Abstract
BxC1−x (x = 0.1 and 0.25) oriented platelets were intercalated with alkali metal vapor (M = K, Rb, Cs), giving first-stage M(B0.1C0.9)8 and M(B0.25C0.75)10. The presence of M(BxC1−x)5 dense domains interstratified in the first-stage structure were brought out from the 00.ℓ simulations. The presence of these domains is attributed to the acceptor electron effect of boron, which slightly enhances the intercalation rate as compared to pure carbon. Intercalation of Cs in liquid ammonia is improved using 1600 °C heat-treated B0.25C0.75 as a host material, and the composition Cs(B0.25C0.75)12 is reached after intercalation. In intercalation compounds of Cs in liquid ammonia obtained from heat-treated B0.25C0.75, as the heat-treatment temperature (HTT) was increased from 1600 to 2000 °C, the segregation of first stage was observed in two structures Cs(BxC1−x)8 and Cs(BxC1−x)10 with the respective 2 × 2 0° and 2.23 × 2.23 two-dimensional lattices of the cesium atoms. The presence of these two structures is assigned to the heterogeneity of the host material induced by the formation of B4C boron carbide domains and the consecutive boron elimination of the BxC1−x lamellar phase with increasing HTT.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
C.E. Lowell, J. Am. Ceram. Soc. 50, 142 (1967).
B. Ottaviani, Ph.D. Thesis, University of Bordeaux, France (1996).
A. Derré, L. Filipozzi, and F. Peron, J de Physique IV colloque C3 supplement to J. de physique II. 195 (1993).
S. Flandrois, B. Ottaviani, A. Derré, and A. Tressaud, J. Phys. Chem. Solids 57, 741 (1996).
L. Duclaux, B. Ottaviani, L. Piraux, E. Grivei, J.P. Issi, F. Béguin, and S. Flandrois, Mol. Cryst. Liq. Cryst. 310, 27 (1998).
F. Saugnac and A. Marchand, C. R. Acad. Sci. Paris 310, 187 (1990).
A. Herold, Bull. Soc. Chim. Fr. 999 (1955).
L. Duclaux, I. Rannou, M. Lelaurain, and F. Béguin, J. Mater. Res. 11, 608 (1996).
A. Herold, in Intercalated Materials, edited by F. Levy (D. Reidel, Dordrecht, Holland 1979), p.400.
J. Maire and J. Mering, in Chemistry and Physics of Carbon, edited by P.L. Walker, Jr. (Marcel Dekker, New York, 1970), Vol. 6, p. 125.
D. Guérard and P. Lagrange, in Physics of Intercalation Compounds (proceedings of the international conference on the Physics of Intercalation Compounds, Trieste, Italy, July 6–10, 1981), edited by Pietronero and E. Tosatti (Springer-Verlag, Berlin, Heidelberg, New York, 1981), p. 223.
W. Rüdorff, E. Schulze, and O. Rubisch, Z. Anorg. Allg. Chem. 282, 232 (1955).
F.J. Salzano and S. Aronson, J. Inorg. Nucl. Chem. 26, 1456 (1964).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Duclaux, L., Béguin, F., Ottaviani, B. et al. Synthesis and Structure of BxC1−x Intercalation Compounds with Heavy Alkali Metals (K, Rb, and Cs). Journal of Materials Research 15, 1409–1416 (2000). https://doi.org/10.1557/JMR.2000.0204
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2000.0204