Mix design for improved strength and freeze-thaw durability of pervious concrete fill in Pearl-Chain Bridges

Abstract

Pearl-Chain Bridges are an innovative precast arch bridge technology which can utilize pervious concrete as fill material. The present study investigates how the mix design of the pervious concrete fill can be influenced by use of an air-entraining admixture, a high-range water reducing admixture, fibers, and by internal curing using lightweight aggregate to best possibly meet the requirements for a fill material in Pearl-Chain Bridges. The 28-day compressive strength, splitting tensile strength, shear strength, permeability, and freeze-thaw durability were determined and compared for eight different mixture proportions using two different sizes of granite coarse aggregate and at two different water-to-cement ratios. The specimens had an average void content of 24–28 %. Specimens containing air entraining and high-range water reducing admixtures were most workable, as determined by fresh density, and thus the easiest to place. The addition of a high-range water reducing admixture and lightweight sand (expanded shale) for internal curing improved the 28-day compressive strength and splitting tensile strength. The coarse aggregate gradation had a large influence on permeability; however, all tested permeabilities were high enough to drain the rain from a 100-year rain event in Denmark. The air entraining agent dosage used was not sufficiently high to create the necessary protective air content in the cement paste, and the freeze-thaw durability of the specimens were generally poor for the utilized test procedure; however, the mix design containing lightweight sand showed improved freeze-thaw durability compared to the other mix designs.

This is a preview of subscription content, access via your institution.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9

References

  1. 1.

    Hertz KD (2015) Super-light SL-Deck elements with fixed end connections. In: Proceedings of fib symposium May 18–20, Copenhagen, pp 465–466

  2. 2.

    Hertz KD, Castberg A, Christensen J (2014) Super-light concrete decks for building floor slabs. Struct Concr J 15:522–529

    Article  Google Scholar 

  3. 3.

    Halding PS, Hertz KD, Schmidt JW (2015b) Precast Pearl-Chain concrete arch bridges. J Eng Struct 103:214–227

    Article  Google Scholar 

  4. 4.

    Lund MSM, Hansen KK, Truelsen R, Johansen L (2016) Pervious concrete fill in Pearl-Chain Bridges: using small-scale results in full-scale implementation. Constr Build Mater 106:404–414

    Article  Google Scholar 

  5. 5.

    IDA Wastewater Commission. Regional variation of extreme rain in Denmark—a new analysis, 1979–2005. Pamphlet No. 28. The Commission, Copenhagen (2006). ISBN: 87-7923-502-6. Danish

  6. 6.

    Tennis PD, Leming ML, Akers DJ (2004) Pervious concrete pavements. EB302.02, Portland Cement Association, Skokie. National Ready Mixed Concrete Association, Silver Spring

  7. 7.

    Schaefer VR, Wang K, Suleiman MT, Kevern JT (2006) Mix design development for pervious concrete in cold weather climates. National Concrete Pavement Technology Center and Iowa State University, Ames

    Google Scholar 

  8. 8.

    Kevern JT, Schaefer VR, Wang K, Suleiman ST (2008) Pervious concrete mixture proportions for improved freeze-thaw durability. J ASTM Int 5(2):1–12

    Google Scholar 

  9. 9.

    Kevern JT (2013) Reducing the curing requirements of pervious concrete using prewetted lightweight aggregate for internal curing [Internet]. University of Missouri-Kansas City, Kansas City. http://www.escsi.org/uploadedFiles/Technical_Docs/Internal_Curing/Pervious20Report20-20Kevern

  10. 10.

    Kevern JT, Biddle D, Cao Q (2015) Effect of macro-synthetic fibers on pervious concrete properties. J Mater Civil Eng 27(9):119–134. doi:10.1061/(ASCE)MT.1943-5533.0001213

    Article  Google Scholar 

  11. 11.

