Abstract
Three types of nanomechanical methods including static nanoindentation, modulus mapping and peak-force quantitative nanomechanical mapping (QNM) were applied to investigate the quantitative nanomechanical properties of the same indent location in hardened cement paste. Compared to the nanoindentation, modulus mapping and peak-force QNM allow for evaluating local mechanical properties of a smaller area with higher resolution. Beside, the ranges of elastic modulus distribution measured by modulus mapping and peak-force QNM are relatively greater than that obtained from nanoindentation, which may be due to a result of the shaper probe and local confinement effect between multiple phases. Moreover, the average value of elastic modulus obtained using peak-force QNM were consistent with those obtained by modulus mapping, while the different in modulus probability distribution could be related to the different nanomechancial theories and contact forces. The probability distributions of elastic modulus measured using nanomechanical methods to provide a basis for the different types of phases existing in cement paste. Based on the observation with high spatial resolution, cement paste can be likely found as nanocalse granular material, in which different submicron scale or basic nanoscale grain units pack together. It indicates that the peak-force QNM can effectively provide an effective insight into the nanostructure characteristic and corresponding nanomechanical properties of cement paste.
This is a preview of subscription content, access via your institution.















References
- 1.
Sobolev K, Shah SP. Nanotechnology of concrete: recent developments and future perspectives, American Concrete Institute, Detroit, SP-254, 2008
- 2.
Scrivener KL, Kirkpatrick RJ (2008) Innovation in use and research on cementitious material. Cem Concr Res 38(2):128–136
- 3.
Sanchez F, Sobolev K (2010) Nanotechnology in concrete—a review. Constr Build Mater 24:2060–2071
- 4.
Šavija B, Luković M, Hosseini SAS, Pacheco J, Schlangen E (2014) Corrosion induced cover cracking studied by X-ray computed tomography, nanoindentation, and energy dispersive X-ray spectrometry (EDS). Mater Struct. doi:10.1617/s11527-014-0292-9
- 5.
Mondal P, Shah SP, Marks LD (2008) Nanoscale characterization of cementitious materials. ACI Mater J 105(2):174–179
- 6.
Trtik P, Kaufmann J, Volz U (2012) On the use of peak-force tapping atomic force microscopy for quantification of the local elastic modulus in hardened cement paste. Cem Concr Res 42(1):215–221
- 7.
Jones CA, Grasley ZC, Ohlhausen JA (2012) Measurement of elastic properties of calcium silicate hydrate with atomic force microscopy. Cem Concr Compos 34(4):468–477
- 8.
Davydov D, Jirásek M, Kopecký L (2011) Critical aspects of nano-indentation technique in application to hardened cement paste. Cem Concr Res 41(1):20–29
- 9.
Sorelli L, Constantinides G, Ulm F-J, Toutlemonde F (2008) The nano-mechanical signature of ultra high performance concrete by statistical nanoindentation techniques. Cem Concr Res 38(12):1447–1456
- 10.
Wang XH, Jacobsen S, Lee SF, He JY, Zhang ZL (2010) Effect of silica fume, steel fiber and ITZ on the strength and fracture behavior of mortar. Mater Struct 43(1–2):125–139
- 11.
Syed Asif SA, Wahl KJ, Colton RJ, Warren OL (2001) Quantitative imaging of nanoscale mechanical properties using hybrid nanoindentation and force modulation. J Appl Phys 90(3):1192–1200
- 12.
Balooch G, Marshall GW, Marshall SH, Warren OL, Asif SAS, Balooch M (2004) Evaluation of a new modulus mapping technique to investigate microstructural features of human teeth. J Biomech 37(8):1223–1232
- 13.
Young TJ, Monclus MA, Burnett TL, Broughton WR, Ogin SL, Smith PA (2011) The use of the PeakForce™ quantitative nanomechanical mapping AFM-based method for high-resolution Young’s modulus measurement of polymers. Meas Sci Technol 22(12):125703
- 14.
Sahin O, Erina N (2008) High-resolution and large dynamic range nanomechanical mapping in tapping-mode atomic force microscopy. Nanotechnology 19(44):445717
- 15.
Oliver WC, Pharr GM (1992) Improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J Mater Res 7(6):1564–1583
- 16.
Constantinides G, Ulm F, Van Vliet K (2003) On the use of nanoindentation for cementitious materials. Mater Struct 36(3):191–196
- 17.
Constantinides G, Ulm F-J (2007) The nanogranular nature of C-S-H. J Mech Phys Solids 55(1):64–90
- 18.
