Effects of curing conditions with different temperature and humidity on damage evolution of concrete during freeze–thaw cycling

  • Original Article
  • Published:
Materials and Structures Aims and scope Submit manuscript

Abstract

To clarify the relationship between the curing conditions (temperature and humidity) of concrete and its frost resistance, several concretes with different water-binder (w/b) ratios and curing conditions were investigated by observing their microstructural damage in a freeze–thaw (F-T) environment using nuclear magnetic resonance (NMR). The results reveal that the curing temperature and humidity significantly influence the pore distribution and porous quality of concrete. With the decrease of the curing temperature and humidity and the increase of the w/b ratio, the proportion of macropores (0.05 μm < r < 1 μm) and microcracks (r ≥ 1 μm) significantly increases. Compared with standard curing, the proportion of macropores and microcracks in concrete under the curing conditions of 10 °C-RH70% and 3 °C-RH50% increased by 16.21% and 26.71% respectively, while the frost resistance of concrete decreased. With the increase of the F-T cycles, the proportion of macropores and microcracks in concrete increased, the proportion of micropores (r < 0.01 μm) and mesopores (0.01 μm < r < 0.05 μm) decreased, and the T2 spectrum curve gradually moved to the right. Notably, the above-mentioned microstructure changes are reflected in the relative dynamic elastic modulus (RDEM). The total ratio of mesopores to macropores significantly influences the damage degree of concrete. Compared with the increase of the w/b ratio, the lack of curing temperature and humidity have greater influence on the frost resistance of concrete. The RDEM of concrete decreases with the increase of the F-T cycles, which is consistent with the change of the microcrack proportion.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig.7
Fig. 8

Similar content being viewed by others

References

  1. Ortiz J, Aguado A, Agulló L, Garcia T (2005) Influence of environmental temperatures on the concrete compressive strength: Simulation of hot and cold weather conditions. Cem Concr Res 35(10):1970–1979. https://doi.org/10.1016/j.cemconres.2005.01.004

    Article  Google Scholar 

  2. Du M, Jin X, Ye H, Jin N, Tian Y (2016) A coupled hygro-thermal model of early-age concrete based on micro-pore structure evolution. Constr Build Mater 111:689–698. https://doi.org/10.1016/j.conbuildmat.2015.10.187

    Article  Google Scholar 

  3. Li C, Wu M, Chen Q, Jiang Z (2018) Chemical and mineralogical alterations of concrete subjected to chemical attacks in complex underground tunnel environments during 20–36 years. Cement Concrete Compo 86:139–159. https://doi.org/10.1016/j.cemconcomp.2017.11.007

    Article  Google Scholar 

  4. Davila JM, Sarmiento AM, Fortes JC, Santisteban M, Grande JA (2021) Determination of the extreme reduction of concrete strength due to acid mine drainage by laboratory tests on specimens located in a real environment. Constr Build Mater 269(7):121817. https://doi.org/10.1016/j.conbuildmat.2020.121817

    Article  Google Scholar 

  5. Qin Y, Zhang XW, Chai JR, Xu ZG, Li SY (2019) Experimental study of compressive behavior of polypropylene-fiber-reinforced and polypropylene-fiber-fabric-reinforced concrete. Constr Build Mater 194:216–225. https://doi.org/10.1016/j.conbuildmat.2018.11.042

    Article  Google Scholar 

  6. Wang R, Yu N, Li Y (2020) Methods for improving the microstructure of recycled concrete aggregate: a review. Constr Build Mater 242:118164. https://doi.org/10.1016/j.conbuildmat.2020.118164

    Article  Google Scholar 

  7. Kodur V, Banerji S (2021) Modeling the fire-induced spalling in concrete structures incorporating hydro-thermo-mechanical stresses. Cement Concrete Compo 117:103902. https://doi.org/10.1016/j.cemconcomp.2020.103902

    Article  Google Scholar 

  8. Li Y, Chen J, Wen L, Wang J, Li K (2021) Investigation of the nonlinear creep of concrete with different initial defect rates under continuous compression with acoustic emission technology. J Mater Civil Eng 33(2):04020441

    Article  Google Scholar 

  9. Orakoglu ME, Liu J, Lin R, Tian Y (2017) Performance of clay soil reinforced with fly ash and lignin fiber subjected to freeze-thaw cycles. J Cold Reg Eng 31(4):04017013

    Article  Google Scholar 

  10. Liu B, Luo G, Xie Y (2018) Effect of curing conditions on the permeability of concrete with high volume mineral admixtures. Constr Build Mater 167:359–371. https://doi.org/10.1016/j.conbuildmat.2018.01.190

