Enhanced mechanical properties of fiber reinforced concrete using closed steel fibers

  • Original Article
  • Published:
Materials and Structures Aims and scope Submit manuscript

Abstract

Concrete is weak in tension and fibers are added to it to make it ductile. One of the commonly used methods, for this purpose, is the addition of steel fibers of different geometries. However, failure of fiber reinforced concrete is initiated by pulling out of fibers, failing to utilize their full capacity. In this study, closed steel fibers (CSF) are proposed for addition into concrete. The objective was to avoid the pulling out of fibers in tension for full capacity utilization. When CSF are embedded into concrete, they are expected to reach the breaking point, utilizing their maximum capacity due to the presence of concrete matrix within the closed geometry of fibers. Different volumes of straight steel fibers (SSF) and CSF were used to investigate and compare their performance. Fresh and hardened concrete properties were considered. Results indicated decrease in workability of fiber reinforced concrete with increasing steel fiber content. No significant change in concrete compressive strength and modulus of elasticity was noted. There was a maximum of 46% increase in tensile strength while 36% increase in flexural strength of concrete with the use of CSF compared to that of SSF. The failure of concrete in tension was initiated by pulling out of open fibers and breaking of closed fibers. Thus, use of closed steel fibers is recommended to make full use of steel fiber tensile capacities which may revolutionize the field of fiber reinforced concrete.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

Similar content being viewed by others

References

  1. Lee JH, Cho B, Choi E (2017) Flexural capacity of fiber reinforced concrete with a consideration of concrete strength and fiber content. Constr Build Mater 138:222–231

    Article  Google Scholar 

  2. Lee JH (2017) Influence of concrete strength combined with fiber content in the residual flexural strengths of fiber reinforced concrete. Compos Struct 168:216–225

    Article  Google Scholar 

  3. Jamshidi M, Karimi M (2009) Characterization of polymeric fibers as reinforcements of cement-based composites. J Appl Polym Sci 115(5):2779–2785

    Article  Google Scholar 

  4. Brandt A (2008) Fibre reinforced cement-based (FRC) composites after over 40 years of development in building and civil engineering. Compos Struct 86(1–3):3–9

    Article  Google Scholar 

  5. Ivorra S, Garces P, Catala G, Andion LG, Zornoza E (2010) Effect of silica fume particle size on mechanical properties of short carbon fiber reinforced concrete. Mater Des 31(3):553–1558

    Article  Google Scholar 

  6. Alberti MG, Enfedaque A, Gálvez JC (2014) On the mechanical properties and fracture behavior of polyolefin fiber-reinforced self-compacting concrete. Constr Build Mater 55:274–288

    Article  Google Scholar 

  7. Kim MJ, Yoo DY, Kim S, Shin M, Banthia N (2018) Effects of fiber geometry and cryogenic condition on mechanical properties of ultra-high-performance fiber-reinforced concrete. Cem Concr Res 107:30–40

    Article  Google Scholar 

  8. Islam MS, Ahmed SJ (2018) Influence of jute fibers on concrete properties. Constr Build Mater 189:768–776

    Article  Google Scholar 

  9. Prisco MD, Lamperti M, Lapolla S, Khurana R (2008) HPFRCC thin plates for precast roofing. In: Proceedings of second international symposium on ultra high performance concrete

  10. Afroughsabet V, Biolzi L, Ozbakkaloglu T (2017) Influence of double hooked-end steel fibers and slag on mechanical and duribility properties of high performance recycle aggregate concrete. Compos Struct 181:273–284. https://doi.org/10.1016/j.compstruct.2017.08.086

    Article  Google Scholar 

  11. Leone M, Centonze G, Colonna D, Micelli F, Aiello MA (2018) Fiber-reinforced concrete with low content of recycled steel fiber: shear behaviour. Constr Build Mater 161:141–155

    Article  Google Scholar 

  12. Abbass W, Khan MI, Mourad S (2018) Evaluation of mechanical properties of steel fiber reinforced concrete with different strengths of concrete. Constr Build Mater 168:556–569

    Article  Google Scholar 

  13. Iqbal S, Ali A, Holschemacher K, Bier TA (2015) Mechanical properties of steel fiber reinforced high strength lightweight self-compacted concrete (SHLSCC). Constr Build Mater 98:325–333

    Article  Google Scholar 

  14. Farhan NA, Sheikh MN, Hadi MNS (2018) Behaviour of ambient cured streel fiber reinforced geopolymer concrete columns under axial and flexural loads. Structures 15:184–195. https://doi.org/10.1016/j.istruc.2018.07.001

    Article  Google Scholar 

  15. Mahmood SMF, Agarwal A, Foster SJ, Valipour H (2018) Flexural performance of steel fiber reinforced concrete beams designed for moment redistribution. Eng Struct 177:695–706

    Article  Google Scholar 

  16. Iqbal S, Ali A, Holschemacher K, Bier TA, Shah AA (2016) Strengthening of RC beams using steel fiber reinforced high strength lightweight self-compacting concrete (SHLSCC) and their strength prediction. Mater Des 100:37–46

    Article  Google Scholar 

  17. Breitenbücher R, Meschke G, Song F, Zhan Y (2014) Experimental analytical and numerical analysis of the pullout behaviour of steel fibres considering different fibre types inclinations and concrete strengths. Struct Concr 15:126–135