Randall NX, Vandamme M, Ulm F-J (2009) Nanoindentation analysis as a two dimensional tool for mapping the mechanical properties of complex surfaces. J Mater Res 24(3):679–690
- 19.
Uskokovic PS, Tang CY, Tsui CP, Ignjatovic N, Uskokovic DP (2007) Micromechanical properties of a hydroxyapatite/poly-L-lactide biocomposite using nanoindentation and modulus mapping. J Eur Ceram Soc 27(2–3):1559–1564
- 20.
Vanlandingham MR, McKnight SH, Palmese GR, Elings JR, Huang X, Bogetti TA, Eduljee RF, Gillespie J (1997) Nanoscale indentation of polymer systems using the atomic force microscope. J Adhes 64(1–4):31–59
- 21.
Li WG, Xiao JZ, Kawashma S, Shekhawat GS, Shah SP (2014) Experimental investigation on quantitative nanomechanical properties of cement paste. ACI Mater J 111(1–6):603–612
- 22.
Miller M, Bobko C, Vandamme M, Ulm F-J (2008) Surface roughness criteria for cement paste nanoindentation. Cem Concr Res 38(4):467–476
- 23.
Li WG, Xiao JZ, Sun ZH, Kawashima S, Shah SP (2012) Interfacial transition zones in recycled aggregate concrete with different mixing approaches. Constr Build Mater 35:1045–1055
- 24.
Xiao JZ, Li WG, Sun ZH, Lange DA, Shah SP (2013) Properties of interfacial transition zones in recycled aggregate concrete tested by nanoindentation. Cem Concr Compos 37:276–292
- 25.
Jennings HM, Thomas JJ, Gevrenov JS, Constantinides G, Ulm F-J (2007) A multi-technique investigation of the nanoporosity of cement paste. Cem Concr Res 37(3):329–336
- 26.
Constantinides G, Ulm F-J (2004) The effect of two types of C-S-H on the elasticity of cement-based materials: results from nanoindentation and micromechanical modeling. Cem Concr Res 34(1):67–80
- 27.
Vandamme M, Ulm F-J, Fonollosa P (2010) Nanogranular packing of C-S-H at substochiometric conditions. Cem Concr Res 40(1):14–26
- 28.
Němeček J, Králík V, Vondřejc J (2013) Micromechanical analysis of heterogeneous structural materials. Cem Concr Compos 36:85–92
- 29.
da Silva WRL, Němeček J, Štemberk P (2014) Methodology for nanoindentation-assisted prediction of macroscale elastic properties of high performance cementitious composites. Cem Concr Compos 45:57–68
- 30.
Alizadeh R, Beaudoin JJ, Raki LR (2011) Mechanical properties of calcium silicate hydrates. Mater Struct 44(1):13–28
- 31.
Fonseca PC, Jennings HM, Andrade JE (2011) A nanoscale numerical model of calcium silicate hydrate. Mech Mater 43(8):408–419
- 32.
Masoero E, Del Gado E, Pellenq RJ-M, Ulm F-J, Yip S (2012) Nanostructure and nanomechanics of cement: polydisperse colloidal packing. Phys Rev Lett 109(15):155503
- 33.
Kim JH, Balogun O, Shah SP (2010) Atomic force acoustic microscopy to measure nanoscale mechanical properties of cement pastes. J Transp Res Board 2141:102–108
- 34.
Brehm D (2012) Size diversity in cement nanoparticles optimizes packing density to give concrete its strength, Department of Civil and Environmental Engineering (CEE) in MIT. http://newsoffice.mit.edu/2012/size-diversity-in-cement-nanoparticles-optimizes-packing-density-to-give-concrete-its-strength
- 35.
Peled A, Castro J, Weiss J (2010) Atomic force microscopy examinations of mortar made by using water-filled lightweight aggregate. J Transp Res Board 2141(1):92–101
Acknowledgments
The authors would like to gratefully acknowledge the National Natural Science Foundation of China (51408210), the Fundamental Research Funds for the Central Universities in Hunan University, China (531107040800) and the financial support from Infrastructure Technology Institute (ITI) at Northwestern University, USA under Grant DTRT06-G-0015. The first author is also grateful for the financial support of the Australian Research Council (DE150101751).
Author information
Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Li, W., Kawashima, S., Xiao, J. et al. Comparative investigation on nanomechanical properties of hardened cement paste. Mater Struct 49, 1591–1604 (2016). https://doi.org/10.1617/s11527-015-0597-3
Received:
Accepted:
Published:
Issue Date:
Keywords
- Hardened cement paste
- Nanoindentation
- Modulus mapping
- Peak-force quantitative nanomechanical mapping (QNM)
- Nanomechanical properties