Abstract
Two new compounds, GdBa4Cu3O8.5+δ (Gd143) and DyBa4Cu3O8.5+δ (Dy143), were synthesized from precursors Gd2O3, Dy2O3, BaO2, and CuO at 1000 °C in an oxygen atmosphere. The oxygen stoichiometric value δ was found to be 0.68 for Gd143 and 0.6 for Dy143 by iodometric titration. Rietveld refinement of x-ray powder diffraction data showed that Gd143 belongs to the space group Pm3 while Dy143 belongs to the space group P23. The two space groups, Pm3 and P23, are very similar. Their main difference is that P23 does not have the inversion symmetry of Pm3. Both compounds have a cubic unit cell with a lattice parameter of 8.16528 ± 0.00006 Å for Gd143 and 8.10807 ± 0.00010 Å for Dy143. Superconducting quantum interference device (SQUID) measurement indicated that neither compound was superconductive down to 5 K.
Similar content being viewed by others
References
D. M. de Leeuw, C. A. H. A. Mutsaers, C. Langereis, H. C. A. Smoorenburg, and P. J. Rommers, Physica C 152, 39 (1988).
D. M. de Leeuw, C. A. H. A. Mutsaers, R. A. Streetman, E. Frikkee, and H. W. E. Zandbergen, Physica C 158, 391 (1989).
F. Abbattista, M. Vallino, D. Mazza, M.L. Borlera, and C. Brisi, Mater. Chem. Phys. 20, 191 (1988).
F. Abbattista, M. Vallino, and D. Mazza, Mater. Chem. Phys. 20, 521 (1989).
P. W. Anderson, J. Phys. Chem. Solids 54, 1457 (1993).
Y. T. Zhu, P. S. Baldonado, E.J. Peterson, D.E. Peterson, and F. M. Mueller, Powder Diffraction 12, 242 (1997).
Y. T. Zhu, E. J. Peterson, P. S. Baldonado, J. Y. Coulter, D. E. Peterson, and F. M. Mueller, J. Phys. Chem. Solids 59, 1331 (1998).
A. C. Larson and R. B. Von Dreele, “GSAS, Generalized Structural Analysis System,” Document LAUR 86-748, Los Alamos National Laboratory, Los Alamos, NM (1993).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhu, Y.T., Peterson, E.J., Baldonado, P.S. et al. Synthesis and crystal chemistry of the new compounds GdBa4Cu3O8.5+δ and DyBa4Cu3O8.5+δ. Journal of Materials Research 14, 334–339 (1999). https://doi.org/10.1557/JMR.1999.0049
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1999.0049