Abstract
Tetragonal ferroelectric materials are polarized to induce the anisotropy necessary for the piezoelectric effect. This poling of the material is inherently an orientation process. Pole figure texture measurements of poling and cross-poling in a lead zirconate titanate Navy VI material show domain motion. The resulting axisymmetric and three-dimensional textures demonstrate the contribution of 90° domain motion to piezoelectricity. Cross-poling results in strong orientations with lower applied fields than in the initial poling steps.
Similar content being viewed by others
References
T. Tsurumi, et al., Jpn. J. Appl. Phys. 36, 5970 (1997).
Y. Saito, Jpn. J. Appl. Phys. 36, 5963 (1997).
S. Wan, W. Shelley, and K.J. Bowman, Ceram. Trans. 313 (1999).
S. Wan and K.J. Bowman, J. Am. Ceram. Soc. 10, 2717 (1998).
Shan Wan, Ph.D. Thesis, Purdue University (May 2000).
U.F. Kocks, in Texture and Anisotropy, edited by U.F. Kocks, C.N. Tome, and H-R. Wenk (Cambridge University Press, Cambridge, United Kingdom, 1998), pp. 44–101.
S. Wan and K.J. Bowman, in Orientation Evolution of Textured Piezoelectric Ceramics under Electric Fields, ICOTOM 12, August 10–13, 1999, edited by J. Szpunar (NRC Press, Ottawa, Canada, 1999), pp. 1453–1499.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wan, S., Bowman, K.J. Cross-poling Textures in a Lead Zirconate Titanate Piezoelectric Material. Journal of Materials Research 15, 1248–1249 (2000). https://doi.org/10.1557/JMR.2000.0180
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2000.0180