Abstract
Stoichiometric Sr1−xBaxNb2O6 (SBN) powder and thin films were prepared by a chemical method. The starting materials were niobium ethoxide and the hydroxides of strontium and barium. Powders were obtained by evaporation of the precursor solution, and thin films were deposited by spin coating. Annealing temperature required to obtain complete conversion to the crystalline material was about 700 °C. Stoichiometric polycrystalline films of Sr1−xBaxNb2O6 were deposited on quartz and silicon substrates. Leakage current-voltage and the capacitance-voltage measurements on a metal/SBN/n-silicon structure show a diode-type characteristic.
Similar content being viewed by others
References
S. Nomura and H. Kojima, Jpn. J. Appl. Phys. 13, 1185 (1974).
S. L. Swartz, IEEE Trans. Electr. Insulation 25, 935 (1990).
J. C. Burfoot, in Active and Passive Thin Film Devices, edited by J. C. Coutts (Academic Press, New York, 1978), pp. 697–741.
E. Dayalan and M. S. Tomar, Thin Solid Films 236, 37 (1993).
R. Xu, Y. Xu, C. J. Chen, and J. D. Mackenzie, J. Mater. Res. 5, 916 (1990).
C. J. Chen, Y. Xu, R. Xu, and J. D. Mackenzie, J. Appl. Phys. 69, 1763 (1991).
S. S. Thony, K. E. Youden, J. S. Harris, Jr., and L. Hesselink, J. Appl. Phys. Lett. 65, 2018 (1994).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kashani, A., Tomar, M.S. & Dayalan, E. A novel route for the synthesis of Sr1−xBaxNb2O6 thin films. Journal of Materials Research 10, 2404–2407 (1995). https://doi.org/10.1557/JMR.1995.2404
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1995.2404