Abstract
During a fire, concrete is submitted to very high temperatures which can lead to structural collapse. The aim of this research is to study the behaviour of mortar specimens made of Portland cement and ground granulated blast furnace slag (GGBFS) which are heated to 900 °C. The samples are submitted to compressive and flexural strength tests and the microstructure is analysed by thermogravimetric analysis (TG and DTA), analysis and mercury intrusion porosimetry. The results indicate that a substitution rate of Portland cement by GGBFS of over 50 % gives residual compressive strengths that, after heating to 600 °C, are close to initial strengths before heating. The greater quantities of bound water, an acceleration of the hydration process due to heating and a lower porosity for specimens with GGBFS explain this increase. At 900 °C, the strong degradation of the microstructure results in strengths of less than 20 % of the initial strengths for specimens with or without GGBFS. Also, after cooling, the GGBFS reduces lime rehydration because of the decomposition of the portlandite between 450 and 550 °C, thus avoiding the risk of concrete cracking.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Mendes A, Sanjayan J, Collins F (2007) Phase transformations and mechanical strength of OPC/Salg pastes submitted to high temperature. Mater Struct 41:345–350
Khoury GA (1992) Compressive strength of concrete at high temperature: a reassessment. Mag Concr Res 44(161):291–309
Noumowe A, Siddique R, Debicki G (2009) Permeability of high-performance concrete subjected to elevated temperature (600 °C). Constr Build Mater 23(5):1855–1861
Metha PK, Monterio PJM (1997) Concrete microstructure, properties and materials. Indian Concrete Institute, Chennai
Alonso C, Fernandez L (2004) Dehydration and rehydration processes of cement paste exposed to high temperature environments. J Mater Sci 39:3015–3024
Mindeguia JC (2009) Contribution expérimentale à la compression des risques d’instabilité thermique des bétons, Thesis of University of Pau and Des pays de l’Adour, pp 31–35
Lin WM, Lin TD, Powers LJ (1996) Microstructures of fire-damaged concrete. ACI Mater J 93(3):199–205
Bazant ZP, Kaplan MF (1996) Concrete at high temperatures: material properties and mathematical models. Pearson Education, Edinburgh
Michel M (2009) Accélération au laitier par du ciment sulfoalumineux. Thesis of the University of Lyon, Lyon, pp 57–70
Wang HY (2008) The effects of elevated temperature on cement paste containing GGBFS. Cem Concr Compos 30:992–999
Aydin S (2008) Development of a high-temperature-resistant mortar by using slag and pumice. Fire Saf J 43:610–617
Mendes A, Sanjayan J, Collins F (2009) Long-term progressive deterioration following fire exposure of OPC versus slag blended cement pastes. Mater Struct 42:95–101
Sarshar R, Khoury GA (1993) Material and environmental factors influencing the compressive strength of unsealed cement paste and concrete at high temperatures. Mag Concr Res 45:51–61
Poon CS, Azhar S, Anson M, Wong YL (2001) Comparison of the strength and durability performance of normal and high-strength pozzolanic concretes at elevated temperatures. Cem Concr Res 31(9):1291–1300
Sullivan PJE, Sharshar R (1992) Performance of concrete at elevated temperatures. Fire Technol 28(3):240–250
Swamy RN (1997) Design for durability and strength through the use of fly ash in concrete. ACI special publication 171:1–72
Lea FC, Stradling RE (1992) The resistance to fire of concrete and reinforced concrete. Engineering 144:341–344
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Delhomme, F., Ambroise, J. & Limam, A. Effects of high temperatures on mortar specimens containing Portland cement and GGBFS. Mater Struct 45, 1685–1692 (2012). https://doi.org/10.1617/s11527-012-9865-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1617/s11527-012-9865-7