    Article  Google Scholar 

  11. Wu Z, Shi C, He W, Wu L (2016) Effects of steel fiber content and shape on mechanical properties of ultra-high performance concrete. Constr Build Mater 103:8–14. https://doi.org/10.1016/j.conbuildmat.2015.11.028

    Article  Google Scholar 

  12. Liu L, Wang X, Zhou J, Chu H, Shen D, Chen H, Qin S (2018) Investigation of pore structure and mechanical property of cement paste subjected to the coupled action of freezing/thawing and calcium leaching. Cem Concr Res 109:133–146. https://doi.org/10.1016/j.cemconres.2018.04.015

    Article  Google Scholar 

  13. Jin L, Yu W, Du X, Yang W (2020) Meso-scale simulations of size effect on concrete dynamic splitting tensile strength: Influence of aggregate content and maximum aggregate size. Eng Fract Mech 230:106979. https://doi.org/10.1016/j.engfracmech.2020.106979

    Article  Google Scholar 

  14. He R, Zheng S, Gan VJ, Wang Z, Fang J, Shao Y (2020) Damage mechanism and interfacial transition zone characteristics of concrete under sulfate erosion and Dry-Wet cycles. Constr Build Mater 255:119340. https://doi.org/10.1016/j.conbuildmat.2020.119340

    Article  Google Scholar 

  15. Jiang L, Niu D, Yuan L, Fei Q (2015) Durability of concrete under sulfate attack exposed to freeze–thaw cycles. Cold Reg Sci Technol 112:112–117. https://doi.org/10.1016/j.coldregions.2014.12.006

    Article  Google Scholar 

  16. Wang Y, An MZ, Yu ZR, Han S, Ji WY (2017) Durability of reactive powder concrete under chloride-salt freeze–thaw cycling. Mater Struct 50(1):1–9. https://doi.org/10.1617/s11527-016-0878-5

    Article  Google Scholar 

  17. Pilehvar S, Szczotok AM, Rodríguez JF, Valentini L, Lanzón M, Pamies R, Kjøniksen AL (2019) Effect of freeze-thaw cycles on the mechanical behavior of geopolymer concrete and Portland cement concrete containing micro-encapsulated phase change materials. Constr Build Mater 200:94–103. https://doi.org/10.1016/j.conbuildmat.2018.12.057

    Article  Google Scholar 

  18. Kuan P, Hongxia Q, Kefan C (2020) Reliability analysis of freeze–thaw damage of recycled ceramic powder concrete. J Mater Civil Eng 32(9):05020008

    Article  Google Scholar 

  19. Zeng Q, Li KF, Fen-Chong T (2016) Effect of supercooling on the instantaneous freezing dilation of cement-based porous materials. J Build Phys 40(2):101–124. https://doi.org/10.1177/1744259116649321

    Article  Google Scholar 

  20. Wang ZD, Zeng Q, Wu YK, Wang L, Yao Y, Li K (2014) Relative humidity and deterioration of concrete under freeze–thaw load. Constr Build Mater 62:18–27. https://doi.org/10.1016/j.conbuildmat.2014.03.027

    Article  Google Scholar 

  21. Liu DY, Tu YM, Shi P, Sas G, Elfgren L (2021) Mechanical and durability properties of concrete subjected to early-age freeze–thaw cycles. Mater Struct 54(6):1–18. https://doi.org/10.1617/s11527-021-01802-x

    Article  Google Scholar 

  22. Zeng Q, Li L, Pang XY, Gui Q, Li KF (2014) Freeze–thaw behavior of air entrained cement paste saturated with 10 wt.% NaCl solution. Cold Reg Sci Technol 102:21–31. https://doi.org/10.1016/j.coldregions.2014.02.003

    Article  Google Scholar 

  23. Wang RJ, Zhang QJ, Li Y (2022) Deterioration of concrete under the coupling effects of freeze-thaw cycles and other actions: A review. Constr Build Mater 319:126045. https://doi.org/10.1016/j.conbuildmat.2021.126045

    Article  Google Scholar 

  24. Zeng Q, Fen-Chong T, Li KF (2013) Elastic behavior of saturated porous materials under undrained freezing. Acta Mech Sinica-Prc 29(6):827–835. https://doi.org/10.1007/s10409-013-0082-6

