Abstract
The texture development during cold rolling and recrystallization of L12-type Co3Ti alloys was investigated as functions of alloy composition and rolling reduction. Two kinds of fully annealed Co3Ti alloys with different alloy compositions (Co77Ti23 and Co78Ti22), whose initial textures and grain sizes were almost identical, were used. After 70% reduction, the cold-rolling textures of both alloys were composed of strong α-fiber and weak β-fiber textures, in which the intensity of {011}〈211〉 orientation was higher than those of {112}〈111〉 and {123}〈634〉 orientations, indicating that texture transition from copper type to brass type occurred in cold-rolled Co3Ti alloys. This texture transition was more prominently recognized in the Co78Ti22 alloy, whose chemical composition was more off-stoichiometric. On the other hand, the recrystallization textures of both alloys were considerably weak, and their orientation spreads were more significant with increasing rolling reduction. Also, the recrystallization textures were basically independent of alloy composition in contrast to the rolling textures.
Similar content being viewed by others
References
K. Aoki and O. Izumi, J. Japan Inst. Met. 43, 1190 (1979).
T. Takasugi and O. Izumi, Acta Metall. 33, 39 (1985).
T. Takasugi, M. Nagashima, and O. Izumi, Acta Metall. Mater. 38, 747 (1990).
G. Gottstein, P. Nagpal, and W. Kim, Mater. Sci. Eng. A108, 165 (1989).
H. Inoue and N. Inakazu, in Proc. Int. Symp. on Intermetallic Compounds—Structure and Mechanical Properties—(JIMIS-6), edited by O. Izumi (The Japan Institute of Metals, Sendai, Japan 1991), pp. 785, 789.
J. Ball and G. Gottstein, Intermetallics 1, 171 (1993).
J. Ball and G. Gottstein, Intermetallics 1, 191 (1993).
C. Escher, S. Neves, and G. Gottstein, Acta Mater. 46, 441 (1998).
S.G. Chowdhury, R.K. Ray, and A.K. Jena, Mater. Sci. Eng. A277, 1 (2000).
B. Bhattacharya and R.K. Ray, Metall. Mater. Trans 31A, 3011 (2000).
T. Takasugi and O. Izumi, Acta Metall. 33, 49 (1985).
H.Y. Yasuda, S. Yamamura, and Y. Umakoshi, Scripta Mater. 44, 765 (2001).
T. Takasugi, S. Rikukawa, and S. Hanada, Acta Metall. Mater. 40, 1985 (1992).
Y. Kaneno, M. Wada, H. Inoue, and T. Takasugi, Mater. Trans. 42, 418 (2001).
J.L. Murray, Binary Alloy Phase Diagrams, edited by T.B. Massalski, J.L. Murray, L.H. Bennet, and H. Baker (American Society for Metals, Metals Park, OH, 1986), p. 803.
M. Dahms and H.J. Bunge, J. Appl. Cryst. 22, 439 (1989).
H. Inoue and N. Inakazu, J. Japan Inst. Metals 58, 892 (1994).
J. Hirsch and K. Lücke, Acta Metall. 36, 2863 (1988).
F.J. Humphreys and M. Hatherly, Recrystallization and Related Annealing Phenomena (Elsevier Science, Oxford, U.K., 1995), p. 44.
H. Hu, R.S. Cline, and S.R. Goodman, Recrystallization, Grain Growth and Textures (American Society for Metals, Metals Park, OH, 1966), p. 295.
Y. Liu, T. Takasugi, O. Izumi, and T. Takahashi, Acta Metall. 36, 2959 (1988).
T. Takasugi and O. Izumi, Acta Metall. 33, 33 (1985).
Y. Liu, T. Takasugi, O. Izumi, and T. Takahashi, Philos Mag. A 59, 437 (1989).
B.H. Kear and H.G.F. Wilsdorf, Trans. Metall. Soc. AIME 224, 382 (1962).
W.B. Hutchinson, F.M.C. Besag, and C.V. Honess, Acta Metall. 21, 1685 (1973).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kaneno, Y., Nakaaki, I. & Takasugi, T. Cold rolling and recrystallization textures in L12-type Co3Ti ordered alloys. Journal of Materials Research 17, 2567–2577 (2002). https://doi.org/10.1557/JMR.2002.0373
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2002.0373