Irradiation Assisted Stress Corrosion Cracking (IASCC) of Nickel-Base Alloys in Light Water Reactors Environments Part II: Stress Corrosion Cracking

  • Mi WangEmail author
  • Miao Song
  • Gary S. Was
  • L. Nelson
  • R. Pathania
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

Radiation-induced microstructural changes control the Irradiation Assisted Stress Corrosion Cracking (IASCC) of core materials, which is a key factor in the extension of the operating lifetime of Light Water Reactors (LWRs). Nickel-base alloys are considered as potential structural materials to replace highly IASCC susceptible austenitic stainless steels. Constant extension rate tensile (CERT) tests were conducted on proton irradiated high strength nickel-base alloy 625 with two different heat treatment conditions (625Plus and 625DA) in both simulated BWR NWC and PWR primary water. Crack length per unit area and fraction of grain boundaries that cracked were used to assess the IASCC susceptibility. Both 625Plus and 625DA showed a very high IASCC susceptibility. 625DA also exhibited greater changes in all microstructure features than 625Plus.

Keywords

Nickel-base alloys Irradiation-assisted stress corrosion cracking Mechanical properties LWRs 

Notes

Acknowledgements

Support for this work was provided by the Electric Power Research Institute (contract no: 10002164 and 10002154) and Department of Energy (contract no: 4000136101). The authors gratefully acknowledge the facilities provided by the Michigan Ion Beam Laboratory and the High Temperature Corrosion Laboratory at the University of Michigan. The authors would also like to thank Dr. Ovidiu Toader of the Michigan Ion Beam Laboratory and Mr. Alex Flick of the High Temperature Corrosion Laboratory for their invaluable support in conducting the experiments.