    Article  Google Scholar 

  25. Li Y, Wang RJ, Li SY, Zhao Y, Qin Y (2018) Resistance of recycled aggregate concrete containing low-and high-volume fly ash against the combined action of freeze–thaw cycles and sulfate attack. Constr Build Mater 166:23–34. https://doi.org/10.1016/j.conbuildmat.2018.01.084

    Article  Google Scholar 

  26. Holthausen RS, Raupach M (2018) Monitoring the internal swelling in cementitious mortars with single-sided 1H nuclear magnetic resonance. Cem Concr Res 111:138–146. https://doi.org/10.1016/j.cemconres.2018.05.021

    Article  Google Scholar 

  27. Li N, Farzadnia N, Shi C (2017) Microstructural changes in alkali-activated slag mortars induced by accelerated carbonation. Cem Concr Res 100:214–226. https://doi.org/10.1016/j.cemconres.2017.07.008

    Article  Google Scholar 

  28. Xue S, Meng F, Zhang P, Bao J, Wang J, Zhao K (2020) Influence of water re-curing on microstructure of heat-damaged cement mortar characterized by low-field NMR and MIP. Constr Build Mater 262:120532. https://doi.org/10.1016/j.conbuildmat.2020.120532

    Article  Google Scholar 

  29. Nunes C, Pel L, Kunecký J, Slížková Z (2017) The influence of the pore structure on the moisture transport in lime plaster-brick systems as studied by NMR. Constr Build Mater 142:395–409. https://doi.org/10.1016/j.conbuildmat.2017.03.086

    Article  Google Scholar 

  30. Zhou CS, Ren FZ, Zeng Q, Xiao LZ, Wang W (2018) Pore-size resolved water vapor adsorption kinetics of white cement mortars as viewed from proton NMR relaxation. Cem Concr Res 105:31–43. https://doi.org/10.1016/j.cemconres.2017.12.002

    Article  Google Scholar 

  31. Ren FZ, Zhou CS, Zeng Q, Zhu T, Feng X, Wang W (2019) The dependence of capillary sorptivity and gas permeability on initial water content for unsaturated cement mortars. Cement Concrete Compo 104:103356. https://doi.org/10.1016/j.cemconcomp.2019.103356

    Article  Google Scholar 

  32. Xie EH, Zhou CS, Song QH, Zeng Q, Wang ZD (2020) The effect of chemical aging on water permeability of white cement mortars in the context of sol–gel science. Cement Concrete Compo 114:103810. https://doi.org/10.1016/j.cemconcomp.2020.103812

    Article  Google Scholar 

  33. Prado PJ, Balcom BJ, Beyea SD, Bremner TW, Armstrong RL, Grattan-Bellew PE (1998) Concrete freeze/thaw as studied by magnetic resonance imaging. Cem Concr Res 28(2):261–270. https://doi.org/10.1016/S0008-8846(97)00222-6

    Article  Google Scholar 

  34. Wang XX, Shen XD, Wang HL, Gao C (2015) Nuclear magnetic reso-nance analysis of concrete-lined channel freeze-thaw damage. J Ceram Soc Jpn 123(1):43–51. https://doi.org/10.2109/jcersj2.123.43

    Article  Google Scholar 

  35. Li Y, Wang R, Li S, Zhao Y, Qin Y (2018) Resistance of recycled aggregate concrete containing low- and high-volume fly ash against the combined action of freeze-thaw cycles and sulfate attack. Constr Build Mater 166(3):23–34. https://doi.org/10.1016/j.conbuildmat.2018.01.084

    Article  Google Scholar 

  36. Li L, Zha Y (2018) Mapping relative humidity, average and extreme temperature in hot summer over China. Sci Total Environ 615:875–881. https://doi.org/10.1016/j.scitotenv.2017.10.022

    Article  Google Scholar 

  37. Shi F, Zhao C, Zhou X, Li X (2019) Spatial variations of climate-driven trends of water vapor pressure and relative humidity in northwest china. Asia-Pac J Atmos Sci 55(2):221–231. https://doi.org/10.1007/s13143-018-0062-7

    Article  Google Scholar 

  38. Chen D, Liu W, Huang F, Li Q, Uchenna-Ochege F, Li L (2020) Spatial-temporal characteristics and influencing factors of relative humidity in arid region of Northwest China during 1966–2017. J Arid Land 12(3):397–412. https://doi.org/10.1007/s40333-020-0098-2

    Article  Google Scholar 

  39. National Standard of the People’s Republic of China (2002) GB/T50081-2002. China Architecture and Building Press, Beijing, Standard for Test Method of Mechanical Properties on Ordinary Concrete ((in Chinese))

    Google Scholar 

  40. National Standard of the People’s Republic of China, GB/T 50082–2009. Standard for test methods of long-term performance and durability of ordinary concrete. China Architecture and Building Press, Beijing, 2009. (in Chinese).

