Influence of mix parameters on pore properties and modulus of pervious concrete: an application of ultrasonic pulse velocity

Abstract

The major objective of this study was to understand the influence of mix parameters on pore properties and modulus of control and silica fume (SF) modified pervious concrete mixtures with an application of ultrasonic pulse velocity (UPV) technique in defining the structural and hydrological properties. A total of twenty-four different pervious concrete mixtures were prepared encompassing three aggregate gradations with four aggregate sizes, and two levels each of water-to-cement (WC) and cement-to-aggregate (CA) ratios. Additionally, 5 % SF was used as partial replacement for cement to produce twelve SF modified pervious concrete mixes. It was found that permeability mainly depends on mix variables such as WC and CA ratios, and gradations since these factors control the interconnected pore structure of the pervious concrete mixes. Based on the measured mix properties, permeability predictive equation was developed, which followed Weibull distribution, and was mathematical robust with very good statistical goodness of fit measures (R 2adj  > 0.80; S e/S y = 0.432). The equation was rational indicative of the fact that porosity alone might not always be significant in defining permeability of the pervious concrete. UPV test technique employing a set of 55 kHz transducers was used to determine dynamic modulus of elasticity (E d) of all mixes, which yielded UPV in the range of 2750–3400 m/s, and E d in the range of 11–19 GPa. The findings were encouraging in that the estimated moduli using UPV were rational, which was also testimonial of the fact that this technique can be confidently used in future in the periodic evaluation of in-service pervious concrete pavements without having to retrieve field cores.

This is a preview of subscription content, access via your institution.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11

References

  1. 1.

    Neithalath N, Sumanasooriya MS, Deo O (2010) Characterizing pore volume, sizes, and connectivity in pervious concretes for permeability prediction. Mater Charact 61:802–813

    Article  Google Scholar 

  2. 2.

    Huang B, Wu H, Shu X, Burdette EG (2009) Laboratory evaluation of permeability and strength of polymer-modified pervious concrete. Constr Build Mater 24:818–823

    Article  Google Scholar 

  3. 3.

    Yahia A, Kabagire D (2014) New approach to proportion pervious concrete. Constr Build Mater 62:38–46

    Article  Google Scholar 

  4. 4.

    Nguyen DH, Sebaibi N, Boutouil M, Leleyter L, Baurd F (2014) A modified method for the design of pervious concrete mix. Constr Build Mater 73:271–282

    Article  Google Scholar 

  5. 5.

    McCain GN, Dewoolkar MM (2009) Strength and permeability characteristics of porous concrete pavements. In: Transportation research board 88th annual meeting compendium of papers DVD, January 2009, Monograph Accession #: 01120148, Report/Paper Numbers: 09–2584. Washington, p 14

  6. 6.

    Tennis PD, Leming ML, Akers DJ (2004) Pervious concrete pavements, EB302.02. Portland Cement Association, National Ready Mixed Concrete Association, Skokie

    Google Scholar 

  7. 7.

    Ghafoori N, Dutta S (1995) Laboratory investigation of compacted no-fines concrete for paving materials. J Mater Civil Eng Am Soc Civil Eng 7(3):183–191

    Article  Google Scholar 

  8. 8.

    Chindaprasrit P, Hatanaka S, Chareerat T, Mishima N, Yuasa Y (2008) Cement paste characteristics and porous concrete properties. Constr Build Mater 22:894–901

    Article  Google Scholar 

  9. 9.

    Deo O, Neithalath N (2010) Compressive behavior of pervious concretes and a quantification of the influence of random pore structure features. Mater Sci Eng A 528:402–412

    Article  Google Scholar 

  10. 10.

    Yang J, Jiang G (2002) Experimental study on properties of pervious concrete pavement materials. Cem Concr Res 33:381–386

    Article  Google Scholar 

  11. 11.

    Huang B, Wu H, Shu X, Burdette EG (2009) Laboratory evaluation of permeability and strength of polymer-modified pervious concrete. Constr Build Mater 24:818–823

    Article  Google Scholar 

  12. 12.

    Gesoglu M, Guneyisi E, Khoshnaw G, Ipek S (2014) Investigating properties of pervious concretes containing waste tire rubbers. Constr Build Mater 63:206–213

    Article  Google Scholar 

  13. 13.

    Ibrahim A, Mahmoud E, Yamin M, Patibandla VC (2013) Experimental study on Portland cement pervious concrete mechanical and hydrological properties. Constr Build Mater 50:524–529

    Article  Google Scholar 

  14. 14.

    Lian C, Zhuge Y (2010) Optimum mix design of enhanced permeable concrete—an experimental investigation. Constr Build Mater 24:2664–2671

    Article  Google Scholar 

  15. 15.

    Pindado MA, Aguado A, Josa A (1999) Fatigue behavior of polymer modified porous concretes. Universitat Politècnica de Catalunya (UPC), School of Civil Engineering (ETSECCPB), Barcelona

    Google Scholar 

  16. 16.

    Chen Y, Wang K, Wang X, Zhou W (2013) Strength, fracture and fatigue of pervious concrete. Constr Build Mater 42:97–104

    MathSciNet  Article  Google Scholar 

  17. 17.

    Deo O, Neithalath N (2011) Compressive response of pervious concretes proportioned for desired porosities. Constr Build Mater 25:4181–4189

    Article  Google Scholar 

  18. 18.

    Jain AK, Chouhan JS (2011) Effect of shape of aggregate on compressive strength and permeability properties of pervious concrete. Int J Adv Eng Res Stud 1:120–126

    Google Scholar 

  19. 19.

