Mild steel plates were welded under stationary and dynamic (longitudinal and transverse vibration) conditions. The frequency and amplitude ranges selected were 0 Hz to 300 Hz and 0 μm to 30 μm, respectively. It has been observed on the basis of experimental findings that vibration, in general, reduces the grain size of the weldment, and this reduction is appreciable at a lower amplitude of vibration. This may be due to the lower energy required for nucleation of the solid phase. Fast removal of latent heat of solidification from the solid liquid interface plays a significant part in the grain refinement under vibration.
Similar content being viewed by others
References
T. Ganaha, B.P. Pearce, and H. W. Kerr, Metall. Trans. 11A, 1351 (1980).
T. P. Fisher, British Foundryman 66, (3), 71 (1973).
D. P. Shukla, D. B. Goel, and P. C. Pandey, Metall. Trans. 11B, 166 (1980).
D. B. Goel, D. P. Shukla, and P. C. Pandey, Trans. Indian Institute of Metals 33 (3), 196 (1980).
B.P. Pearce and H.W. Kerr, Metall. Trans. 12B, 479 (1981).
S. Kou and Y. Le, Welding J. 64 (3), 51 (1985).
S. Kou and Y. Le, Metall. Trans. 16A, 1345 (1985).
J.D. Scarbrough and C.E. Burgan, Welding J. 63 (6), 54 (1984).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Tewari, S.P. Influence of vibration on grain size and degree of grain refinement in mild steel weldments. Journal of Materials Research 8, 2228–2230 (1993). https://doi.org/10.1557/JMR.1993.2228
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1993.2228