Abstract
For the first time, we are reporting the growth of high quality single crystalline 3C-SiC epitaxially on hexagonal silicon carbide substrates using Hot Filament Chemical Vapor Deposition (HF-CVD) on full 4” wafers. Rocking curve X-Ray diffraction (XRD) measurements resulted in a full width at half maximum (FWHM) as low as 88 arcsec for a 40 µm thick layer. We achieved this quality using a carefully optimized process making use of the additional degrees of freedom the hot filaments create. The filaments allow for precursor pre-cracking and a tuning of the vertical thermal gradient, which creates an improved thermal field compared to conventional Chemical Vapor Deposition. Growth rates of up to 8 µm/h were achieved with standard silane and propane chemistry, and further increased to 20 µm/h with chlorinated chemistry. The use of silicon carbide substrates promises superior layer quality compared to silicon substrates due to their better match in lattice parameters and thermal expansion coefficients. High resolution scanning electron microscopy, X-Ray rocking measurements, and micro-Raman allow us to assess the crystalline quality of our material and to compare it to layers grown on low-cost silicon substrates. Hall measurements reveal a linear increase of the charge carrier density in the material with the flow of nitrogen gas as a dopant. Electron densities above 10-18 cm-3 have been reached.
Similar content being viewed by others
References
A. Severino, “3C-SiC epitaxial growth on large area silicon: Thin films,” Silicon Carbide Epitaxy, 2012: 145–191 ISBN: 978-81-308-0500-9 Chapter 7, Editor: Francesco La Via
Z. Wu et. al., “Epitaxial growth of SiC films at low temperature and its photoluminescence,“ IEEE proceedings Solid State and Integrated Circuit Technology (2006)
K. Yasui et. al., “Low-Temperature Heteroepitaxial Growth of SiC on (100) Si Using Hot-Mesh Chemical Vapor Deposition,” Japanese Journal of Applied Physics Vol. 44, No. 3 (2005), 1361–1364
H-Y. Mao et. al., “Hot-Wire chemical vapor deposition and characterization pf p-type nanocrystalline SiC films and their use in Si heterojunction solar cells,” Thin Solid Films 520 (2012), 2110–2114
Z. Zhang et al., “Epitaxial monocrystalline SiC films grown on Si by HFCVD at 780°C,” Materials Science and Engineering B75 (2000), 177–179
J. Robbins and M. Seman, “Production of bulk silicon carbide with hot-filament chemical vapor deposition,” United States Patent # 8,409,351, Issued April 2, 2013
S. Nakashima et. al., “Raman Investigation of SiC Polytypes,” phys. stat. sol. (a) 162 (1997), 39
H. Pedersen et. al., “Chloride-Based CVD Growth of Silicon Carbide for Electronic Applications” Chem. Rev., 2012, 112 (4), 2434–2453
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hens, P., Brow, R., Robinson, H. et al. Hot Filament CVD epitaxy of 3C-SiC on 6H and 3C-SiC substrates. MRS Advances 2, 289–294 (2017). https://doi.org/10.1557/adv.2017.20
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2017.20