Abstract
CeO2 thin films as insulating layers for high-temperature superconducting digital devices were studied. The dependence on substrate temperature and oxygen pressure of the surface morphology and crystallinity of CeO2 thin films prepared by pulsed laser deposition were investigated. CeO2 thin films with a flat and closely grained surface were obtained at a relatively low oxygen pressure of 3.6 Pa, whereas higher oxygen pressure led to CeO2 thin films with a rough surface and columnar grains. The recovery of oxygen content in superconducting layers was examined for multilayer structures with CeO2 thin films. Enough oxygen was supplied to the upper and lower superconducting layers when the multilayer was cooled slowly in 3 × 10−4 Pa oxygen pressure after deposition. Resistively shunted junction type I-V characteristics were confirmed for interface-engineered ramp-edge junctions in a multilayer structure including four superconducting layers with CeO2 thin films.
Similar content being viewed by others
References
K.K. Likharev. and V.K. Semenov.: RSFQ logic/memory family: A new Josephson-junction thechnology for sub-terahertz-clock-frequency digital systems. IEEE Trans. Appl. Supercond. 1, 3 (1991).
Y. Soutome, T. Fukazawa, K. Saito, A. Tsukamoto and K. Takagi: HTS surface-modified junctions with integrated ground-planes for SFQ circuits. IEICE Trans. Electron. E85–C:3, 759 (2002).
H. Katsuno, S. Inoue, T. Nagano and J. Yoshida: A novel multilayer process for HTS SFQ circuit. IEEE Trans. Appl. Supercond. 13, 809 (2003).
H. Wakana, S. Adachi, H. Sugiyama, Y. Takahashi, T. Sugano, M. Horibe, Y. Ishimaru, Y. Tarutani and K. Tanabe: Ramp-edge junctions with interface-modified barriers fabricated on YBCO thick films. IEEE Trans. Appl. Supercond. 13, 595 (2003).
H. Katsuno, T. Nagano, S. Inoue, J. Yoshida: Development of the fabrication process for HTC SFQ circuits (2). Extended Abstracts, 49th Spring Meeting, Jpn. Soc. Appl. Phys. 28a-ZD-2 (in Japanese).
A. Kamitani, H. Wakana, S. Adachi and K. Tanabe: Investigation of BaZrO3 and SrZrO3 insulating layers on La-YBCO ground plane for high-Tc devices. Physica C 412, 1414 (2004).
A. Kamitani, H. Wakana, S. Adachi, Y. Nakajima, K. Higuchi, H. Yamamoto and K. Tanabe: Examination of MgO insulator thin films for high-Tc superconducting devices. Physica C (in press).
M. Hidaka, M. Maruyama and T. Sato: Single flux quantum (SFQ) sampler made of high-Tc superconductor. Ins. Electron. Inf. Commun. Eng. J86–C, 1128 2003, (in Japanese).
M.A.A.M. van Wijck, M.A.J. Verhoeven, E.M.C.M. Reuvekamp, G.J. Gerritsma., D.H.A. Blank and H. Rogalla: CeO2 as insulating layer in high Tc superconducting multilayer and crossover structures. Appl. Phys. Lett. 68, 553 (1996).
H. Sato, R. Miyakawa, N. Nakamura, S.R. Gjoen., H. Akoh and S. Takada: YBa2Cu3Ox crossover structures using CeO2 film as insulating layer. Jpn. J. Appl. Phys. 35, L311 (1996).
A. Tsukamoto, T. Fukazawa, Y. Soutome, Y. Tarutani and K. Takagi: Faburication of YBCO/CeO2/YBCO crossover and via structures for digital circuit and integrated SQUID applications. Supercond. Sci. Technol. 12, 1001 (1999).
H. Wakana, S. Adachi, A. Kamitani, K. Nakayama, Y. Ishimaru, Y. Tarutani and K. Tanabe: Development of thin film multilayer structures with smooth surface for HTS SFQ circuits. IEICE Trans. Electron. E88–C.2, 208 (2005).
S. Adachi, H. Wakana, M. Horibe, N. Inoue, T. Sugano and K. Tanabe: Preparation of La-doped Yb-123 thin films for high-Tc devices. Physica C 378–381, 1213 (2002).
A. Kamitani, S. Adachi, H. Wakana and K. Tanabe: Improvement in crystal orientation and in-plane alignment of La-doped YBCO thin film on BaZrO3-buffered MgO substrate. J. Mater. Res. 20, 1529 (2005).
B.H. Moeckley. and K. Char: Properties interface-engineered high Tc Josephson junctions. Appl. Phys. Lett. 71, 2526 (1997).
T. Sato, M. Hidaka and S. Tahara: High-temperature superconducting edge-type Josephson junctions with modified interfaces. IEEE Trans. Appl. Supercond. 9, 3141 (1999).
H. Wakana, S. Adachi, M. Horibe, Y. Ishimaru, O. Horibe, Y. Tarutani and K. Tanabe: Influence of counter-layer deposition condition on critical current spread in interface-modified ramp-edge junction arrays. Jpn. J. Appl. Phys. 2 Lett. 41, L239 (2002).
D.J. Lichtenwalner., O. Auciello, R. Dat and A.I. Kingon.: Investigation of the ablated flux characteristics during pulsed laser ablation deposition of multicomponent oxides. J. Appl. Phys. 74, 7497 (1993).
X. Fang, M. Tachiki and T. Kobayashi: Excimer-laser abration of RuO2 observed by a streak camera. J. Appl. Phys. 85, 2492 (1999).
Author information
Authors and Affiliations
Corresponding author
Additional information
Address all correspondence to this author.
This author was an editor of this journal during the review and decision stage. For the JMR policy on review and publication of manuscripts authored by editors, please refer to http://www.mrs.org/publications/jmr/policy.html.
Rights and permissions
About this article
Cite this article
Kamitani, A., Wakana, H., Ogawa, A. et al. CeO2 insulating films for application to high-temperature superconducting digital devices. Journal of Materials Research 21, 263–269 (2006). https://doi.org/10.1557/jmr.2006.0026
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/jmr.2006.0026