    Article  Google Scholar 

  18. Isla F, Ruano G, Luccioni B (2015) Analysis of steel fibers pull-out Experimental study. Constr Build Mater 100:183–193

    Article  Google Scholar 

  19. Yoo DY, Kim S, Park GJ, Park JJ, Kim SW (2017) Effects of fiber shape, aspect ratio, and volume fraction on flexural behavior of ultra-high-performance fiber-reinforced cement composites. Compos Struct 174:375–388

    Article  Google Scholar 

  20. Wille K, Kim DJ, Naaman AE (2011) Strain-hardening UHP-FRC with low fiber contents. Mater Struct 44(3):583–598

    Article  Google Scholar 

  21. Wu Z, Shi C, He W, Wu L (2016) Effects of steel fiber content and shape on mechanical properties of ultra high performance concrete. Constr Build Mater 103:8–14

    Article  Google Scholar 

  22. Zile E, Zile O (2013) Effect of fiber geometry on the pullout response of mechanically deformed steel fibers. Cem Concr Res 44:18–24

    Article  Google Scholar 

  23. Bhutta A, Farooq M, Zanotti C, Banthia N (2017) Pull-out behavior of different fibers in geopolymer mortars: effects of alkaline solution concentration and curing. Mater Struct 50(1):1–13

    Article  Google Scholar 

  24. Nguyen DL, Kim DJ (2014) Compressive behavior of ultra-high-performance fiber-reinforced concretes with steel fibers. Korea Concr Inst Spring Conv 945–946

  25. Hassan AMT, Jones SW, Mahmud GH (2012) Experimental test methods to determine the uniaxial tensile and compressive behaviour of ultra high performance fibre reinforced concrete (UHPFRC). Constr Build Mater 37:874–882

    Article  Google Scholar 

  26. Alsaif A, Koutas L, Bernal SA, Guadagnini M, Pilakoutas K (2018) Mechanical performance of steelf fiber reinforced concrete for flexible concrete pavements. Constr Build Mater 172:533–543

    Article  Google Scholar 

  27. Cecini D, Austin SA, Cavalaro S, Palmeri A (2018) Accelerated electric curing of steel-fiber reinforced concrete. Constr Build Mater 189:192–204

    Article  Google Scholar 

  28. Khan M, Cao M, Ali M (2018) Effect of Basal fibers on mechanical properties of calcium carbonate whisker-steel fiber reinforced concrete. Constr Build Mater 192:742–753

    Article  Google Scholar 

  29. ASTM C143/C143 M-15a (2015) Standard test method for slump of hydraulic-cement concrete, ASTM International, West Conshohocken, PA. www.astm.org

  30. ASTM C138/C138 M-17a (2017) Standard test method for density (unit weight), yield, and air content (gravimetric) of concrete, ASTM International, West Conshohocken, PA. www.astm.org

  31. ASTM C192/C192 M-16a (2016) Standard practice for making and curing concrete test specimens in the laboratory, ASTM International, West Conshohocken, PA. www.astm.org

  32. ASTM C39/C39 M-18 (2018) Standard test method for compressive strength of cylindrical concrete specimens, ASTM International, West Conshohocken, PA. www.astm.org

  33. ASTM C496/C496 M-17 (2017) Standard test method for splitting tensile strength of cylindrical concrete specimens, ASTM International, West Conshohocken, PA. www.astm.org

  34. ASTM C469/C469 M-14 (2014) Standard test method for static modulus of elasticity and Poisson’s ratio of concrete in compression, ASTM International, West Conshohocken, PA. www.astm.org

  35. ASTM C1609/C1609 M-12. Standard test method for flexural performance of fiber-reinforced concrete (using beam with third-point loading), ASTM International, West Conshohocken, PA. www.astm.org

  36. Mazaheripour H, Ghanbarpour S, Mirmoradi SH, Hosseinpour I (2011) The effect of polypropylene fibers of the properties of fresh and hardened lightweight self-compacting concrete. Constr Build Mater 25:351–358

    Article  Google Scholar 

  37. Altun F, Aktas B (2013) Investigation of reinforced concrete beams behavior of steel fiber added lightweight concrete. Constr Build Mater 38:575–581

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Civil Engineering, Sarhad University of Science and Information Technology, Peshawar, Pakistan

    Shahid Iqbal

  2. Department of Civil Engineering, CECOS University of IT and Emerging Sciences, Peshawar, Pakistan

    Ihsan Ali

  3. Department of Civil Engineering Technology, University of Technology, Nowshera, Pakistan

    Shah Room

  4. Faculty of Engineering, Abasyn University, Peshawar, Pakistan

    Shaukat Ali Khan

  5. Department of Civil Engineering, Quaid-e-Awam University College of Engineering, Science and Technology, Larkana, Pakistan

    Ahsan Ali

Authors
  1. Shahid Iqbal
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Ihsan Ali
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Shah Room
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Shaukat Ali Khan
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Ahsan Ali
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Shah Room.

Ethics declarations

Conflict of interest

The authors declare that they have no conflict of interest.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Iqbal, S., Ali, I., Room, S. et al. Enhanced mechanical properties of fiber reinforced concrete using closed steel fibers. Mater Struct 52, 56 (2019). https://doi.org/10.1617/s11527-019-1357-6

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1617/s11527-019-1357-6

Keywords

Search

Navigation