Abstract
The mechanisms are studied for enhanced formation of C54–TiSi2 at about 700 °C when rapid thermal annealing at 3 °C/s in N2 is performed on 32-nm-thick codeposited Ti–5.9 at.% Ta on Si(100) single-crystal substrates. The enhancement is related to an increased C54–TiSi2 nucleation rate due to the development of a multilayered microstructure. The multilayer microstructure forms at temperatures below 600 °C with the formation of an amorphous disilicide adjacent to the Si substrate and a M5Si3 (M = Ti, Ta) capping layer. This amorphous disilicide crystallizes at higher temperatures to C49–TiSi2. The multilayer microstructure introduces an additional interface that increases the area available for the heterogeneous nucleation of C54. The capping layer is identified as hexagonal Ti 5Si3 or its isomorphous compound (Ti1–xTax)5Si3. Crystal simulations demonstrate that C54(040) has a lattice mismatch of 6–7% relative to Ti5Si3(300) suggesting that a pseudomorphic epitaxial relationship may lower the interfacial energy between these two phases and reduce the energy barrier for C54 nucleation. A C40 disilicide phase was also observed at temperatures above that required to form C54–TiSi2 suggesting that, in the present experiments, the C40 phase does not play a major role in catalyzing C54 formation.
Similar content being viewed by others
References
R. Beyers and R. Sinclair, J. Appl. Phys. 57, 5240 (1985).
H. Jeon, C.A. Sukow, J.W. Honeycutt, G.A. Rozgonyi, and R.J. Nemanich, J. Appl. Phys. 71, 4269 (1992).
Z. Ma and L.H. Allen, in Evolution of Surface and Thin-Film Microstructure, edited by H.A. Atwater, E.H. Chason, M.L. Grabow, and M.G. Lagally (Mater. Res. Soc. Symp. Proc. 280, Pittsburgh, PA, 1993), p. 593.
A. Quintero, M. Libera, C. Cabral, Jr., L.A. Clevenger, and J.M.E. Harper, in Thin Films–Structure and Morphology, edited by S.C. Moss, D. Ila, R.C. Cammarata, E.H. Chason, T.L. Einstein, and E.D. Williams (Mater. Res. Soc. Symp. Proc. 441, Pittsburgh, PA, 1997), p. 303.
A. Mouroux, S.L. Zhang, W. Kaplan, S. Nygren, M. Ostling, and C.S. Petersson, Appl. Phys. Lett. 69, 975 (1996).
A. Mouroux, S.L. Zhang, and C.C. Petersson, Phys. Rev. B 56, 10614 (1997).
C. Cabral, Jr., L.A. Clevenger, J.M.E. Harper, F.M. d’Heurle, R.A. Roy, K.L. Saenger, G.L. Miles, and R.W. Mann, J. Mater. Res. 12, 304 (1997).
C. Cabral, Jr., L.A. Clevenger, J.M.E. Harper, F.M. d’Heurle, J.M.E. Harper, R.A. Roy, C. Lavoie, K.L. Saenger, G.L. Miles, R.W. Mann, and J.S. Nakos, Appl. Phys. Lett. 71, 3531 (1997).
A. Quintero, M. Libera, C. Cabral, Jr., C. Lavoie, and J.M.E. Harper, Microscopy and Microanalysis 4, 666 (1998).
P. Stadelmann and P-H. Jouneau, EMS on line, Centre Interdepartmental de Microscopie Electronique, Ecole Polytechnique Federale de Lausanne, http://cimewww.epfl.ch/CIOL/.
International Tables for X-Ray Crystallography (Kynoch Press, Birmingham, England, 1965), Vol. 1.
Joint Committee on Powder Diffraction Standards (JCPDS) (Swarthmore, PA).
D.B. Williams and C.B. Carter, Transmission Electron Microscopy (Plenum Press, New York, 1996).
S.P. Murarka, Silicides for VLSI applications (Academic Press, Orlando, 1983).
J. Musil, A.J. Bell, J. Vlcek, and T. Hurknas, J. Vac. Sci. Technol. A14, 2247 (1996).
P.M. Marcus and F. Jona, J. Phys. Condens. Matter 9, 6241 (1997).
J.W. Edington, Practical Electron Microscopy in Materials Science (Van Nostrand Reinhold, New York, 1976).
J. Bonevich, D. van Heerden, and D. Josell, J. Mater. Res. 14, 1977 (1999).
W. L. Johnson in Materials Interfaces: Atomic-Level Structure and Properties, edited by D. Wolf and S. Yip (Chapman and Hall, London, 1992).
W.L. Johnson, Phase Transformation in Thin Films—Thermodynamics and Kinetics, edited by M. Atzmon, A.L. Greer, J.M.E. Harper, and M.R. Libera (Mater. Res. Soc. Symp. Proc. 311, Pittsburgh, PA, 1993), p. 71.
W.F. Smith, Foundations of Materials Science and Engineering (McGraw-Hill, New York, 1990).
A.R. Miedema, P.F. de Chatel, and F.R. de Boer, Physica B 100, 1 (1980).
R.J. Kemantick and C.E. Meyers, Chem. Mater. 8, 287 (1996).
M.E. Schlesinger, Chem. Rev. 90, 607 (1990).
D.A. Porter and K.E. Easterling, Phase Transformation in Metals and Alloys (Chapman and Hall, London, 1992).
M.H. Wang and L.J. Chen, J. Appl. Phys. 61, 1339 (1992).
L.A. Clevenger, C. Cabral, Jr., R.A. Roy, C. Lavoie, J. Jordan-Sweet, S. Brauer, G. Morales, K.F. Ludwig, Jr., and G.B. Stephenson, Thin Solid Films 289, 220 (1995).
A. Noya, M. Takeyama, K. Sasaki, E. Aoyagi, and K. Hiraga, J. Vac. Sci. Technol. A 15, 253 (1997).
V. Svilan, K.P. Rodbell, L.A. Clevenger, C. Cabral, Jr., R.A. Roy, C. Lavoie, J. Jordan-Sweet, and J.M.E. Harper, J. Elec. Mater. 26, 1090 (1997).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Quintero, A., Libera, M., Cabral, C. et al. Mechanisms for enhanced C54–TiSi2 formation in Ti–Ta alloy films on single-crystal Si. Journal of Materials Research 14, 4690–4700 (1999). https://doi.org/10.1557/JMR.1999.0635
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1999.0635