Plastic shrinkage cracking of concrete incorporating mineral admixtures and its mitigation

  • Original Article
  • Published:
Materials and Structures Aims and scope Submit manuscript

Abstract

In recent years, there has been a rapid increase in the use of mineral admixtures for high performance and durable concrete. Plastic shrinkage cracking in such concretes is a serious concern in large surface area/volume applications. The present study has two objectives: firstly, to investigate the influence of incorporating fly ash and granulated blast furnace slag (GGBS) on the susceptibility to such cracking; and secondly, to assess the techniques, such as fibre and shrinkage reducing admixture (SRA) addition, and spraying of curing compounds, to mitigate the cracking. The results indicate that replacement of ordinary Portland cement (OPC) with fly ash and GGBS increases the possibility of plastic shrinkage cracking significantly, with higher severity as the replacement level increases; 30% replacement of OPC with fly ash and GGBS doubled and quadrupled the crack area, respectively, mainly due to higher binder finesses, and the delay of setting and strength gain. Among the fibres tested, polypropylene and polyester fibres, at the recommended dosages of about 0.9 kg/m3, completely eliminated cracking in the most affected concrete (i.e., with 30% GGBS) while the dosages of the polyacrylonitrile and glass fibres had to be increased to provide a higher volume fraction. Two glycol-based SRAs, and two curing compounds based on acrylic resin and methacrylate mitigated cracking by significantly reducing evaporation from the surface of concrete.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

Similar content being viewed by others

References

  1. Uno PJ (1998) Plastic shrinkage cracking and evaporation formulas. ACI Mater J 95(4):365–375

    Google Scholar 

  2. Powers TC (1960) Physical properties of cement paste and concrete. In: Proceedings of the fourth international symposium on the chemistry of cement, Washington, DC, pp 577–608

  3. Ghourchian S, Wyrzykowski M, Baquerizo L, Lura P (2018) Susceptibility of Portland cement and blended cement concretes to plastic shrinkage cracking. Cement Concr Compos 85:44–55

    Article  Google Scholar 

  4. Banthia N, Gupta R (2006) Influence of polypropylene fibre geometry on plastic shrinkage cracking in concrete. Cem Concr Res 36(7):1263–1267

    Article  Google Scholar 

  5. Leemann A, Nygaard P, Lura P (2014) Impact of admixtures on the plastic shrinkage cracking of self-compacting concrete. Cement Concr Compos 46:1–7

    Article  Google Scholar 

  6. Nasir M, Al-Amoudi OSB, Maslehuddin M (2017) Effect of placement temperature and curing method on plastic shrinkage of plain and pozzolanic cement concretes under hot weather. Constr Build Mater 152:943–953

    Article  Google Scholar 

  7. Wongtanakitcharoen T, Naaman AE (2006) Unrestrained early age shrinkage of concrete with polypropylene, PVA, and carbon fibres. Mater Struct 40(3):289–300

    Article  Google Scholar 

  8. Dias WPSÃ (2003) Influence of mix and environment on plastic shrinkage cracking. Mag Concr Res 55(4):385–394

    Article  Google Scholar 

  9. Banthia N, Gupta R (2009) Plastic shrinkage cracking in cementitious repairs and overlays. Mater Struct 42:567–579

    Article  Google Scholar 

  10. Wang K, Shah SP, Phuaksuk P (2002) Plastic shrinkage cracking in concrete materials—influence of fly ash and fibres. ACI Mater J 98(6):458–464

    Google Scholar 

  11. Banthia N, Yan C, Mindess S (1996) Restrained shrinkage cracking in fibre reinforced concrete: a novel test technique. Cem Concr Res 26(1):9–14

    Article  Google Scholar 

  12. Boghossian E, Wegner LD (2008) Use of flax fibres to reduce plastic shrinkage cracking in concrete. Cement Concr Compos 30(10):929–937

    Article  Google Scholar 

  13. Combrinck R, Boshoff WB (2013) Typical plastic shrinkage cracking behaviour of concrete. Mag Concr Res 65(8):486–493

    Article  Google Scholar 

  14. Naaman AE, Wongtanakitcharoen T, Hauser G (2005) Influence of different fibres on plastic shrinkage cracking of concrete. Cem Concr Res 36(7):1263–1267

    Google Scholar 

  15. Pelisser F, Neto ABSS, Rovere HLL, Pinto RCA (2010) Effect of the addition of synthetic fibers to concrete thin slabs on plastic shrinkage cracking. Constr Build Mater 24(11):2171–2176

    Article  Google Scholar 

  16. Qi C, Weiss J, Olek J (2003) Characterization of plastic shrinkage cracking in fibre reinforced concrete using image analysis and a modified Weibull function. Mater Struct 36(260):386–395

