Abstract
Room-temperature ductility of two Ti–Al–Nb intermetallic alloys with close chemical compositions was investigated by tensile testing. The two alloys’ ductilities in the B2 single-phase state were significantly different, which indicated that the ductility of B2 phase state was sensitive to the chemical composition. The alloy with more ductile B2 phase exhibited higher ductility in O + B2 two-phase state.
Similar content being viewed by others
References
D. Banerjee, Prog. in Mater. Sci. 42, 135 (1997).
A.K. Gogia, T.K. Nandy, D. Banerjee, T. Carisey, J.L. Strudel, and J.M. Franchet, Intermetallics 6, 741 (1998).
D. Banerjee, in Intermetallic Compounds: Vol. 2 Practice, edited by J.H. Westbrook and R.L. Fleischer (John Wiley & Sons, New York, 1995), p. 91.
R.G. Rowe, D.G. Konitzer, A.P. Woodfield, and J.C. Chesnutt, in High Temperture Ordered Intermetallics IV, edited by L.A. Johnson, D.P. Pope, and J.O. Stiegler (Mater. Res. Soc. Symp. Proc. 213, Pittsburgh, PA, 1991), p. 703.
T.K. Nandy, R.S. Mishra, A.K. Gogia, and D. Banerjee, Scripta Metall. Mater. 32, 851 (1995).
T.K. Nandy and D. Banerjee, Intermetallics 8, 915 (2000).
C.J. Boehlert and D.B. Miracle, Metall. Mater. Trans. A 30A, 2349 (1999).
F. Tang, S. Emura, and M. Hagiwara, Scripta Mater. 44, 671 (2001).
F. Tang, S. Nakazawa, and M. Hagiwara, Scripta Mater. 43, 1065 (2000).
F. Tang, S. Nakazawa, and M. Hagiwara, Mater. Sci. Eng. A 325A, 194 (2002).
Y. Mao, S. Li, J. Zhang, J. Peng, D. Zou, and Z. Zhong, Intermetallics 8, 659 (2000).
S. Takaki, CAMP-ISIJ 12, 1150 (1999).
S.V. Kamat, A.K. Gogia, and D. Banerjee, Acta Mater. 46, 239 (1998).
M.H. Loretto, D. Hu, and Y.G. Li, Intermetallics 8, 1243 (2000).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Tang, F., Hagiwara, M. Effect of compositional modification on ductility of B2 phase in Ti–Al–Nb intermetallic alloy. Journal of Materials Research 17, 2611–2614 (2002). https://doi.org/10.1557/JMR.2002.0378
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2002.0378