Low Temperature Oxidation of Silicon(100) Substrates Using Atomic Oxygen


Low temperature oxidation process of Si(100) substrates using atomic oxygen has been proposed. For the generation of atomic oxygen, microwave plasma remotely attached on the oxidation chamber was used. In the microwave plasma, the large amount of rare gas and a small amount of O2 gas mixture was supplied. The existence of the large amount of rare gas controls the plasma energy to some restricted values associated with the metastable states of the rare gas. Consequently, using Kr as mixed rare gas, atomic oxygen were efficiently generated instead of excited O2 molecules with any vibrational or ionized states. The oxidation kinetics of crystalline Si using this process was shown to be diffusion limiting, even if the oxide thickness was less than several nm. The activation energy of B, which is referred to as the parabolic rate constant, was found to be as low as 0.14eV. In addition, lower interface trap density of 2.6 × 1011/cm2/eV at the mid gap could be achieved for the as-grown SiO2/Si(100) interface at the processing temperature of 500C.

This is a preview of subscription content, access via your institution.


  1. [1]

    J.R. Ligenza: J.Appl.Phys. 36(1965)2703.

    CAS  Article  Google Scholar 

  2. [2]

    J. Kraitchman: J.Appl.Phys. 38(1967)4323.

    Article  Google Scholar 

  3. [3]

    T. Sugano: Thin Solid Films 92(1982)19.

    CAS  Article  Google Scholar 

  4. [4]

    C. Martinet and R.A.B. Devine: Appl.Phys.Lett. 67(1995)3500.

    CAS  Article  Google Scholar 

  5. [5]

    K. Watanabe, S. Kimura and T. Tatsumi: Jpn.J.Appl.Phys. 38(1999)L1055.

    CAS  Article  Google Scholar 

  6. [6]

    Y.W. Choi and B.T. Ahn- J.Appl.Phys. 86(1999)4004.

    CAS  Article  Google Scholar 

  7. [7]

    P.W. Milonni and J.H. Eberly: Lasers, John Wiley&Sons, New York, 1988, pp. 425.

    Google Scholar 

  8. [8]

    C.E. Moore. Atomic Energy Levels, NSRDS-NBS, Washington D.C., 1971.

    Google Scholar 

  9. [9]

    B.E. Deal and A.S. Grove: J.Appl.Phys. 36(1965)3770.

    CAS  Article  Google Scholar 

  10. [10]

    J.K. Franklin, J.G. Dillard, H.M. Rosenstock, J.T. Herron, K. Draxl and F.H. Field. Ionization Potentials, Appearance Potentials, and Heats of Formation of Gaseous Positive Ions, NSRDS-NBS, Washington D.C., 1969.

    Book  Google Scholar 

  11. [11]

    E.H. Nikollian and J.R. Brews: MOS Physics and Technology, John Wiley and Sons Inc., New York, 1982, pp.331.

    Google Scholar 

Download references

Author information



Corresponding author

Correspondence to Τ. Ueno.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Ueno, Τ., Chikamura, S., Sakuraba, F. et al. Low Temperature Oxidation of Silicon(100) Substrates Using Atomic Oxygen. MRS Online Proceedings Library 592, 246–250 (1999). https://doi.org/10.1557/PROC-592-239

Download citation