  41. ASTM C666/C666M-03, 2003. Standard test method for resistance of concrete to rapid freezing and thawing. In: American Society of Testing and Materials.

  42. Halperin WP, Bhattacharja S, D’Orazio F (1991) Relaxation and dynamical properties of water in partially filled porous materials using NMR techniques. Magn Reson Iaging 9(5):733–737. https://doi.org/10.1016/0730-725X(91)90365-S

    Article  Google Scholar 

  43. Tamtsia BT, Beaudoin JJ (2000) Basic creep of hardened cement paste A re-examination of the role of water. Cem Concr Res 30(9):1465–1475. https://doi.org/10.1016/S0008-8846(00)00279-9

    Article  Google Scholar 

  44. Xu F, Wang S, Li T, Liu B, Li B, Zhou Y (2021) Mechanical properties and pore structure of recycled aggregate concrete made with iron ore tailings and polypropylene fibers. J Build Eng 33:101572. https://doi.org/10.1016/j.jobe.2020.101572

    Article  Google Scholar 

  45. Rosenbrand E, Fabricius IL, Fisher Q, Grattoni C (2015) Permeability in Rotliegend gas sandstones to gas and brine as predicted from NMR, mercury injection and image analysis. Mar Petrol Geol 64:189–202. https://doi.org/10.1016/j.marpetgeo.2015.02.009

    Article  Google Scholar 

  46. Zeng Q. Poromechanics of freezing behavior of cement-based porous materials saturated with salt solution. Tsinghua University 2012. [in Chinese]

  47. Deng X, Gao X, Wang R, Gao M, Yan X, Cao W, Liu J (2021) Investigation of microstructural damage in air-entrained recycled concrete under a freeze–thaw environment. Constr Build Mater 268:121219. https://doi.org/10.1016/j.conbuildmat.2020.121219

    Article  Google Scholar 

  48. Sun ZH, Scherer GW (2010) Effect of air voids on salt scaling and internal freezing. Cem Concr Res 40(2):260–270. https://doi.org/10.1016/j.cemconres.2009.09.027

    Article  Google Scholar 

  49. Li XD, Dong W, Wu ZM, Chang QR (2010) Experimental investigation on double K fracture parameters for small size specimens of concrete. Eng Mech 2(27):166–172. https://doi.org/10.3724/SP.J.1011.2010.01138

    Article  Google Scholar 

  50. Cañizo JA, Einav A, Lods B (2018) On the rate of convergence to equilibrium for the linear Boltzmann equation with soft potentials. J Math Anal Appl 462(1):801–839. https://doi.org/10.1016/j.jmaa.2017.12.052

    Article  MathSciNet  MATH  Google Scholar 

  51. Van den Heede P, Furniere J, De Belie N (2013) Influence of air entraining agents on deicing salt scaling resistance and transport properties of high-volume fly ash concrete. Cement concr Compo 37:293–303. https://doi.org/10.1016/j.cemconcomp.2013.01.005

    Article  Google Scholar 

  52. Xing BY, Cheng PY, Tang JP, Xie NH, Zeng Q, Zhou CS (2021) Pore structure evolution of water-saturated mortar under freeze-thaw cycles. J Chin Ceram Soc 49(02):331–339 [in Chinese]

    Google Scholar 

Download references

Acknowledgements

The authors would like to acknowledge the National Natural Science Foundation of China (No.52079109 and 52009110) and Doctoral Innovation Fund of Xi’an University of Technology (No.252072009) and editors and reviewers for their hard work.

Author information

Authors and Affiliations

  1. State Key Laboratory of Eco-Hydraulics in Northwest Arid Region, Xi’an University of Technology, No. 5, Jinhua south road, Beilin district, Xi’an, 710048, Shaanxi, China

    Junhao Chen, Yanlong Li, Yang Li, Lifeng Wen & Hanyu Guo

Authors
  1. Junhao Chen
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Yanlong Li
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Yang Li
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Lifeng Wen
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Hanyu Guo
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Yanlong Li.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Chen, J., Li, Y., Li, Y. et al. Effects of curing conditions with different temperature and humidity on damage evolution of concrete during freeze–thaw cycling. Mater Struct 55, 80 (2022). https://doi.org/10.1617/s11527-022-01921-z

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1617/s11527-022-01921-z

Keywords

Search

Navigation