Abstract
The microstructure of Ag-doped La2/3Sr1/3MnO3 (LSMO) thin films deposited on (001) LaAlO3 single-crystal substrates was systematically investigated in cross section and plan view by high-resolution electron microscopy and analytical electron microscopy. The results showed that the films deposited at 750 °C were perfectly epitaxial with or without Ag-doping. No Ag in the doped film was detected. On the other hand, the LSMO films deposited at 400 °C were less perfect. With increasing Ag-doping level, the shape of LSMO grains became irregular, and the grain size increased gradually. Large polycrystalline clusters consisting of LSMO, AgO, and Ag grains formed in the doped films, and the amount and size of them increased with increasing Ag-doping level. Ag existed at the LSMO grain boundaries in its elemental state. A growth process for the LSMO-Ag system is discussed based on the experimental results. The enhancement of the magnetic spin disorders at the grain boundaries and interfaces caused by doping Ag could result in an improvement of low-field magnetoresistance.
Similar content being viewed by others
References
J.M.D. Coey, J. Appl. Phys. 85, 5576 (1999).
H.R. Khan, Mater. Sci. Forum 373–376, 93 (2001).
C. Zener, Phys. Rev. 82, 403 (1951).
H.Y. Hwang, S-W. Cheong, N.P. Ong, and B. Batlogg, Phys. Rev. Lett. 77, 2041 (1996).
A. Gupta, G.Q. Gong, G. Xiao, P.R. Duncombe, P. Lecoeur, P. Trouilloud, Y.Y. Wang, V.P. Dravid, and J.Z. Sun, Phys. Rev. B 54, 15629 (1996).
X.W. Li, A. Gupta, G. Xiao, and G.Q. Gong, Appl. Phys. Lett. 71, 1124 (1997).
J.Y. Gu, C. Kwon, M.C. Robson, Z. Trajanovic, K. Ghosh, and R.P. Sharma, Appl. Phys. Lett. 70, 1763 (1997).
H.L. Ju and H. Sohn, Solid State Commun. 102, 463 (1997).
T. Walter, K. Dörr, K-H. Müller, B. Holzapfel, D. Eckert, M. Wolf, D. Schläfer, L. Schultz, and R. Grötzschel, Appl. Phys. Lett. 74, 2218 (1999).
N.D. Mathur, G. Burnell, S.P. Isaac, T.J. Jackson, B-S. Teo, J.L. MacManus-Driscoll, L.F. Cohen, J.E. Evetts, and M.G. Blamire, Nature 387, 266 (1997).
C. Kwon, Q.X. Jia, Y. Fan, M.F. Hundley, D.W. Reagor, J.Y. Coulter, and D.E. Peterson, Appl. Phys. Lett. 72, 486 (1998).
C.J. Lu, Z.L. Wang, G.C. Xiong, and G.J. Lian, J. Mater. Res. 15, 2454 (2000).
D. Kumar, M. Sharon, R. Pinto, P.R. Apte, S.P. Pai, S.C. Purandare, L.C. Gupta, and R. Vijayaraghavan, App. Phys. Lett. 62, 3522 (1993).
A.Z. Moshfegh, Y.Q. Wang, Y.Y. Sun, A. Mesarwi, P.H. Hor, and A. Ignatiev, Physica C 218, 396 (1993).
R. Pinto, P.R. Apte, S.P. Pai, and D. Kumar, Physica C 207, 13 (1993).
D. Kumar, M. Sharon, P.R. Apte, R. Pinto, S.P. Pai, S.C. Purandare, C.P. D’Souza, L.C. Gupta, and R. Vijayaraghavan, J. Appl. Phys. 76, 1349 (1994).
R. Kalyanaraman, S. Oktyabrsky, and J. Narayan, J. Appl. Phys. 85, 6636 (1999).
R. Shreekala, M. Rajeswari, S.P. Pai, S.E. Lofland, V. Smolyaninova, K. Ghosh, S.B. Ogale, S.M. Bhagat, M.J. Downes, R.L. Greene, R. Ramesh, and T. Venkatesan, Appl. Phys. Lett. 74, 2857 (1999).
T. Tao, Q.Q. Cao, K.M. Gu, H.Y. Xu, S.Y. Zhang, and Y.W. Du, Appl. Phys. Lett. 77, 723 (2000).
R. Bathe, K.P. Adhi, S.I. Patil, G. Marest, B. Hannoyer, and S.B. Ogale, Appl. Phys. Lett. 76, 2104 (2000).
C.K. Ong, S.Y. Xu, and W.Z. Zhou, Rev. Sci. Instrum. 69, 3659 (1998).
Q. Zhan, R. Yu, L.L. He, D.X. Li, and X.N. Guo, Acta Metall. Sin. 37, 337 (2001).
O.I. Lebedev, G. Van Tendeloo, S. Amelinckx, H.L. Ju, and K.M. Krishnan, Philos. Mag. A 80, 673 (2000).
R. Von Helmot, J. Wecker, K. Samwer, L. Haupt, and K. Bärner, J. Appl. Phys. 76, 6925 (1994).
J.A. Kerr, in CRC Handbook of Chemistry and Physics 1999–2000, edited by D.R. Lide (CRC Press, Boca Raton, FL, 1998).
R. Pinto, P.R. Apte, K.P. Adhi, S.B. Ogale, D. Kumar, and M.S. Hegde, J. Appl. Phys. 78, 5204 (1995).
J. Li, Q. Huang, Z.W. Li, L.P. You, S.Y. Xu, and C.K. Ong, J. Phys.: Condens. Matter 13, 3419 (2001).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhan, Q., Yu, R., He, L.L. et al. The effect of doping Ag on the microstructure of La2/3Sr1/3MnO3 films. Journal of Materials Research 17, 2712–2719 (2002). https://doi.org/10.1557/JMR.2002.0392
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2002.0392