Micrqporous Silica Gels from Alkylsilicate-Water Two Phase Hydrolysis


Microporous silica gels have been synthesized through a nano-particulate sol-gel route. These gels have uniformly distributed and extremely small pores(< 15Â in diameter). Hydrolysis and condensation reactions leading to these gels were carried out in an alkyl silicate-water (ammonia) two phase system. These reactions took place at the alkyl silicate droplet-water interfacial boundary. No alcohol was added. A clear, stable and uniformly distributed colloidal silica suspension having an average particle size less than 6 nm was prepared by this method. Fast hydrolysis, slow condensation and low solubility all contribute to a high supersaturation level and result in the formation of small particles. This process is consistent with classic nucleation theory. When the particles are produced under acidic rather than under basic reaction conditions, smaller particles are formed due to the slower condensation rate and lower solubility of these silica particles in acidic conditions. At the same pH, alkylsilicates having smaller alkyl groups react faster with water leading to smaller primary particles. Homogeneous nucleation conditions are achieved when the water/alkylsilicate ratio is high.

This is a preview of subscription content, access via your institution.

Literature Cited

  1. 1

    M.K. Titulaer, J.B.H. Jansen and J.W. Geus, J. Non-Cryst. Solids, 168, 1–13 (1994).

    CAS  Article  Google Scholar 

  2. 2

    M.A. Anderson and L. Chu, U. S. Patent No. 5 194 200 (16 Mar. 1993).

  3. 3

    Q. Xu and M.A. Anderson; J. mater. Reseach. 6, 1073–1081 (1991).

    CAS  Article  Google Scholar 

  4. 4

    L.C. Klein and N. Giszpenc, American Ceramic Soc. Bull., 69, 1821–1825 (1990).

    CAS  Google Scholar 

  5. 5

    R.J. Uhlhorn, K. Keizer and A.J. Burggraaf, J. Membr. Sci., 66, 271 (1992).

    CAS  Article  Google Scholar 

  6. 6

    A. Julbe, C. Guizard, A. Larbot, L. Cot and, A. Giroir-Fendier, J. Membr. Sci. 77, 2–3, 137-153 (1993).

    Article  Google Scholar 

  7. 7

    B.E. Yoldas, J. Non-Cryst. Solids, 51, 105 (1982).

    CAS  Article  Google Scholar 

  8. 8

    P.K. Her. The Chemistry Of Silica. (Wiley Interscience, New York, 1979).

    Google Scholar 

  9. 09

    C.J. Brinker and G.W. Scherer, Sol-Gel Science. (Academic Press, Boston, 1990).

    Google Scholar 

  10. 10

    W. Stöber, E. Fink and E. Bohn, J.Colloid And Interface Sci. 26, 62 (1968).

    Article  Google Scholar 

  11. 11

    C.J. Brinker, K.D. Keefer, D.W. Schaefer and C.S. Ashley, J. Non-Cryst, Solids, 48, 47 (1982).

    CAS  Article  Google Scholar 

  12. 12

    S. Sakka, K. Aoki, RKozoka and J. Yamaguchi, J. Mater. Sci., 28, 4607–4614 (1993).

    CAS  Article  Google Scholar 

  13. 13

    A.K. Van Helden, J.W. Jansen and A. Vrij, J.Colloid and Interface Sci., 81 (1980).

    Google Scholar 

  14. 14

    A. van Blaaderen and A.P.M. Kentgens, J.Non-Cryst, Solids, 149, 161 (1992).

    Article  Google Scholar 

  15. 15

    A. Kaiser and H. Schmidt, J.Non-Cryst, Solids, 63, 261(1984).

    CAS  Article  Google Scholar 

  16. 16

    D. Avnir and V.R. Kaufman, J.Non-Cryst, Solids, 192, 180(1987).

    Article  Google Scholar 

  17. 17

    F.F. Abraham, Homogeneous Nucleation theory: (New York, Academic Press, 1974).

    Google Scholar 

  18. 18

    A.G. Walton, The Formation and Properties of Precipitation: (New York, Interscince Publishers,1967).

    Google Scholar 

  19. 19

    A.E. Nielsen, Kinetics of Precipitation. (The macmillan company, 1964).

    Google Scholar 

  20. 20

    G.H. Bogush, C.J. Brinker, P.D. Majors and D.M. Smith, (Mater. Res. Soc. Symp. Proc. Vol. 180, Materials research society,1990), p.491

    Google Scholar 

Download references

Author information



Corresponding author

Correspondence to L. Chu.

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Chu, L., Tejedor-Tejedor, M.I. & Anderson, M.A. Micrqporous Silica Gels from Alkylsilicate-Water Two Phase Hydrolysis. MRS Online Proceedings Library 346, 855–860 (1994). https://doi.org/10.1557/PROC-346-855

Download citation