Abstract
The reaction of tetraethoxysilane (TEOS) and the subsequent deposition of SiOx on the basal plane and edges of highly oriented pyrolytic graphite (HOPG) were studied. Interfacial bonding and surface morphologies resulting from different reaction conditions were probed using scanning tunneling microscopy (STM), Auger electron spectroscopy (AES), Rutherford backscattering spectroscopy (RBS), temperature programmed desorption (TPD), and high resolution electron energy loss spectroscopy (HREELS). The initial reaction of TEOS was found to occur at surface defects. STM images indicated that SiCx films do not grow layer-by-layer, confirming earlier indirect observations to that effect.
Similar content being viewed by others
References
J.D. Buckley, Ceram. Bull. 67, 364 (1988).
J. R. Strife and J. E. Sheehan, Ceram. Bull. 67, 369 (1988).
D.W. McKee, Carbon 25, 551 (1987).
J.E. Sheehan, Carbon 27, 709 (1989).
K. L. Luthra, Carbon 26, 217 (1988).
A. A. Cochran, J. B. Stephenson, and J. G. Donaldson, J. Metals 37, August, 37 (1970).
D.W. McKee, C.L.Spiro, and E.J. Lamby, Carbon 22, 507 (1984).
E. J. Hippo, N. Murdie, and A. Hyjazie, Carbon 27, 689 (1989).
C. Kozlowski and P. Sherwood, Carbon 25, 751 (1987).
C. Kozlowski and P. Sherwood, J. Chem. Soc., Faraday Trans. 1 81, 2745 (1985).
C. Kozlowski, and P. Sherwood, Carbon 24, 357 (1986).
W. P. Hoffman and P. Ehrburger, J. Anal. Appl. Pyrolysis 15, 275 (1989).
J.B. Danner, M. A. Rueter, and J.M. Vohs, Langmuir 9, 455 (1993).
R. E. Palmer, J. F. Annett, and R. F. Willis, Phys. Rev. Lett. 58, 2490 (1987).
P.A. Thiry, M. Liehr, J.J. Pireaux, P. Sporken, R. Caudano, J.Pl. Vigeron, and A.A. Lucas, J. Vac. Sci. Technol. B 3, 1118 (1985).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hoveland, M.M., Danner, J.B., Vohs, J.M. et al. Initial stages of SiOx deposition on graphite. Journal of Materials Research 9, 933–939 (1994). https://doi.org/10.1557/JMR.1994.0933
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1994.0933