When powder mixtures of {Al2(SO4)3 + Na2SO4}or {γ–Al2O3 [obtained by heating Al2(SO4)3 at 900 °C for 3 h] + Na2SO4} were heated in an alumina crucible at 1100 °C for 1 h, α–Al2O3 platelets were formed. The powder mixture of {Al2(SO4)3 + 2Na2SO4} yielded aggregations of platelets that were less than 5 μm in size. The size of the aggregations increased in proportion to the amount of Na2SO4, and aggregations of 120 μm were obtained using a mixture of {Al2(SO4)3 + 6Na2SO4}. The powder mixture of {γ–Al2O3 + 2Na2SO4 yielded hexagonal platelets having an average diameter of 3.7 μm and an average thickness of 0.3 μm. In addition to aggregation size, the size of the hexagonal platelets also increased in proportion to the amount of Na2SO4, and platelets having an average diameter of 5 μm were obtained using a mixture of {γ–Al2O3 + 6Na2SO4}.
Similar content being viewed by others
References
K-H. Heussner and N. Claussen, J. Eur. Ceram. Soc. 5, 193 (1989).
P.S. Form, R. Pyrz, B. Clausen, and E.Ø. Nielsen, Mater. Sci. Eng. A197, 231 (1995).
Y. Zhou, J. Vleugels, T. Laoui, and O. Van Der Biest, J. Mater. Sci. Lett. 13, 1089 (1994).
Y. Yang, Z. Yang, and Q. Yuan, J. Mater. Sci. Lett. 15, 185 (1996).
Y. Zhou, J. Vlengels, T. Laoui, and O. Van Der Biest, J. Eur. Ceram. Soc. 15, 297 (1995).
M.C. Fredel and A.R. Boccaccini, J. Mater. Sci. 31, 4375 (1996).
E. Champion, S. Gautier, and D. Bernache-Assolant, J. Mater. Sci. 7, 125 (1996).
A.R. Boccaccini and P.A. Trusty, J. Mater. Sci. 15, 60 (1996).
V. Massardier, E. Maire, and P. Merle, Mater. Sci. Eng. A203, 105 (1995).
K. Daimon and E. Kato, J. Cryst. Growth 75, 348 (1986).
C.A. Shaklee and G.L. Messing, J. Am. Ceram. Soc. 77, 2977 (1994).
N.S. Bell, S-B. Cho, and J.H. Adair, J. Am. Ceram. Soc. 81, 1411 (1998).
S. Ono, G. Yamaguchi, H. Yanagida, and T. Shimizu, J. Ceram. Soc. Jpn. (Yogyo-Kyokai-shi) 76, 207 (1968).
S. Kato, T. Iga, S. Sano, and E. Ishii, J. Ceram. Soc. Jpn. (Yogyo-Kyokai-shi) 77, 60 (1969).
E. Kato, K. Daimon, A. Yamaguchi, and T. Yamada, J. Ceram. Soc. Jpn. (Yogyo-Kyokai-shi) 85, 134 (1977).
E.M. Levin and H.F. McMurdie, Phase Diagrams for Ceramists 1975 Supplement (American Ceramic Society, Westerville, OH, 1975), Fig. 4708.
I. Brain, Thermochemical Data of Pure Substances, Part II, La-Zr, 2nd ed. (VHC, Weinheim, Germany, 1993), p. 1003.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hashimoto, S., Yamaguchi, A. Synthesis of α–Al2O3 platelets using sodium sulfate flux. Journal of Materials Research 14, 4667–4672 (1999). https://doi.org/10.1557/JMR.1999.0631
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1999.0631