Abstract
The effects of Si additions on the behavior of high modulus carbon fiber reinforced aluminum matrix (CF/Al) composites during thermal exposure at 773 K for different times have been investigated. The composites were fabricated via hybridization with a small volume fraction of SiC particles using a pressure-casting process. The change of longitudinal tensile strength, the strength degradation of carbon fibers, and the microstructural observations on the interfaces of CF/pure Al composites and CF/Al-Si composites after thermal exposure undoubtedly indicate that the alloying element Si in an aluminum matrix can effectively prohibit the interfacial reactions at the fiber/aluminum interface and has positive effects on the characteristics of CF/Al composites.
Similar content being viewed by others
References
H. Khan, Metall. Trans. 7A, 1281 (1976).
H. M. Cheng, S. Akiyama, A. Kitahara, K. Kobayashi, and B. L. Zhou, Mater. Sci. Technol. 8, 275 (1992).
R. Chen, G. D. Zhang, and R. J. Wu, in Proc. 8th Int. Conf. on Compos. Mater., Honolulu, SAMPE (1991), paper 19F.
T. A. Chemyshova and L. I. Kobeleva, J. Mater. Sci. 20, 3524 (1985).
S. Kohara and N. Muto, in Proc. 5th Int. Conf. on Compos. Mater. (TMS, Warrendale, PA, 1985), p. 631.
Y. Sawada and M. G. Bader, ibid, 785 (1985).
H. M. Cheng, A. Kitahara, K. Kobayashi, and B. L. Zhou, J. Mater. Sci. Lett. 10, 795 (1991).
H. M. Cheng, A. Kitahara, S. Akiyama, K. Kobayashi, and B. L. Zhou, J. Mater. Sci. 27, 3617 (1992).
H. Asanuma and A. Okura, J. Jpn. Inst. Mt. 48, 1198 (1984).
M. Kh. Shorshorov, T. A. Chernyshova, and L. I. Kobeleva, in Progress in Science and Engineering of Composites, edited by T. Hayashi et al. (Jpn. Soc. for Composite Materials, Tokyo, 1982), p. 1273.
K. J. Protnoj, V. I. Bogdarov, A. V. Mikhailov, and D. L. Fuks, Doklady AN SSSR, 240, 1154 (1978).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Cheng, HM., Zhou, BL., Kitahara, A. et al. Effect of silicon additions on characteristics of carbon fiber reinforced aluminum composites during thermal exposure. Journal of Materials Research 11, 1284–1292 (1996). https://doi.org/10.1557/JMR.1996.0163
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1996.0163