Abstract
The synthesis of Y2Ti2O7-Al2O3 compositional (multiphase) ceramics from powder mixtures Al2O3-Y2O3-TiO2 was carried out in two stages: 1) under the traditional sintering and then 2) in regime of directed laser heating. It was established that the sintering of mixtures with different content of components and the ratio of TiO2/Y2O3 = 2.34 in ceramic specimens the main phases are Y2Ti2O7 and α-Al2O3. The content of the main phases in ceramic materials also depends upon the oxide content in the initial mixtures. In ceramics the Y3Al5O12 is formed only at sufficiently high content of titanium and yttrium oxides in initial mixtures. In laser remelting, the phase composition is substantially different from that obtained at the traditional sintering, and depends on the mode of laser heating: irradiation power and the moving speed of the laser beam (i.e., heating temperature). Under certain conditions of laser remelting can be obtained superficial ceramic layer with crystallographic directional crystallization of Y2Ti2O7 and Al2O3 crystallites. The size of crystallites and the coefficient texturing also depend on the mode of laser treatment.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
N.A. Toropov, Diagrams of a state of silicate systems, 2nd ed. (Nauka, Leningrad, 1969).
M. Vlasova, M. Kakazey, P.A. Marquez Aguilar, V. Stetsenko, A. Bykov and S. Lakiza, J. Alloys and Compounds. S199–S204, 586(2014).
Q. Lou, J. Zhou, Y. Qi and H. Cai, Laser Applications of Transparent Polycrystalline Ceramic, Chapter 20, Ed. Costas Sikalidis (Advances in Ceramics - Synthesis and Characterization, Processing and Specific Applications, 2011) pp. 447–478.
J. Sanghera, W. Kim, G. Villalobos, B. Shaw, C. Baker, J. Frantz, B. Sadowski, and I. Aggarwal, Materials. 5, 258–277 (2012).
YanyanGuo, Dianyuan Wang, Xin Zhao and Fang Wang, Mater. Res. Bull. 73, 84–89 (2016).
Pengpeng Dai, Xintong Zhang, Meng Zhou, Xinghua Li, Jikai Yang, Panpan Sun, Changshan Xu and Yichun Liu, J. Am. Ceram. Soc. 95, 658–662 (2012).
S. Ochiai, M. Hojo, A. Mitani, N. Nakagawa, S. Sakata, K. Sato, T. Takahashi, T. Ueda and Y. Waku, Compos. Sci. Technol. 61, 2117–2128 (2001).
T. A. Parthasarathy, T. Mah and L. E. Matson, J. Ceram. Process. Res. 5, 380–390 (2004).
M. Vlasova, P. A. Márquez Aguilar, M. Kakazey, A. Escobar Martinez and R. Guardian Tapia, J. Advanc. Microscopy Research, 10, 303–313 (2015).
M. Vlasova, P. A. Márquez Aguilar, A. Escobar Martinez, M. Kakazey, R. Guardian Tapia and A. Trujillo Estrada, Appl. Surf. Sci. 377, 416–425 (2016).
S.P. Harimkar and N.B. Dahotre, J. Appl. Phys. 100 (2) 024901–024901–6 (2006).
S. Ruppi, Int. J. Refract. Met. Hard Mater. 23 (4–6), 306–316 (2005).
M. Vlasova, M. Kakazey, P.A. Marquez Aguilar, R. Guardian Tapia, V. Stetsenko, A. Bykov and S. Lakiza, Advanc. Ceram. Sci. and Engineering 2 (3), (2013).
P. A. Márquez Aguilar, M. Vlasova, S. Lakiza‚ M. Kakazey, A. Bykov and V. Stetsenko, Advanc. in Sci.andTechn. 88, 74–79 (2014).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Márquez Aguilar, P.A., Vlasova, M., Kakazey, M. et al. Phase Transformation in Zone of Laser Treatment of Y2Ti2O7-Al2O3 Compositional Ceramics. MRS Advances 2, 3831–3836 (2017). https://doi.org/10.1557/adv.2017.606
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2017.606