Abstract
This new type nanocomposite powder was prepared with electroless plating enhanced by ultrasonic wave. High-resolution transmission electron microscopy (HRTEM) showed that As-plated particles have nanometer scale average size. X-ray diffraction (XRD) analysis showed the presence of a noncrystalline structure in the plating layer on the nano-Al2O3 matrix. The content of the plating layer was analyzed by energy dispersive X-ray spectroscopy (EDX) technology. The plating layer content was adjustable by changing the solution concentration.
This is a preview of subscription content, log in via an institution to check access.
References
Chen, D.J., Mayo, M.J., 1996. Rapid rate sintering of nanocrystalline ZrO2 minus 3 mol% Y2O3.J. Am. Ceram. Soc.,79(4):906–912.
Li, H.Q., Liu, J.B., 1998. Low temperature electroless nickel plating by use of ultrasonic wave.Plating and Polish,17(3):14–17(in Chinese).
Li, J., Mao, D.S., 1997. A new kind of cermet and its wear resistance.Letter of advanced technology,7(7): 15–20.
Li, Y.K., Guo, L., 1995. Studies of fracture behavior on nano-Al2O3 and Al2O3-based nanocomposite ceramics.J. Jilin Arboriculture College,11(3):155–159(in Chinese).
Mao, D.S., Li, J., Guo, S.Y. et al., 1997. Study of abrasion behavior of an advanced Al2O3−TiC−Co ceramic.Wear,209(1):153–159.
Mao, D.S., Liu, X.H., Li, J. et al., 1998. Fine cobalt-toughened Al2O3−TiC ceramic and its wear resistance.J. Mate. Sci.,33(23):5677–5682.
Ni, Y.H., Ge, X.W., Xu, X.L. et al., 2000. Developments in preparation of nano-scale materials.J. Inorganic Mater.,15(1):9–15(in Chinese).
Wu, S.J., De, J., Lutgard, C. et al., 1996. Sintering of nanophase gamma-Al2O3 powder.J. Am. Ceram. Soc.,79(8): 2207–2211.
Zhang, L.D., 1993. Nanomaterials. Science Press, Beijing. p. 54(in Chinese).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Guo-ping, L., Jian, L. & Shang-jun, W. Preparation and characteristics of new type nanocomposite powder. J. Zheijang Univ.-Sci. 2, 376–378 (2001). https://doi.org/10.1631/BF02840550
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1631/BF02840550