Reference

  1. 1.
    S. Bruemmer, New issues concerning radiation-induced material changes and irradiation-assisted stress corrosion cracking in light water reactors, in Proceeding of 10th International Conference on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors. (Houston, TX, 2002)Google Scholar
  2. 2.
    O. Chopra, A. Rao, A review of irradiation effects on LWR core internal materials—Neutron embrittlement. J. Nucl. Mater. 412, 195–208 (2011)CrossRefGoogle Scholar
  3. 3.
    O. Chopra, A. Rao, A review of irradiation effects on LWR core internal materials—IASCC susceptibility and crack growth rates of austenitic stainless steels. J. Nucl. Mater. 409, 235–256 (2011)CrossRefGoogle Scholar
  4. 4.
    P. Andresen, F. Garner, J. Gorman, S. Maloy, J. Nelson, L. Tan, T. Toloczko, G. Was, Technical report: critical issues report and roadmap for the advanced radiation-resistant materials program, EPRI, Palo Alto, CA: 2012. 1026482, (2012)Google Scholar
  5. 5.
    F. Garner, B. Oliver, L. Greenwood, D. Edwards, S. Bruemmer, M. Grossbeck (2002) Generation and retention of helium and hydrogen in austenitic steels irradiated in a variety of LWR and test reactor spectral environments. Pacific Northwest National Laboratory (PNNL), Richland, WA (US)Google Scholar
  6. 6.
    P. Scott, A review of irradiation assisted stress corrosion cracking. J. Nucl. Mater. 211, 101–122 (1994)CrossRefGoogle Scholar
  7. 7.
    E. Kenik, R. Jones, G. Bell, Irradiation-assisted stress corrosion cracking. J. Nucl. Mater. 212, 52–59 (1994)CrossRefGoogle Scholar
  8. 8.
    G. Was, S. Bruemmer, Effects of irradiation on intergranular stress corrosion cracking. J. Nucl. Mater. 216, 326–347 (1994)CrossRefGoogle Scholar
  9. 9.
    J. Busby, G. Was, E. Kenik, Isolating the effect of radiation-induced segregation in irradiation-assisted stress corrosion cracking of austenitic stainless steels. J. Nucl. Mater. 302, 20–40 (2002)CrossRefGoogle Scholar
  10. 10.
    G. Smith, D. Tillack, S. Patel, Alloy 625: impressive past, significant presence, awesome future, in Superalloys 718,625,706 and Various Derivatives. The Minerals. (Metals and Materials Society, 1991), pp. 35–46Google Scholar
  11. 11.
    L. Shoemaker, Alloys 625 and 725: trends in properties and applications, in Superalloys 718, 625, 706 and Derivatives. The Minerals, (Metals and Materials Society, 2005), pp. 409–418Google Scholar
  12. 12.
    J. Rakowski, C. Stinner, M. Lipschutz, J. Preston Montague, The use and performance of wrought 625 alloy in primary surface recuperators for gas turbine engines, in Superalloys 718,625,706 and Derivatives, (2005), pp. 271–286Google Scholar
  13. 13.
    M. Song, M. Wang, G. Was, Irradiation assisted stress corrosion cracking (IASCC) of nickel-base alloys in light water reactors (LWRs) environments Part I: microstructure characterization, in Proceeding of 18th International Conference on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors. (Portland, Oregon, 2017)Google Scholar
  14. 14.
    J.S.R.I.M. Ziegler, Program (IBM Corporation, Yorktown, NY, 2013)Google Scholar
  15. 15.
    F. Carrette, M. Lafont, G. Chatainier, L. Guinard, B. Pieraggi, Analysis and TEM examination of corrosion scales grown on Alloy 690 exposed to pressurized water at 325 °C. Surf. Interface Anal. 34, 135–138 (2002)CrossRefGoogle Scholar
  16. 16.
    A. Machet, A. Galtayries, S. Zanna, L. Klein, V. Maurice, P. Jolivet, M. Foucault, P. Combrade, P. Scott, P. Marcus, XPS and STM study of the growth and structure of passive films in high temperature water on a nickel-base alloy. Electrochim. Acta 49, 3957–3964 (2004)CrossRefGoogle Scholar
  17. 17.
    L. Marchetti, S. Perrin, Y. Wouters, F. Martin, M. Pijolat, Photoelectrochemical study of nickel base alloys oxide films formed at high temperature and high pressure water. Electrochim. Acta 55, 5384–5392 (2010)CrossRefGoogle Scholar
  18. 18.
    M. Sennour, L. Marchetti, F. Martin, S. Perrin, R. Molins, M. Pijolat, A detailed TEM and SEM study of Ni-base alloys oxide scales formed in primary conditions of pressurized water reactor. J. Nucl. Mater. 402, 147–156 (2010)CrossRefGoogle Scholar
  19. 19.
    Marchetti-Sillans L (2007) Ph.D. thesis: Corrosion généralisée des alliages à base nickel en milieu aqueux à haute température: apport à la compréhension des mécanismes. École Nationale Supérieure des Mines Saint-EtienneGoogle Scholar
  20. 20.
    Macdonald D (2016) The electrochemical nature of stress corrosion cracking. in Stress Corrosion Cracking of Nickel Based Alloys in Water-Cooled Nuclear Reactors: The Coriou Effect. 239 CrossRefGoogle Scholar
  21. 21.
    G. Was. Irradiation assisted corrosion and stress corrosion cracking (IAC/IASCC) in nuclear reactor systems and components, in Nuclear Corrosion Science and Engineer (Woodhead Publishing, 2012)Google Scholar
  22. 22.
    G. Was, Fundamentals of radiation materials science (Springer, Metals and Alloys, 2007)Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  • Mi Wang
    • 1
    Email author
  • Miao Song
    • 1
  • Gary S. Was
    • 1
  • L. Nelson
    • 2
  • R. Pathania
    • 3
  1. 1.University of MichiganAnn ArborUSA
  2. 2.JLN ConsultingMills RiverUSA
  3. 3.Electric Power Research InstitutePalo AltoUSA

Personalised recommendations