Abstract
This study consisted of the characterization of longitudinal cracking pattern observed in weld joint in the manufacture of 304L steel pipelines with thin wall thickness by GTAW process. These tubes are used in food and automotive industries. The cracks grown in the liquid-solid interdendritic zones at high temperatures. It was found that the cracks are associated with change on solidification mode and presence of the holes produced by shrinkage. The change in the solidification mode was associated with the presence of second phase particles. The results suggest that the formation of cracks is promoted by increasing current during the welding although the heat input is constant.
Similar content being viewed by others
References
S. Kou. “Welding Metallurgy” (J. Willey 2003) p 457.
S. W. Shyu, H. Y. Huang, K. H. Tseng and C. P. Chou. J Mater. Engineering and Performance 17, 193–201 (2008).
Z. Li, H. Zhong, Q. Sun, Z. Xu and Q. Zhai. Materials Science and Engineering A 506, 191–195 (2009).
J. C. Lippold and D. J. Kotecki. “Welding Metallurgy and weldability of stainless steels”. (John Willey 2005) p357.
P. S. Korinko and S.H. Malene, ASM Intemational 4, 61–68 (2001).
A.Y. Jang, D.J. Lee, S.H. Lee, J.H. Shim, S.W. Kang, H.W. Lee, Materials & Design 32, 371–376 (2011).
R. Kacar, O. Baylan. Materials & Design 25, 317–329 (2004).
K.H. Lo, C.H. Shek, J.K.L. Lai. Materials Science and Engineering: R: Reports 65, 39–104(2009).
S. Kumar, A.S. Shahi. Materials & Design 32, 3617–3623 (2011).
Acknowledgments
The authors gratefully acknowledge the technical supports of COMIMSA and Tubos Samuel de México S.A. de C.V.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ruíz-Mondragón, J.J., Acevedo-Dávila, J., García-Vázquez, F. et al. Characterization of Metallurgical Defects in the Melt Zone of 304L Steel Tubes Manufactured by GTAW Process. MRS Online Proceedings Library 1372, 41–46 (2011). https://doi.org/10.1557/opl.2012.122
Published:
Issue Date:
DOI: https://doi.org/10.1557/opl.2012.122