Abstract
Electronic transport parallel and perpendicular to growth direction has been studied in a series of microcrystalline silicon samples obtained by various dilutions of silane in hydrogen. It is clearly shown that the transport properties (dark conductivity, drift mobility, ambipolar diffusion length and photoconductivity) under dark and under illumination conditions are enhanced as the dilution is increased. Furthermore, these films exhibit no degradation upon light-soaking. X-Ray diffraction patterns of the samples confirm that there is a correlation between the amount of crystalline fraction in the samples and the transport properties, as well as a preferential orientation along the growth direction. A similar correlation is found with the shift of the Si-H stretching mode peak of the infrared spectra (IR). Because transport properties have been measured by different techniques (dark conductivity, ambipolar length and photoconductivity in the direction perpendicular to growth direction, drift mobility in the direction parallel to growth direction), no statement can be made about a possible anisotropy in transport, as it would be expected from the columnar shape of the crystallites.
Similar content being viewed by others
References
J. Meier, P. Torres, R. Platz, S. Dubail, U. Kroll, J. A. Anna Selvan, N. Pellaton Vaucher, Ch. Hof, D. Fischer, H. Keppner, A. Shah, K.-D. Ufert, P. Giannoulès and J. Koehler, Mat. Res. Soc. Symp. Proc. 420, 3 (1996).
H. Curtins, N. Wyrsch, M. Favre and A. V. Shah, Plasma chem. & Plasma Proc. 7, 267 (1987).
J. Meier, S. Dubail, R. Flückiger, D. Fischer, H. Keppner and A. Shah, Proc. of the 1st WCPEC, Hawaii, USA, 409 (1994).
P. Torres, J. Meier, R. Flückiger, U. Kroll, J. A. Anna Selvan, H. Keppner, A. Shah, S. D. Littelwood, I. E. Kelly, P. Giannoulés, Appl. Phys. Lett. 69, 1373 (1996).
N. Beck, P. Torres, J. Fric, Z. Remeš A. Poruba, H. Stuchlíková, A. Fejfar, N. Wyrsch, M. Vanaěček, J. Kočka and A. Shah, to be published in Mat. Res. Soc. Symp. Proc., Fall meeting, Boston (1996).
E. Sauvain, Ph. D. Thesis, Université de Neuchâtel, (1992).
M. Stutzmann, W. B. Jackson and C. C Tsai, Phys. Rev. B 32, 23 (1985).
H. Liu and M. Xu, Sol. Stat. Comm. 58, 601 (1986).
D. Ritter, E. Zeldov and K. Weiser, Appl. Phys. Lett. 49, 791 (1986).
I. Balberg, A. E. Delahoy and H. A. Weakliem, Appl. Phys. Lett. 53, 992 (1988).
M. Goerlitzer, N. Beck, P. Torres, J. Meier, N. Wyrsch and A. Shah, J. Appl. Phys. 80, 5111 (1996).
N. Wyrsch, M. Goerlitzer, N. Beck, J. Meier and A. Shah, Mat. Res. Soc. Symp. Proc. 420, 801 (1996).
H. Keppner et al., to be published in Mat. Res. Soc. Symp. Proc, Fall meeting, Boston (1996).
U. Kroll, J. Meier, A. Shah, S. Mikhailov and J. Weber, J. Appl. Phys. 80, 4971 (1996).
H. Wagner and W. Beyer, Solid State Commun. 48, 587 (1983).
Y. J. Chabal, E. E. Chaban and S. B. Christman, J. Electron Spectrosc. Relat. Phenom. 29, 35 (1983).
Y. J. Chabal, Phys. Rev. Lett. 50, 1850 (1983).
T. Satoh and A. Hiraki, J. Appl. Phys. 24, L491 (1985).
U. Kroll, J. Meier, H. Keppner, S. D. Littlewood, I. E. Kelly, P. Giannoulès and A. Shah, Mat. Res. Soc. Symp. Proc. 377, 39 (1995).
Acknowledgement
This work was supported by the Swiss National Science Foundation under FN-45696 and by the Swiss Federal Office of Energy under Research grant 19431.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Goerlitzer, M., Beck, N., Torres, P. et al. Electronic transport and structure of microcrystalline silicon deposited by the VHF-GD technique. MRS Online Proceedings Library 467, 301–306 (1997). https://doi.org/10.1557/PROC-467-301
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-467-301