Containment of internal expansion caused by alkali-aggregate reaction with ultra-high performance fiber reinforced concrete

  • Original Article
  • Published:
Materials and Structures Aims and scope Submit manuscript

Abstract

In severe climatic condition, concrete structures can undergo various damages including alkali-aggregate reaction (AAR) which generally induces internal swelling and cracks in the reactive aggregates and surrounding cement paste. This study proposes an innovative repair technique which consists in casting a thin UHPC layer directly on the affected concrete substrate. For such repair, once UHPC is poured in the formwork, self-induced tensile stresses developed in UHPC by its restrained shrinkage on the concrete substrate. Later, the UHPC repair sustains further tensile stresses resulting from additional AAR internal expansion. The main objective of this research project was to evaluate the UHPC behavior under restrained shrinkage conditions and to assess the available strain margin to contain the AAR expansion in different UHPC repair configurations. A special device adapted to ring specimens was developed to first simulate the restrained shrinkage and second generate the AAR expansion. Experimental results showed that a repair in high performance concrete (HPC) cracks under restrained shrinkage and thus cannot confine internal expansion. For the UHPC repairs, no cracks developed under restrained shrinkage and very limited internal tensile stress was generated in the repair. The expansion applied thereafter on the UHPC repairs showed that the UHPC tensile strain available to confine AAR expansion without loss of watertighness is inversely proportional to the fiber content in the UHPC, i.e. 0.28%, 0.2% and 0.17% for fiber contents of 2%, 3% and 4% in volume respectively. Addition of 1.2% of rebar in the UHPC repair extends by 30% the tensile strain available to confine the AAR, while presence of cold joints in this reinforced repair reduced this performance.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12

Similar content being viewed by others

References

  1. OECD (1989) Durability of concrete road bridges—Report by a group of scientific experts from the Organization for Economic Co-operation and Development—in French (OECD). OECD, Paris

    Google Scholar 

  2. Fournier B, Bérubé M-A (2000) Alkali-aggregate reaction in concrete: a review of basic concepts and engineering implications. Can J Civ Eng 27(2):167–191

    Article  Google Scholar 

  3. Saouma V (2013) Numerical modeling of AAR. CRC Press, Boca Raton

    Book  Google Scholar 

  4. Smaoui N (2003) Contribution to the evaluation of the structural behavior of structures affected by the alkali-silica reaction (RAS)—in French. Laval University, Quebec

    Google Scholar 

  5. Hobbs DW (1988) Alkali-silica reaction in concrete. Thomas Telford Publishing, London

    Book  Google Scholar 

  6. Esposito R, Anaç C, Hendriks MA, Copuroglu O (2016) Influence of the alkali-silica reaction on the mechanical degradation of concrete. J Mater Civil Eng 28(6)

  7. Larive C (1997) Combined contributions of experimentation and modeling to the understanding of the alkali reaction and its mechanical effects—in French. Ecole nationale des ponts et chaussees, Paris

  8. Charron J-P, Desmettre C (2013) Interest of using fiber-reinforced concrete for the construction of sustainable structures—in French. Polytechnique Montreal, Montreal

    Google Scholar 

  9. Hydro-Quebec (2021) Hydro-Quebec annual report—in French. Canada Hydro-Quebec, Quebec

  10. Bérubé M-A, Durand B, Vézina D, Fournier B (2000) Alkali-aggregate reactivity in Quebec (Canada). Can J Civ Eng 27(2):226–245

    Article  Google Scholar 

  11. Bérubé M-A, Smaoui N, Fournier B, Bissonnette B, Durand B (2005) Evaluation of the expansion attained to date by concrete affected by alkali–silica reaction. Part III: application to existing structures. Can J Civil Eng 32(3):463–479

    Article  Google Scholar 

  12. Charron J-P (2003) Contribution to the study of the early age behavior of cementitious materials under conditions of free and restricted deformation—in French. Laval University, Quebec

    Google Scholar 

  13. Graybeal BA (2006) Material property characterization of ultra-high performance concrete: United States. Federal Highway Administration. Office of Infrastructure

  14. Vernet C (2003) UHPC microstructure and related durability performance laboratory assessment and field experience examples. In: Proceedings of the International symposium on high performance concrete

  15. Dénarié E, Damien J, Nicolas F, Dominique C (2013) Rejuvenation of maritime signalisation structures with UHPFRC. In: Symposium on ultra-high performance fiber-reinforced concrete, UHFFRC, Marseille, France

  16. Habel K (2004) Structural behaviour of elements combining ultra-high performance fibre reinforced concretes (UHPFRC) and reinforced concrete. EPFL, Lausanne

    Google Scholar 

  17. Habel K, Charron J-P, Denarié E, Brühwiler E (2006) Autogenous deformations and viscoelasticity of UHPFRC in structures. Part I: experimental results. Mag Concr Res 58(3):135–145

    Article  Google Scholar 

  18. Kamen A (2007) Early and delayed behavior of a hardening UHPFRC under thermomechanical effects—in French. EPFL, Lausanne