    National Ready Mixed Concrete Association (NRMCA). Freeze-thaw resistance of pervious concrete. NRMCA, Silver Spring (2004)

  12. 12.

    ASTM Standard C666/C666M-03. Standard test method for resistance of concrete to rapid freezing and thawing. ASTM International, West Conshohocken (2008). doi:10.1520/C0666_C0666M-03R08

  13. 13.

    Henderson V, Tighe S (2012) Evaluation of pervious concrete pavement performance in cold weather climates. Int J Pavement Eng. 13(3):197–208. doi:10.1080/10298436.2011.572970

    Article  Google Scholar 

  14. 14.

    ASTM Standard C150/C150M-12. Standard specification for portland cement. ASTM International, West Conshohocken (2012). doi:10.1520/C0150_C0150M-12

  15. 15.

    ASTM Standard C618-12a. Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete. ASTM International, West Conshohocken (2012). doi:10.1520/C061812a

  16. 16.

    ASTM Standard C311/C311-13. Standard test methods for sampling and testing fly ash or natural pozzolans for use in portland-cement concrete. ASTM International, West Conshohocken (2014). doi:10.1520/C0311-13

  17. 17.

    ASTM Standard C136-06. Standard test method for sieve analysis of fine and coarse aggregate. ASTM International, West Conshohocken (2006). doi:10.1520/C0136-06

  18. 18.

    ASTM Standard C29/C29M-09. Standard test method for bulk density (“unit weight”) and voids in aggregate. ASTM International, West Conshohocken (2009). doi:10.1520/C0029_C0029M-09

  19. 19.

    ASTM Standard C1761/C1761M-13b. Standard specification for lightweight aggregate for internal curing of concrete. ASTM International, West Conshohocken (2013). doi:10.1520/C1761_C1761M-13b

  20. 20.

    ASTM Standard C192/C192M-14. Standard practice for making and curing concrete test specimens in the laboratory. ASTM International, West Conshohocken (2014). doi:10.1520/C0192_C0192M-14

  21. 21.

    ASTM Standard C1688/C1688M-13. Standard test method for density and void content of freshly mixed pervious concrete. ASTM International, West Conshohocken (2013). doi:10.1520/C1688_C1688M-13

  22. 22.

    ASTM Standard C1754-12. Standard test method for density and void content of hardened pervious concrete. ASTM International, West Conshohocken (2012). doi:10.1520/C1754_C1754M-12

  23. 23.

    ASTM Standard C39/C39M-14a. Standard test method for compressive strength of cylindrical concrete specimens. ASTM International, West Conshohocken (2014). doi:10.1520/C0039_C0039M-14A

  24. 24.

    ASTM Standard C496/C496M-11. Standard test method for splitting tensile strength of cylindrical concrete specimens. ASTM International, West Conshohocken (2011). doi:10.1520/C0469_C0469M-14

  25. 25.

    Test Method No. Iowa 406-C: method of test for determining the shearing strength of bonded concrete. Lowa Department of Transportation, Des Moines (2000)

  26. 26.

    Kevern JT, Wang K, Schaefer VR (2010) Effect of coarse aggregate on the freeze-thaw durability of pervious concrete. J ASTM Int 22(2):469–475

    Google Scholar 

  27. 27.

    Shu X, Huang B, Wu H, Dong Q, Burdette AG (2011) Performance comparison of laboratory and field produced pervious concrete mixtures. Constr Build Mater 25:3187–3192

    Article  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to Mia S. M. Lund.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Lund, M.S.M., Kevern, J.T., Schaefer, V.R. et al. Mix design for improved strength and freeze-thaw durability of pervious concrete fill in Pearl-Chain Bridges. Mater Struct 50, 42 (2017). https://doi.org/10.1617/s11527-016-0907-4

Download citation

Keywords

  • Fill material
  • Freeze-thaw durability
  • Pearl-Chain Bridge
  • Permeability
  • Pervious concrete
  • Strength properties