Plastic Deformation Processes Accompanying Stress Corrosion Crack Propagation in Irradiated Austenitic Steels

  • M. N. Gussev
  • G. S. Was
  • J. T. Busby
  • K. J. Leonard
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

During stress corrosion crack propagation, stress values in the crack tip vicinity often exceed material yield stress limit. Plastic deformation processes may accompany and influence cracking. Here, stress corrosion crack propagation and deformation mechanisms were investigated using EBSD analysis. The investigated material was 304L Ti-enriched austenitic stainless steel irradiated to 10.4 dpa at 320°C in the BOR-60 fast reactor. Crack growth tests were conducted in a simulated Normal Water Chemistry (NWC) environment in the temperature range 288–320 °C using compact tension specimens. By analyzing crack trajectory and grain structure in the crack vicinity, it was established that grain orientation with respect to the acting stress direction was not a key factor controlling crack propagation. No crystallographic orientation susceptible to cracking was identified. Also, EBSD analysis revealed strong inhomogeneity in plastic strain distribution along the crack path. Most crack-adjacent grains remained virtually strain-free whereas few grains experienced strong plastic strain. These areas were presumed to be “plastic bridges” or “ductile ligaments.”

Keywords

EBSD Stress corrosion cracking Deformation localization Neutron irradiation Austenitic steel 

References

  1. 1.
    K. Fukuya, Current understanding of radiation-induced degradation in light water reactor structural materials. J. Nucl. Sci. Technol. 50, 213–254 (2013)CrossRefGoogle Scholar
  2. 2.
    Z. Jiao, G. Was, Impact of localized deformation on IASCC in austenitic stainless steels. J. Nucl. Mater. 408, 246–256 (2011)CrossRefGoogle Scholar
  3. 3.
    G.S. Was, Y. Ashida, P.L. Andresen, Irradiation-assisted stress corrosion cracking. Corros. Rev. 29, 7–49 (2011)CrossRefGoogle Scholar
  4. 4.
    J. Massoud, P. Dubuisson, P. Scott, V. Chamardine, CIR II program: description of the Boris 6 and 7 experiments in the BOR-60 fast breeder reactor, EPRI Report, vol. 1011787 (2005)Google Scholar
  5. 5.
    P. Scott, Materials reliability program: a review of the cooperative irradiation assisted stress corrosion cracking research program (MRP-98), EPRI Report, vol. 1002807 (2003)Google Scholar
  6. 6.
    M. Ernestova, J. Burda, Crack growth testing of tailored alloys from Boris 6 and 7 irradiations, EPRI Report, vol. 1021235 (2009)Google Scholar
  7. 7.
    A. Jenssen, J. Stjärnsäter, R. Pathania, Crack growth rates of irradiated commercial stainless steels in BWR and PWR environments, in 15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (Wiley Online Library, 2011), pp. 1229–1240Google Scholar
  8. 8.
    S. Van Dyck, IASCC mechanisms-controlling material factors: SCC crack-growth tests on selected Boris-6 tailored heats, Palo Brussels, Belgium: SCK-CEN, (2009)Google Scholar
  9. 9.
    G.S. Was, Y. Ashida, K.J. Stephenson, A. Flick, P.L. Andersen, Identifying mechanisms and mitigation strategies for irradiation assisted stress corrosion cracking of austenitic steels in LWR core components, EPRI Report, vol. 3002003105 (2014)Google Scholar
  10. 10.
    Y. Ashida, A. Flick, P.L. Andresen, G.S. Was, The key factors affecting crack growth behavior of neutron-irradiated austenitic alloys, in 15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (Wiley Online Library, 2011), pp. 1241–1254Google Scholar
  11. 11.
    M. Kamaya, K. Kubushiro, Y. Sakakibara, S. Suzuki, H. Morita, Y. Rika, D. Kobayashi, K. Yamagiwa, T. Nishioka, Y. Yamazaki et al., Round robin crystal orientation measurement using EBSD for damage assessment. Mech. Eng. J. 3, 16–77 (2016)Google Scholar
  12. 12.
    S. Wroski, J. Tarasiuk, B. Bacroix, A. Baczmaski, C. Braham, Investigation of plastic deformation heterogeneities in duplex steel by EBSD. Mater. Charact. 73, 52–60 (2012)CrossRefGoogle Scholar
  13. 13.
    R. Yoda, T. Yokomaku, N. Tsuji, Plastic deformation and creep damage evaluations of type 316 austenitic stainless steels by EBSD. Mater. Charact. 61, 913–922 (2010)CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  • M. N. Gussev
    • 1
  • G. S. Was
    • 2
  • J. T. Busby
    • 1
  • K. J. Leonard
    • 1
  1. 1.Oak Ridge National LaboratoryOak RidgeUSA
  2. 2.University of MichiganAnn ArborUSA

Personalised recommendations