    B. Beverskog, I. Puigdomenech, Pourbaix Diagrams for the Ternary System of Iron-chromium-nickel. Corrosion 55(11), 1077–1087 (1999)CrossRefGoogle Scholar
  8. 8.
    R.J. Lemire, G.A. McRae, The Corrosion of Alloy 690 in High-temperature Aqueous Media—thermodynamic Considerations. J. Nucl. Mater. 294(1–2), 141–147 (2001)CrossRefGoogle Scholar
  9. 9.
    B.T. Lu, J.L. Luo, Y.C. Lu, Passivity Degradation of Nuclear Steam Generator Tubing Alloy Induced by Pb Contamination at High Temperature. J. Nucl. Mater. 429(1–3), 305–314 (2012)CrossRefGoogle Scholar
  10. 10.
    B.T. Lu, J.L. Luo, Y.C. Lu, Effects of pH on Lead-induced Passivity Degradation of Nuclear Steam Generator Tubing Alloy in High Temperature Crevice Chemistries. Electrochim. Acta 87(1), 824–838 (2013)CrossRefGoogle Scholar
  11. 11.
    S.-I. Pyun, C. Lim, R.A. Oriani, The Role of Hydrogen in the Pitting of Passivating Films on Pure Iron. Corros. Sci. 33(3), 437–444 (1992)CrossRefGoogle Scholar
  12. 12.
    J.G. Yu, C.S. Zhang, J.L. Luo, P.R. Norton, Investigation of the Effect of Hydrogen on the Passive Film on Iron by Surface Analysis Techniques. J. Electrochem. Soc. 150(2), B68–B75 (2003)CrossRefGoogle Scholar
  13. 13.
    S.R. Morrison, Electrochemistry at Semiconductor and Oxidized Metal Electrodes (Plenum Press, New York, USA, 1980)CrossRefGoogle Scholar
  14. 14.
    M. Bojinov, G. Fabricius, T. Laitinen, K. Mäkelä, T. Saario, G. Sundholm, Coupling between Ionic Defect Structure and Electronic Conduction in Passive Films on Iron, Chromium and Iron-Chromium Alloys. Electrochim. Acta 45(13), 2029–2048 (2000)CrossRefGoogle Scholar
  15. 15.
    N.E. Hakiki, M. Da Cunha Belo, A.M.P. Simões, M.G.S. Ferreira, Semiconducting Properties of Passive Films Formed on Stainless Steels—Influence of the Alloying Elements. J. Electrochem. Soc. 145(11), 3821–3829 (1998)CrossRefGoogle Scholar
  16. 16.
    M. Da Cunha Belo, N.E. Hakiki, M.G.S. Ferreira, Semiconducting Properties of Passive Films Formed on Nickel-base Alloys Type Alloy 600: Influence of the Alloying Elements. Electrochim. Acta 44(14), 2473–2481 (1999)CrossRefGoogle Scholar
  17. 17.
    N. Fairley, Casa Software Ltd., 1999–2011Google Scholar
  18. 18.
    D. Costa, H. Talah, P. Marcus, M. Le Calvar, and A. Gelpi, Interaction of Lead with Nickel-base Alloys 600 and 690, Proceedings of the Seventh International Conference on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, NACE, (1995) pp. 199–208Google Scholar
  19. 19.
    H. Radhakrishnan, A.G. Carcea, R.C. Newman, Influence of Pb2+ Ions on the Dissolution and Passivation of Nickel and Ni-21Cr in Acidic Solutions. Corros. Sci. 47(12), 3234–3248 (2005)CrossRefGoogle Scholar
  20. 20.
    R.W. Staehle, “Assessment of and Proposal for a Mechanistic Interpretation of High Nickel Alloys in Lead-Containing Environments”, Proceedings of the Eleventh International Conference on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, American Nuclear Society, 2004, pp. 381–424Google Scholar
  21. 21.
    R.W. Staehle, “Clues and Issues in the SCC of High Nickel Alloys Associated with Dissolved Lead”, Proceedings of the Twelfth International Conference on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, NACE, 2005, pp. 1163–1210Google Scholar
  22. 22.
    D.H. Xia, Y. Behnamian, H.N. Feng, H.Q. Fan, L.X. Yang, C. Shen, J.L. Luo, Y.C. Lu, S. Klimas, Semiconductivity Conversion of Alloy 800 in Sulphate, Thiosulphate, and Chloride Solutions. Corros. Sci. 87, 265–277 (2014)CrossRefGoogle Scholar
  23. 23.
    D.H. Xia, Y. Behnamian, L. Yang, H.Q. Fan, R.K. Zhu, J.L. Luo, Y.C. Lu, S. Klimas, Semiconductivity of Steam Generator Tubing Alloys in Simulated Crevice Chemistries Containing Lead and Sulphur. Corros. Eng., Sci. Technol. 51(1), 37–50 (2016)CrossRefGoogle Scholar
  24. 24.
    A. Seyeux, V. Maurice, P. Marcus, Oxide Film Growth Kinetics on Metals and Alloys—I. Physical Model. J. Electrochem. Soc. 160(6), C189–C196 (2013)CrossRefGoogle Scholar
  25. 25.
    M.C. Biesinger, B.P. Payne, A.P. Grosvenor, L.W.M. Lau, A.R. Gerson, R.S.C. Smart, Resolving Surface Chemical States in XPS Analysis of First Row Transition Metals, Oxides and Hydroxides: Cr, Mn, Fe, Co and Ni. Appl. Surf. Sci. 257(7), 2717–2730 (2011)CrossRefGoogle Scholar
  26. 26.
    B.P. Payne, M.C. Biesinger, N.S. McIntyre, X-ray Photoelectron Spectroscopy Studies of Reactions on Chromium Metal and Chromium Oxide Surfaces. J. Electron Spectrosc. Relat. Phenom. 184(1–2), 29–37 (2011)CrossRefGoogle Scholar
  27. 27.
    C.D. Wagner, A.V. Naumkin, A. Kraut-Vass, J.W. Allison, C.J. Powell, J.R. Jr. Rumble, NIST Standard Reference Database 20, Version 3.4 (Web Version) (http:/srdata.nist.gov/xps/) 2003Google Scholar
  28. 28.
    E.A. Marquis, B.P. Geiser, T.J. Prosa, D.J. Larson, Evolution of Tip Shape during Field Evaporation of Complex Multilayer Structures. J. Microsc. 241(3), 225–233 (2011)CrossRefGoogle Scholar
  29. 29.
    S.Y. Persaud, J.M. Smith, C.D. Judge, F.Long, A. Korinek, B. Capell, et al., “High Resolution Characterization of Pb-Caustic SCC in Alloy 800”, Manuscript Submitted for Publication, 2017Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.Canadian Nuclear LaboratoriesChalk RiverCanada

Personalised recommendations