    Google Scholar 

  19. ASTM-C1581 (2004) Standard test method for determining age at cracking and induced tensile stress characteristics of mortar and concrete under restrained shrinkage

  20. Argouges M (2010) Study of the mechanisms and kinetics of self-healing in cracked cementitious mortars—in French. University of Sherbrooke, Sherbrooke

    Google Scholar 

  21. Weiss WJ, Yang W, Shah SP (2000) Influence of specimen size/geometry on shrinkage cracking of rings. J Eng Mech 126(1):93–101

    Google Scholar 

  22. See HT, Attiogbe EK, Miltenberger MA (2003) Shrinkage cracking characteristics of concrete using ring specimens. Mater J 100(3):239–245

    Google Scholar 

  23. Hossain AB, Weiss J (2004) Assessing residual stress development and stress relaxation in restrained concrete ring specimens. Cement Concr Compos 26(5):531–540

    Article  Google Scholar 

  24. Denarié E (2006) SAMARIS D25b-Guidance for the use of UHPFRC for rehabilitation of concrete highway structures. MCS/EU

  25. Messan A (2006) Contribution to the study of the behavior at a very young age of thin structures in mortar—in French. Université Montpellier II-Sciences et Techniques du Languedoc, Montpellier

    Google Scholar 

  26. Moon J-H, Rajabipour F, Pease B, Weiss J (2006) Quantifying the influence of specimen geometry on the results of the restrained ring test. J ASTM Int 3(8):1–14

    Google Scholar 

  27. Abid S (2021) Containment of expansion caused by the alkali-aggregate reaction with ultra-high performance fiber-reinforced concrete (UHPC)—in French, Master Thesis, Polytechnique Montreal, Montreal

  28. Beaurivage F (2009) Study of the influence of structural parameters on the behavior laws of fiber concretes for the design of structures—in French. Polytechnique Montreal, Montreal

    Google Scholar 

  29. Lagier F, Massicotte B, Charron J-P (2015) Bond strength of tension lap splice specimens in UHPFRC. Constr Build Mater 93:84–94

    Article  Google Scholar 

  30. Wille K, El-Tawil S, Naaman AE (2014) Properties of strain hardening ultra high performance fiber reinforced concrete (UHP-FRC) under direct tensile loading. Cement Concr Compos 48:53–66

    Article  Google Scholar 

  31. Yoo D-Y, Banthia N, Yoon Y-S (2017) Ultra-high-performance fiber-reinforced concrete: shrinkage strain development at early ages and potential for cracking. J Test Eval 45(6):2061–2070

    Article  Google Scholar 

  32. Du J, Meng W, Khayat KH, Bao Y, Guo P et al (2021) New development of ultra-high-performance concrete (UHPC). Compos B Eng 224:109220

    Article  Google Scholar 

  33. Burkart I, Müller HS (2008) Creep and shrinkage characteristics of ultra high strength concrete (UHPC). In: Proceedings of the second international symposium on ultra high performance concrete, pp 469–476

  34. Flietstra JC (2011) Creep and shrinkage behavior of ultra high-performance concrete under compressive loading with varying curing regimes. Master's Thesis, Michigan Technological University

  35. Yang J, Chen B, Su J, Xu G, Zhang D et al (2022) Effects of fibers on the mechanical properties of UHPC: a review. J Traffic Transp Eng (English Edition)

  36. Hobbs D (1990) Alkali-silica reaction: its effect on concrete members and structures. Developments in structural engineering. Forth rail bridge centenary conference, Heriot-Watt University, Endinburgh, Scotland, vol 1–2. Spon, E&FN, August 21–23

  37. Shah H, Weiss J (2006) Quantifying shrinkage cracking in fiber reinforced concrete using the ring test. Mater Struct 39(9):887

    Article  Google Scholar 

  38. Wang J-Y, Bian C, Xiao R-C, Ma B (2019) Restrained shrinkage mechanism of ultra high performance concrete. KSCE J Civ Eng 23(10):4481–4492

    Article  Google Scholar 

Download references

Acknowledgements

City of Montréal, Jacques Cartier and Champlain Bridges Incorporated, St-Lawrence Seaway, Béton préfabriqué du Lac, Euclid Chemical, Sika, Natural Sciences and Engineering Research Council of Canada (NSERC) and Mitacs financially supported the research project. The authors are grateful to the technical staff of Polytechnique Montreal structural laboratory for their help in conducting the experimental program.

Author information

Authors and Affiliations

  1. Department of Civil, Geological and Mining Engineering, Polytechnique Montreal, Montreal, Canada

    S. Abid, C. Desmettre & J.-P. Charron

Authors
  1. S. Abid
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. C. Desmettre
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. J.-P. Charron
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to J.-P. Charron.

Ethics declarations

Conflict of interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Abid, S., Desmettre, C. & Charron, JP. Containment of internal expansion caused by alkali-aggregate reaction with ultra-high performance fiber reinforced concrete. Mater Struct 56, 32 (2023). https://doi.org/10.1617/s11527-023-02116-w

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1617/s11527-023-02116-w

Keywords

Search

Navigation