Abstract
The polycrystalline sample of Ba2Co1.5Mg0.5Fe11.88Ga0.12O22 Y-type hexaferrite, doped with Ga-cation, was prepared by using the solid-state reaction method. The crystalline structure of sample was investigated by x-ray diffractometer (XRD), and the magnetic properties of sample were measured by vibrating sample magnetometer (VSM), and Mössbauer spectrometer. The crystal structure of prepared sample was determined to be rhombohedral with space group R-3m. From the temperature dependence of the magnetization curves under 100 Oe between 4.2 and 740 K, two temperature-dependent magnetic transitions occurred in the Ba2Co1.5Mg0.5Fe11.88Ga0.12O22 sample. Mössbauer spectra of the sample were analyzed at various temperatures ranging from 4.2 to 620 K, and the Ba2Co1.5Mg0.5Fe11.88Ga0.12O22 sample showed abrupt changes in Hhf and EQ at 200 K, indicating the spin transition effect. We have also determined the magnetic transition temperature TC, in addition to the temperature dependent magnetization and ZVC measurements.
Similar content being viewed by others
References
H. Ueda, Y. Tanaka, Y. Wakabayashi and T. Kimura, Physica B 536, 118 (2018).
S. Ishiwata, Y. Taguchi, H. Murakawa, Y. Onose and Y. Tokura, science 319, 1643 (2008).
Y. Wang, S. Zhang, W. K. Zhu, L. Ling, L/Zhang, Z. Qu, L. Pi, W. Tong, M. Tian and Y. Zhang, Appl. Phys. Lett. 110, 262901 (2017).
Y. Hiraoka, Y. Tanaka, M. Oura, Y. Wakabayashi and T. Kimura, J. Magn. Magn. Mater. 384, 160 (2015).
K. Zhai et al., Nature Comm. 8, 519 (2017).
Y. Kitagawa, Y. Hiraoka, T. Honda, T. Ishikura, H. Nakamura and T. Kimura, Nature Mater. 9, 797 (2010).
H. B. Lee, Y. S. Song, J. H. Chung, S. H. Chun, Y. S. Chai, K. H. Kim, M. Reehuis, K. Prokes and S. Mat’as, Phys. Rev. B 83, 144425 (2011).
H. Chang, H. B. Lee, Y-S. Song, J-H. Chung, S. A. Kim, I. H. Oh, M. Reehuis and J. Schefer, Phys. Rev. B 85, 064402 (2012).
S. Shen, Y. Chai and Y. Sun, Sci. Rep. 5, 8254 (2015).
T. Nakajima, Y. Tokunaga, M. Matsuda, S. Dissanayake, J. Fernandez-Baca, K. Kakurai, Y. Taguchi, Y. Tokura and T-h. Arima, Phys. Rev. B 94, 195154 (2016).
S. Hirose, K. Haruki, A. Ando and T. Kimura, Appl. Phys. Lett. 104, 022907 (2014).
S. Shen, L. Yan, Y. Chai, J. Cong and Y. Sun, Appl. Phys. Lett. 104, 032905 (2014).
W. Xu et al., AIP Advances. 4, 067122 (2014).
H. Ueda, Y. Tanaka, H. Nakajima, S. Mori, K. Ohta, K. Haruki, S. Hirose, Y. Wakabayashi and T. Kimura, Appl. Phys. Lett. 109, 182902 (2014).
M. Zhang, L. Yin, Q. Liu, X. Kong, Z. Zi, J. Dai and Y. Sun, J. Alloys Comp. 725, 1252 (2017).
A. Nikzad, A. Ghasemi, M. K. Tehrani1 and G. R. Gordani, J. Supercond. Nov. Magn. 28, 3579 (2015).
W-S. Noh et al., Phys. Rev. Lett. 114, 117603 (2015).
A. Collomb, M. A. Hadj Farhat and J. C. Joubert, Mater. Res. Bull. 24, 453 (1989).
J. T. Lim, C. M. Kim, B. W. Lee and C. S. Kim, J. Appl. Phys. 111, 07A518 (2012).
S. Ishiwata, D. Okuyama, K. Kakurai, M. Nishi, Y. Taguchi and Y. Tokura, Phys. Rev. B 81, 174418 (2010).
H. N. Ok, K. S. Baek, E. C. Kim and C. S. Kim, Phys. Rev. B 48, 3212 (1993).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lim, J.T., Kim, J. & Kim, C.S. Investigation of Spin Reorientation in Ga Substituted Y-type Hexaferrite based on Mössbauer Spectroscopy. J. Korean Phys. Soc. 73, 1708–1711 (2018). https://doi.org/10.3938/jkps.73.1708
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.3938/jkps.73.1708