Abstract
Extruded eutectoid Zn–Al alloy was welded by a melt of the same eutectoid alloy. Two different microstructures were observed in the joint part and in the bulk of the welded alloy. Typical dendritic structure of as-cast Zn–Al alloy was observed in the joint part of the welded alloy. The bulk of the welded Zn–Al alloy appeared as fine grain structure. Two different metastable phases, η′T decomposed from η′s of the chilled as-cast state and η′E of the extruded state, were found to be unstable during the early stages of aging. A four-phase transformation occurred after the decompositions of these two metastable phases of η′T. Microstructures of both the joint part and bulk of the welded alloy were investigated simultaneously during the aging processes.
Similar content being viewed by others
References
Y. H. Zhu, Chin. J. Met. Sci. Technol. 6, 125 (1990).
Y. H. Zhu, G. Torres-Villaseñor and C. Piña, J. Mater. Sci. 29, 1549 (1994).
Y. H. Zhu and F. E. Goodwin, J. Mater. Sci. Technol. 10, 121 (1994).
Y. H. Zhu and S. Murphy, Cin. J. Met. Sci. Technol. 65, 261 (1987).
Y. H. Zhu, B. Yan, and W. Huang, Symp. Proc. Zn–Al Casting Alloys, Toronto, Canada (1986), p. 23.
Y. H. Zhu, W. Huang, and B. Yan, Shanghai Metals (Nonferous Fascicule) 9, 1 (1988).
Y. H. Zhu and F. E. Goodwin, J. Mater. Res. 8, 3043 (1993).
J. Krol and K. Wegrezyn, Archiwum Hutnictwa, 17, 119 (1971).
R. Ciach, J. Krol, and K. Wegrezyn, Bulletin de LACADEMIE Polonais des Science serie des Sciences Techniques 17 (4), 341 (1969).
S. Murphy, Z. Metallk. 71, 96 (1980).
Y. H. Zhu and S. Murphy, Chin. J. Met. Sci. Technol. 2, 105 (1986).
Y. H. Zhu, Chin. J. Met. Sci. Technol. 5, 113 (1989).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhu, Y.H. Microstructural changes in welded Zn–Al alloy. Journal of Materials Research 11, 593–598 (1996). https://doi.org/10.1557/JMR.1996.0072
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1996.0072