    Article  Google Scholar 

  17. Sanjuán MA, Moragues A (1997) Polypropylene-fibre-reinforced mortar mixes: optimization to control plastic shrinkage. Compos Sci Technol 57(6):655–660

    Article  Google Scholar 

  18. Lura P, Mazzotta GB, Rajabipour F, Weiss J (2006) Evaporation, settlement, temperature evolution, and development of plastic shrinkage cracks in mortars with shrinkage-reducing admixtures. In: Proceedings of the international RILEM-JCI seminar on concrete durability and service life planning (Ein-Bokek, Israel), pp 203–213

  19. Lura P, Pease BJ, Mazzotta G, Rajabipour F, Weiss J (2007) Influence of shrinkage-reducing admixtures on development of plastic shrinkage cracks. ACI Mater J 104(2):187–194

    Google Scholar 

  20. Mora J, Gettu R, Olazábal C, Martín MA (2001) Study of plastic shrinkage cracking in concrete due to high rates of evaporation. In: Banthia N, Sakai K, Gjørv OE (eds) Concrete under severe conditions: environment and loading (International conference, Vancouver). University of British Columbia, Vancouver, Canada, pp 1425–1432

  21. Mora-Ruacho J, Gettu R, Aguado A (2009) Influence of shrinkage-reducing admixtures on the reduction of plastic shrinkage cracking in concrete. Cem Concr Res 39:141–146

    Article  Google Scholar 

  22. Rongbing B, Jian S (2005) Synthesis and evaluation of shrinkage-reducing admixture for cementitious materials. Cem Concr Res 35(3):445–448

    Article  Google Scholar 

  23. Saliba J, Rozière E, Grondin F, Loukili A (2011) Influence of shrinkage reducing admixtures on plastic and long-term shrinkage. Cem Concr Compos 33(2):209–217

    Article  Google Scholar 

  24. Shah SP, Karagüler ME, Sarigaphuti M (1993) Effects of shrinkage-reducing admixtures on restrained shrinkage cracking of concrete. ACI Mater J 89(3):289–295

    Google Scholar 

  25. Xie XS, Tian F, Hong YH (2011) Experimental investigation into the impact of polypropylene fibres and SRA on the early crack resistance of concrete. Adv Mater Res 194–196:858–864

    Article  Google Scholar 

  26. Peyton S (2006) Curing practices to reduce plastic shrinkage in concrete bridge decks. M.S. thesis, University of Arkansas, USA

  27. ASTM Standard Designation C1579-13, Standard test method for evaluating plastic shrinkage cracking of restrained fibre reinforced concrete, West Conshohocken, Pennsylvania, USA

  28. Mora J, Gettu R, Olazábal C, Martín MA, Aguado A (2000) Effect of the incorporation of fibers on the plastic shrinkage of concrete. In: Rossi P, Chanvillard G (eds) Fibre-reinforced concretes (FRC), BEFIB’2000 (Lyon, France). RILEM Publications S.A.R.L., Cachan, pp 705–714

  29. Kronloff A, Leivo M, Sipari P (1995) Experimental study on the basic phenomena on shrinkage and cracking of fresh mortar. Cem Concr Res 25(8):1747–1754

    Article  Google Scholar 

  30. Sirajuddin M (2015) Plastic shrinkage cracking of concrete with mineral admixtures and its mitigation. M.S. thesis, IIT Madras, Chennai, India

  31. Kai Y, Mingquan Z, Bryan M, Changhui Y, Chong W, Xiaohong Z, Zhilu Z (2017) Investigations of effects of Portland cement fineness and alkali content on concrete plastic shrinkage cracking. Constr Build Mater 144:279–290

    Article  Google Scholar 

Download references

Acknowledgements

The work done here was conducted in the Construction Materials Laboratory at IIT Madras. BASF, Chryso, W.R. Grace, Bekaert, Dolphin, Reliance Industry Ltd. and Owens Corning are thanked for donating some of the materials used in this study.

Author information

Authors and Affiliations

  1. Department of Civil Engineering, Indian Institute of Technology Madras, Chennai, 600036, India

    Moghul Sirajuddin & Ravindra Gettu

Authors
  1. Moghul Sirajuddin
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Ravindra Gettu
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Moghul Sirajuddin.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Sirajuddin, M., Gettu, R. Plastic shrinkage cracking of concrete incorporating mineral admixtures and its mitigation. Mater Struct 51, 48 (2018). https://doi.org/10.1617/s11527-018-1173-4

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1617/s11527-018-1173-4

Keywords

Search

Navigation