    Cosic K, Korat L, Ducman V, Netinger I (2014) Influence of aggregate type and size on properties of pervious concrete. Constr Build Mater 78:69–76

    Article  Google Scholar 

  20. 20.

    Neithalath N, Weiss J, Olek J (2006) Predicting the permeability of pervious concrete (enhanced porosity concrete) from non-destructive electrical measurements. Purdue University, rmcfoundation.org

  21. 21.

    Sumanasooriya MS, Neithalath N (2011) Pore structure features of pervious concretes proportioned for desired porosities and their performance prediction. Cem Concr Compos 33:778–787

    Article  Google Scholar 

  22. 22.

    Haselbach LM, Valavala S, Montes F (2005) Permeability predictions for sand-clogged Portland cement pervious concrete pavement systems. J Environ Manag 81:42–49

    Article  Google Scholar 

  23. 23.

    Li H, Kayhanian M, Harvey JT (2013) Comparative field permeability measurement of permeable pavements using ASTM C1701 and NCAT permeameter methods. J Environ Manag 118:144–152

    Article  Google Scholar 

  24. 24.

    Deo O (2011) Influence of material structure on the structural and environmental properties of pervious concretes. PhD Thesis

  25. 25.

    Martin WD III, Kaye NB, Putman BJ (2014) Impact of vertical porosity distribution on the permeability of pervious concrete. Constr Build Mater 59:78–84

    Article  Google Scholar 

  26. 26.

    Qin Y, Yang H, Deng Z, He J (2015) Water permeability of pervious concrete is dependent on the applied pressure and testing methods. Adv Mater Sci Eng 2015:1–6

    Google Scholar 

  27. 27.

    Kuang X, Sansalone J, Ying G, Ranieri V (2010) Pore-structure models of hydraulic conductivity for permeable pavement. J Hydrol 399:148–157

    Article  Google Scholar 

  28. 28.

    Nagy PB, Adler L, Bonner BP (1990) Slow wave propagation in air-filled porous materials and natural rocks. J Acoust Soc Am 56:2504–2506

    Google Scholar 

  29. 29.

    Amini K, Lesak A, Adato J, Delatte N Using ultrasonic pulse velocity to predict properties and performance of pervious concrete. Transportation Research Board 93rd Annual meeting, Paper No. 14-2137

  30. 30.

    Delatte N, Miller D (2007) Portland cement pervious concrete pavement: field performance investigation on parking lot and roadway pavements. Final report, National Ready Mix Concrete Association

  31. 31.

    IS 12269:2013 Indian Standard, Ordinary Portland cement—53-grade specification, New Delhi

  32. 32.

    Perumal K, Sundararajan R Effect of partial replacement of cement with silica fume on the strength and durability characteristics of high performance concrete. In: 29th conference on our world in concrete & structures, Article Online Id: 100029050

  33. 33.

    Amudhavalli NK, Mathew J (2012) Effect of silica fume on strength and durability parameters of concrete. Int J Eng Sci Emerg Technol 3(1):28–35

    Google Scholar 

  34. 34.

    Ghutke VS, Bhandari PS Influence of silica fume on concrete, International Conference on Advances in Engineering & Technology – 2014 (ICAET 2014). IOSR J Mech Civil Eng (IOSR-JMCE), pp. 45–47. http://iosrjournals.org/iosr-jmce/papers/ICAET-2014/ce/volume-3/9.pdf?id=7622

  35. 35.

    Silica fume users manual- Technical Report, Report No.-FHWA-IF-05-016, Grant No.-DTFH61-99-X-00063, Federal Highway Administration, U S Department of Transportation

  36. 36.

    Putman BJ, Neptune AI (2011) Comparison of test specimen preparation techniques for pervious concrete pavements. Constr Build Mater 25(8):3480–3485

    Article  Google Scholar 

  37. 37.

    Bonicelli A, Giustozzi F, Crispino M (2015) Experimental study on the effects of fine sand addition on differentially compacted pervious concrete. Constr Build Mater 91(30):102–110

    Article  Google Scholar 

  38. 38.

    ASTM (2012) Standard test method for density and void content of hardened pervious concrete. ASTM C1754-12, West Conshohocken

  39. 39.

    ASTM (2009) Standard test method for pulse velocity through concrete. ASTM C597-09, West Conshohocken

  40. 40.

    Thomle J, Goede WG, Haselbach L (2009) Pervious concrete, Palouse basin water summit. Pullman. http://www.palousewatersummit.org/2009pbws_1615_thomle_goede_haselbach.pdf

  41. 41.

    Goede WG (2009) Pervious concrete: investigation into structural performance and evaluation of the applicability of existing thickness design methods. MS Thesis, Washington State University

Download references

Acknowledgments

The authors gratefully acknowledge the Government of India Ministry of Human Resource Development Department of Higher Education for financial support vide Future of Cities research project Grant Number F. No. 4-22/2014-TS.I, dated 23 January 2014.

Author information

Affiliations

Authors

Corresponding author

Correspondence to Krishna Prapoorna Biligiri.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Chandrappa, A.K., Biligiri, K.P. Influence of mix parameters on pore properties and modulus of pervious concrete: an application of ultrasonic pulse velocity. Mater Struct 49, 5255–5271 (2016). https://doi.org/10.1617/s11527-016-0858-9

Download citation

Keywords

  • Pervious concrete
  • Silica fume
  • Permeability
  • Ultrasonic pulse velocity
  • Water-to-cement ratio
  • Cement-to-aggregate ratio