Abstract
Thin films of La0.67Sr0.33MnO3 (LSMO) were prepared at 670 °C on LaAlO3 (LAO) and SrTiO3 (STO) substrates by liquid-delivery metalorganic chemical vapor deposition. X-ray diffraction analysis 2¸/¸ and pole figure scans showed that the films are epitaxial with (001)LSMO//(001)LAO and (001)LSMO//(001)STO. The crystal structure of LSMO/LAO was indexed as face-centered cubic with a double cell and LSMO/STO as simple cubic. Electron microscopy revealed square facets and elongated grain features. Films heat-treated between 700 and 800 °C on LAO resulted in a structural change, while those on STO showed an increase in texture.
Similar content being viewed by others
References
M.L. Weaver, L.P.M. Brandao, A. Morrone, E.S. Gilman, K-H. Dahmen, and H. Garmestani, J. Mater. Res. 14, 2007 (1999).
K-H. Dahmen and M.W. Harris, Chem. Vap. Deposition 3, 27 (1997).
M.E. Hawley, G.W. Brown, P.C. Yashar, and C. Kwon, J. Cryst. Growth 211, 86 (2000).
T. Manabe, T. Fujimoto, I. Yamaguchi, W. Kondo, I. Kojima, S. Mizuta, and T. Kumagai, Thin Solid Films 323, 99 (1998).
P.B. Tavares, V.S. Amaral, J.P. Araujo, A.A.C.S. Lourenco, J.M. Vieira, and J.B. Sousa, J Magn. Magn. Mater. 196, 490 (1999).
P.A. LangJhar, F.F. Lange, T. Wagner, and M. Rühlle, Acta Mater. 46, 773 (1998).
Y.H. Li, K.A. Thomas, A. Goyal, M. Rajeswari, N.D. Mathur, M.G. Blamire, J.E. Evetts, T. Venkatesan, and J.L. MacManus-Driscoll, J. Mater. Res. 13, 2161 (1998).
G.W. Brown, Q.X. Jia, E.J. Peterson, D.K. Hristova, M.F. Hundley, J.D. Thompson, C.J. Magloire, J. Tesmer, and M.E. Hawley, in Epitaxial Oxide Thin Films III, edited by D.G. Schlom, C-B. Eom, M.E. Hawley, C.M. Foster, and J.S. Speck, (Mater. Res. Soc. Symp. Proc. 474, Pittsburgh, PA, 1997), p. 179.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Meda, L., Kennon, L., Bacaltchuk, C. et al. Effects of thermal annealing on the texture of La0.67Sr0.33MnO3 thin films. Journal of Materials Research 16, 1887–1889 (2001). https://doi.org/10.1557/JMR.2001.0258
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2001.0258