Abstract
We examined the densification of 12CaO · 7Al2O3 (C12A7), which has a microporous lattice framework with a cavity of approximately 0.4 nm. Fully densified translucent ceramics are obtained when hydrated C12A7 powders prepared as precursors are sintered in a dry oxygen atmosphere at 1300 °C. The average transmittance between 400–800 nm for 1-mm-thick samples is improved up to approximately 70% with a 48-h increase in the sintering time. Dissociation of water molecules at the grain–pore interface into grains which entraps hydroxide ions in the crystallographic cage, and the release of the hydroxide ions into the atmosphere during the sintering procedure are considered to play crucial roles in the pore-annihilation processes.
Similar content being viewed by others
References
J. Jeevaratnam, F.P. Glasser, and L.S.D. Glasser, J. Am, Ceram. Soc. 47, 105 (1964).
R.W. Nurse, J.H. Welch, and A.J. Majumdar, Trans. Br. Ceram. Soc. 64, 323 (1965).
G.I. Zhmoidin and A.K. Chatterjee, Cement Conc. Res. 14, 386 (1984).
K. Hayashi, M. Hirano, S. Matsuishi, and H. Hosono, J. Am. Chem. Soc. 124, 738 (2002).
R.N. Edmonds and A.J. Majumdar, Cement Conc. Res. 18, 473 (1988).
M. Lacerda, J.T.S. Irvine, F.P. Glasser, and A.R. West, Nature 332, 525 (1988).
J.T.S. Irvine, M. Lacerda, and A.R. West, Mater. Res. Bull. 23, 1033 (1988).
M. Lacerda, J.T.S. Irvine, E.E. Lachowski, F.P. Glasser, and A.R. West, Br. Ceram. Trans. 87, 191 (1988).
M. Matsuda, Y. Inda, W. Hisamatsu, K. Yamashita, and T. Umegaki, J. Mater. Sci. Lett. 15, 933 (1996).
M. Sykora and J.R. Kincaid, Nature 387, 162 (1997).
H. Hosono, K. Yamazaki, and Y. Abe, J. Am. Ceram. Soc. 70, 867 (1987).
C.F. Bohren and D.R. Huffman, Absorption and Scattering of Light by Small Particles (Wiley-Interscience, New York, 1983).
T. Shimanouchi, Tables of Molecular Vibrational Frequencies, Consolidated Vol. 1 (NSRDS-NBS Washington, 39, 1972).
J.E. Shelby, J. Vitko Jr., and R.E. Benner, J. Am. Ceram. Soc. 61, C-59 (1982).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hayashi, K., Hirano, M. & Hosono, H. Translucent ceramics of 12CaO · 7Al2O3 with microporous structure. Journal of Materials Research 17, 1244–1247 (2002). https://doi.org/10.1557/JMR.2002.0185
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2002.0185