Abstract
The magnetic Nd–Fe–B powders were prepared by a mechanochemical method, including the processes of spray drying, debinding, milling, H2 reduction, Ca reduction, and washing. The liquid solution dissolved with various metal salts was first spray-dried to prepare the precursor powders having uniformly dispersed Nd, Fe, and B components. The precursor powders in turn were subjected to the subsequent processes. The particle size of the resultant Nd–Fe–B powders was about 1 μm. Effects of the process parameters on phases, morphologies, microstructures, compositions, and thermal properties of the powders were investigated.
Similar content being viewed by others
References
M. Sagawa, S. Fujimura, M. Togawa, H. Yamamoto, and Y. Matsuura, J. Appl. Phys. 55, 2083 (1984).
J.J. Croat, J.F. Herbst, R.W. Lee, and F.E. Pinkerton, J. Appl. Phys. 55, 2078 (1984).
G.C. Hadjipanayis, R.C. Hazelton, and K.P. Lawless, J. Appl. Phys. 55, 2073 (1984).
N.C. Koon and B.N. Das, J. Appl. Phys. 55, 2063 (1984).
Ph. I’Héritier, P. Chaudouet, R. Madar, A Rouault, J.P. Senateur, and R. Fruchart, C.R. Acad. Sci. 299, 849 (1984).
K. Oesterreicher and H. Oesterreicher, Phys. Status Solidi A 85, K61 (1984).
R.E. Cech, U.S. Patent 3,625,779 (1971); J. Metals 26, 32 (1974).
F. Kornfeld, Goldschmidt Informiert 4/75, No. 35 (Th. Goldschmidt AG, Essen, FRG, 1975).
C. Herget, Metal Powder Rep. 41, 438 (1987).
Y. Okajima, T. Tsugita, T. Takechi, and S. Okada, U.S. Patent No. 4,681,623 (1987).
G.J. Qi, M. Hino, and A. Yazawa, Materials Transaction, JIM, 31, 463 (1990).
M.Z. Su, S.F. Liu, X.L. Qian, and J.H. Lin, J. Alloys Compounds 249, 229 (1997).
T.Y. Liu, W.C. Chang, C.J. Chen, T.Y. Chu, and C.D. Wu, IEEE Trans. Magn. 28, 2593 (1992).
J.H. Lin, S.F. Liu, X.L. Qian, J.M. Bayi, and M.Z. Su, J. Alloys Compounds 238, 113 (1996).
Q.M. Cheng, J.H. Lin, and M.Z. Su, Solid State Commun. 106, 455 (1998).
S. Kramp, M. Feri, Ph. I’Héritier, P. Ezekwenna, and J.C. Joubert, J. Magn. Magn. Mater. 157/158, 73 (1996).
S. Ram and J.C. Joubert, Appl. Phys. Lett. 61, 613 (1992).
E. Claude, S. Ram, I. Gimenez, P. Chaudo et, D. Boursier, and J.C. Joubert, IEEE Trans. Mag. 29, 2767 (1993).
J.H. Lin, S.F. Liu, Q.M. Cheng, X.L. Qian, L.Q. Yang, and M.Z. Su, J. Alloys Compounds. 249, 237 (1997).
G.F. Sun, J.F. Chen, W. Dahl, H.J. Klaar, and W.G. Burchard, J. Appl. Phys. 64, 5519 (1988).
T.Y. Liu, C.J. Chen, C.H. Lin, and W.C. Chang, J. Appl. Phys. 70, 6612 (1991).
C.J. Chen, T.Y. Liu, Y.C. Hung, C.H. Lin, S.H. Chen, and C.D. Wu, J. Appl. Phys. 69, 5501 (1991).
B.K. Kim, C.J. Choi, and X.L. Dong, US Patent No. (in filing)
S. Katta and W.H. Gauvin, J. AIChE 21,1 (1975).
J.S. Reed, Introduction to the Principles of Ceramic Processing (John Wiley & Sons, New York, 1988), pp. 313–326.
S.J. Lukasiewicz, J. Am. Ceram. Soc. 72, 617 (1989).
K. Master, Spray Drying (Wiley Interscience, New York, 1976).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dong, X.L., Kim, B.K., Choi, C.J. et al. Synthesis of Nd2Fe14B powders by spray-drying and reduction–diffusion processes. Journal of Materials Research 16, 1083–1089 (2001). https://doi.org/10.1557/JMR.2001.0150
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2001.0150