Abstract
Micro-tensile specimens of coarse-grained Ti52at%Al crystals have been deformed in situ in a high voltage electron microscope at room temperature. In addition to some twinning, “simple” 1/2〈110] dislocations as well as superdislocations were moving, with the simple dislocations prevailing even if their orientation factor is lower than that of the superdislocations. Both types of dislocations are pinned, probably by small precipitates having a distance along the dislocations of about 100 nm. The precipitates consist most probably of Al2O3. Under stress, the dislocations bow out between the obstacles. The bowing is stronger for 1/2〈110] dislocations. An effective stress of about 41 MPa is estimated from their curvature. The kinematic behaviour of the dislocations is in accord with precipitation hardening. The dislocations are generated by the double-cross slip mechanism. Their density within the slip bands corresponds to a long-range internal stress of about 40 MPa. These data are consistent with the flow stress of PST crystals in the easy orientation, taken from the literature.
Similar content being viewed by others
References
G. Hug, A. Loiseau and P. Veyssière, Philos. Mag. A 57, 499 (1988).
B.H. Kear and H.G.E. Wilsdorf, Trans. Metall. Soc. A.I.M.E. 224, 382 (1962).
Y.G. Zhang, M.C. Chaturvedi and C.Q. Chen, Philos. Mag. A 67, 979 (1993).
S.A. Court, V.K. Vasudevan and H.L. Fraser, Philos. Mag. A 61, 141 (1990).
M.M. Morris, Philos. Mag. A 68, 237 (1993).
M.M. Morris, Philos. Mag. A 68, 259 (1993).
S. Farenc, D. Caillard and A. Couret, Proc. 6th Int. Symp. on Intermetallic Compounds, Structure and Mechanical Properties (Tokyo, 1991), p. 791.
S. Farenc and A. Couret, in High-Temperature Ordered lntermetallic Alloys V, edited by I. Baker et al. (Mater. Res. Soc. Proc. 288, Pittsburgh, PA, 1993), p. 465.
S. Farenc, A. Coujou and A. Couret, Philos. Mag. A 67, 127 (1993).
T.P. Johnson, N.E. Jesper, J.M. Young, R.M. Ward, and M.H. Jacobs, in Euromat 93, edited by R. Pichoir and P. Costa (Les Editions de Physique, Paris, 1993), Vol. I, p. 371.
U. Messerschmidt and F. Appel, Ultramicroscopy 1, 223 (1976).
U. Messerschmidt, Z. Metallkunde 84, 6 (1993).
M.H. Yoo (private communication).
C.L. Fu and M.H. Yoo, Philos. Mag. A 62, 159 (1990).
J.S. Koehler, Phys. Rev. 86, 52 (1952).
E. Orowan, in Dislocations in Metals, edited by M. Cohen (Amer. Inst. Mining and Metall. Eng., New York, 1954), p. 103.
W.G. Johnston and J.J. Gilman, J. Appl. Phys. 31, 632 (1960).
M. Yamaguchi, Y. Umakoshi and T. Yamane, in Dislocations in Solids, edited by H. Suzuki et al. (Univ. of Tokyo Press, Tokyo, 1985), p. 77.
B.A. Greenberg, V.I. Anisimov, Ya.N. Gornostirev, and G.G. Taluts, Scr. Metall. 22, 859 (1988).
S. Naka (private communication)
W.H. Tian. T. Sano and M. Nemoto, Philos. Mag. A 68, 965 (1993).
Y.W. Kim, J. Metals 41, 24 (1989).
S.C. Huang and E.L. Hall, in High-Temperature Ordered lntermetallic Alloys III, edited by C.T. Liu et al. (Materials Res. Soc. Proc. 133, Pittsburgh, PA, 1989), p. 373.
R.O. Scattergood and D.J. Bacon, Philos. Mag. 31, 179 (1975).
M. Yamaguchi, H. Inui, Y. Shirai, K. Kishida, and K. Ito, in Strength of Materials, edited by H. Oikawa, K. Maruyama, S. Takeuchi, and M. Yamaguchi (Jap. Inst. of Metals, 1994), p. 33.
F. Louchet and B. Viguier, Scripta Metall. Mater. 31, 369 (1994).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Messerschmidt, U., Bartsch, M., Häussler, D. et al. Dislocation Motion in λ Tial Studied by in situ Straining Experiments in the Hvem. MRS Online Proceedings Library 364, 47–52 (1994). https://doi.org/10.1557/PROC-364-47
Published:
Issue Date:
DOI: https://doi.org/10.1557/PROC-364-47