As-grown YBa2Cu3Ox films prepared on single crystal (100)MgO substrates by rf thermal plasma evaporation have the advantages of a high deposition rate of 730 nm/min, a large area deposition over 300 cm2, and a high Jc of 6.8 × 105 A/cm2 (77 K, O T), as reported in previous papers.1,2 We report in this paper about the preparation of YBa2Cu3Ox films on yttria-stabilized zirconia (YSZ) polycrystalline substrates for a practical application using this technique to synthesize these films on flexible (metal or flexible polycrystal) substrates. Films prepared on YSZ polycrystalline substrates grew with a c-axis orientation at a relatively high deposition rate and exhibited a zero resistance temperature (TcO) of 88 K and a critical current density Jc of 3500 A/cm2 (77 K, O T). Films prepared on flexible YSZ polycrystalline tapes with a length of 100 mm were also grown with a c-axis orientation and exhibited TcO) over 77 K.
Similar content being viewed by others
References
S. Yuhya, K. Kikuchi, Y. Shiohara, K. Terashima, and T. Yoshida, J. Mater. Res. 7, 2673 (1992).
K. Kikuchi, S. Yuhya, and Y. Shiohara, J. Mater. Sci. Lett. 12, 1392 (1993).
A. D. Berry, D. K. Gaskill, R. T. Holm, E. J. Cukauskas, and R. L. Henry, Appl. Phys. Lett. 52, 1743 (1988).
Y. Enomoto, T. Murakami, M. Suzuki, and K. Moriwaki, Jpn. J. Appl. Phys. 26, L1284 (1987).
T. Terashima, K. Iijima, K. Yamamoto, Y. Bando, and H. Mazaki, Jpn. J. Appl. Phys. 27, L91 (1988).
T. Venkatesan, X. D. Wu, B. Dutta, A. Inam, M. S. Hedge, D. M. Hwang, C. C. Chang, L. Nazar, and B. Wilkens, Appl. Phys. Lett. 54, 581 (1989).
K. Terashima, K. Eguchi, T. Yoshida, and K. Akashi, Appl. Phys. Lett. 52, 1274 (1988).
K. Terashima, H. Komaki, and T. Yoshida, IEEE Trans. Plasma Sci. 18, 980 (1990).
Y. Hirokawa, Y. Takamura, H. Komaki, K. Terashima, and T. Yoshida, J. Mater. Synthesis and Processing 1, 53 (1993).
Y. Iijima, K. Onabe, N. Futaki, N. Tanabe, N. Sadakata, O. Kohno, and Y. Ikeno, Proc. 5th Int. Symp. on Superconductivity (Springer-Verlag, Tokyo, 1992), p. 661.
N. Tatsumi, J. Tsujino, S. Yuhya, K. Kikuchi, and Y. Shiohara, Proc. 5th Int. Symp. on Superconductivity (Springer-Verlag, Tokyo, 1992), p. 665.
K. Fujino, N. Yoshida, S. Takano, S. Okuda, T. Hara, H. Ishii, and T. Yamamoto, Proc. 5th Int. Symp. on Superconductivity (Springer-Verlag, Tokyo, 1992), p. 673.
N.G. Chew, S.W. Goodyear, J.A. Edwards, J.S. Satchel, S.E. Blenkinsop, and R. G. Humphreys, Appl. Phys. Lett. 57, 2016 (1990).
T. Arikawa, H. Itozaki, K. Harada, K. Higashi, S. Tanaka, and S. Yazu, Jpn. J. Appl. Phys. 27, L91 (1988).
J. F. Hamet, B. Mercy, M. Hervieu, and B. Raveau, Physica C 193, 465 (1992).
D. Dimos, P. Chaudhari, J. Mannhart, and F. K. LeGoues, Phys. Rev. Lett. 61, 219 (1988).
D. Dimos, P. Chaudhari, and J. Mannhart, Phys. Rev. B 41, 4038 (1990).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Tsujino, J., Tatsumi, N. & Shiohara, Y. Superconducting YBa2Cu3Ox films prepared on YSZ polycrystalline substrates by rf thermal plasma evaporation. Journal of Materials Research 9, 1089–1097 (1994). https://doi.org/10.1557/JMR.1994.1089
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1994.1089