Abstract
We report a new Mg-based bulk metallic glass-forming alloy: Mg65Cu7.5Ni7.5Zn5 Ag5Y10. The alloy exhibits a glass-forming ability significantly stronger than all previously discovered Mg-based glass formers. Fully glassy rods 9 mm in diameter can be obtained by using copper mold casting. The critical cooling rate for glass formation was estimated to be <50 Ks−1. The reduced glass-transition temperature (Trg) of the glass was determined to be 0.59.
Similar content being viewed by others
References
W.L. Johnson, Mater. Res. Soc. Bull. 24(10), 42 (1999).
A. Inoue, Acta Mater. 48, 279 (2000).
A. Inoue and A. Takeuchi, Mater. Trans. 43, 1892 (2002).
A. Inoue, A. Kato, T. Zhang, S.G. Kim, and T. Masumoto, Mater. Trans. JIM 32, 609 (1991).
A. Inoue, T. Nakamura, N. Nishiyama, and T. Masumoto, Mater. Trans. JIM 33, 937 (1992).
R. Busch, W. Liu, and W.L. Johnson, J. Appl. Phys. 83, 4134 (1998).
H.G. Kang, E.S. Park, W.T. Kim, D.H. Kim, and H.K. Cho, Mater. Trans. JIM 41, 846 (2000).
E.S. Park, H.G. Kang, W.T. Kim, and D.H. Kim, J. Non-Cryst. Solids 279, 154 (2001).
H. Men, Z.Q. Hu, and J. Xu, Scripta Mater. 46, 699 (2002).
K. Amiya and A. Inoue, Mater. Trans. JIM 41, 1460 (2000).
K. Amiya and A. Inoue, Mater. Trans. JIM 42, 543 (2001).
X.H. Lin and W.L. Johnson, J. Appl. Phys. 78, 6514 (1995).
D. Turnbull, Contemp. Phys. 10, 473 (1969).
Z.P. Lu, Y. Li, and S.C. Ng, J. Non-Cryst. Solids. 270, 103 (2000).
S.S. Murty and K. Hono, Mater. Trans. JIM 41, 1538 (2000).
H.S. Chen and D. Turnbull, Acta Metall. 17, 1021 (1969).
A. Inoue, Mater. Trans. JIM 36, 866 (1995).
T.A. Wanliuk, J. Schroers, and W.L. Johnson, Appl. Phys. Lett. 78, 1213 (2001).
A. Inoue, W. Zhang, T. Zhang, and K. Kurosaka, Acta Metall. 49, 2645 (2001).
A. Inoue, T. Zhang, and T. Masumoto, J. Non-Cryst. Solids 156–158, 473 (1993).
A.L. Greer, Nature 366, 303 (1993).
P.J. Desré, Mater. Trans. JIM 38, 583 (1997).
T. Egami, Mater. Trans. 43, 510 (2002).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ma, H., Ma, E. & Xu, J. A new Mg65Cu7.5Ni7.5Zn5Ag5Y10 bulk metallic glass with strong glass-forming ability. Journal of Materials Research 18, 2288–2291 (2003). https://doi.org/10.1557/JMR.2003.0319
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2003.0319