Abstract
The microstructural rejuvenation through non-conventional heat treatments (NCHT) of a conventional cast superalloy Inconel 939 was investigated. The primary and secondary main constituents of the NCHT microstructures were characterized through its morphology and composition applying conventional microscopy and analytical scanning electron microscope (SEM). The results showed a complete rejuvenation of the overage microstructure (disordered coarse cuboids of 1.2μm from γ′, continuous films of M23C6 carbides and coarse MC carbides as well as γ-γ′ eutectics) into a more homogeneous microstructure; spherical ordered primary γ′ and secondary γ′ precipitates ranging between 357 to 442 nm and 30 to 50 nm respectively and depending on the applied heat treatment. Also blocky type MC and discreet M23C6 carbides dispersed within the dendrite and in the interdendritic regions were observed. There was no evidence of the formation of detrimental phases with the NCHT, which can affect the long-term properties of the alloy during service.
Similar content being viewed by others
References
S.W.K. Shaw, Superalloys, 275 (1980).
K.M. Delargy, S.W.K. Shaw and G.D.W. Smith, Mater. Sci. and Technol. 2, 1031 (1986).
Z. Miskovic, M. Jovanovic, M. Gligic and B. Lukic, Vacumm 43, 709 (1992).
C. Hammond and J. Nutting, Met. Sci., 474 (1977).
M.A. González, D.I. Martínez, A. Pérez and A. Garza, FIME-UANL, Mater. Res. Soc. Symp. P, 1275 (2010).
G. Lvov, V.I. Levit, and M.J. Kaufman, Metall. Mater. Trans. A, 35A, 1669 (2004).
P. Wangyao, V. Krongtong, W. Homkrajai, N. Panich, and G. Lothongkum, JOM-J. Min. Met. Mat. S. 17, 87 (2007).
Donald J. Tillack, James M. Manning and J.R. Hensley, Heat Treating of Nonferrous Alloys, (ASM Metals Handbook, 1991) pp. 907.
V. Krongtong, P. Tuengsook, W. Homkrajai, E. Nisaratanapor and P. Wangyao, Acta Metall. Slov. 11, 171 (2005).
P. Wangyao, N. Chuankrerkkul, S. Polsilapa, P. Sopon and W. Homkrajai, J. Sci. 36(3), 312 (2009).
R. Brooks, Heat Treatment, Structure and Properties of Nonferrous Alloys, (American Society for Metals, Ohio, 1982) pp. 139.
W. Hatala and J. Schirra, Superalloys, 137 (1996).
S.A. Sajjadi, H.R. Elahifar and H. Farhangi, J. Alloy. Compd. 455, 215 (2008).
P. Wangyao, J. Zrnik, I Mamuzic, S. Polsilapa, S. Klaijumrang, Metalurgija 46, 195 (2007).
S.A. Sajjadi, S.M. Zebarjad, R.I.L. Guthrie and M. Isac, J. Mater. Process. Tech. 175, 376 (2006).
R.F. Decker, Paul D. Merica Research Laboratory, Steel Strengthening Mechanism Symposium, 1 (1969).
E. Nembach, S. Schanzer, W. Scharer and K. Trinckauf, Acta Metall. 36, 1471 (1988).
Acknowledgments
The author would like to thank the CONACyT Mexico and the Paicyt as well as the Universidad Autonoma de Nuevo León for their financial support.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
González, M.A., Martínez, D.I., Pérez, A. et al. Microstructural Rejuvenation Through Non-conventional Heat Treatments of an Inconel 939 Superalloy. MRS Online Proceedings Library 1372, 89–96 (2011). https://doi.org/10.1557/opl.2012.114
Published:
Issue Date:
DOI: https://doi.org/10.1557/opl.2012.114