Abstract
A study of the quasicrystalline phases obtained from a quaternary alloy of Al–Cu–Co–Fe is carried out. The formation of these phases is based on a gravity chill-casting technique. The alloy was cast in a wedge-shaped copper mold. Optical and scanning electron micrographs show a characteristic dendritic growing in regions close to the wedge edge. These types of dendrites display apparent symmetries that resemble the tenfold, fivefold, and eightfold symmetries obtained in quasicrystalline materials. Electron diffraction patterns, in addition to x-ray diffraction patterns, show two kinds of quasicrystalline phases. The icosahedral and decagonal phases coexist in these types of alloys also with binary and ternary compounds of intermetallic nature.
Similar content being viewed by others
References
D. Shechtman I. Blech D. Gratias and J.W. Cahn Phys. Rev. Lett. 53, 1951 (1984).
R. Perez J. Mater. Sci. 27, 5141 (1992).
D.A. Lilienfeld M. Nastasi H.H. Johnson D.G. Ast and J.W. Mayer Phys. Rev. Lett. 55, 1587 (1985).
K. G. Kreider F. S. Biancaniello and H. J. Kaufman Scripta Metall. 21, 657 (1987).
D.M. Follstaedt and J.A. Knapp Phys. Rev. Lett. 56, 1827 (1986).
S.J. Poon A. J. Drehman and K. R. Lawless Phys. Rev. Lett. 55, 2324 (1985).
J. Eckert L. Schultz and K. Urban Acta Metall. Mater. 39 (7), 1497 (1991).
K. Hiraya B. P. Zang M. Hirabashi A. Inoue and T. Masumoto Jpn. J. Appl. Phys. 27 (12), L2252 (1988).
A. P. Tsai A. Inoue and T. Masumoto Mater. Trans. JIM 30 (2), 150 (1989).
J. A. Juarez-Islas, D. H. Warrington and H. Jones J. Mater. Sci. 24, 2076 (1989).
Selected Powder Diffraction for Metals and Alloys, Int. Center for Diffraction Data, JCPDS, Swarthmore, PA, Vols. I and II (1978).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Perez, R., Arizmendi, A., Juarez-Islas, J.A. et al. Formation of quasicrystalline phases in an Al–Cu–Co–Fe alloy obtained by using a gravity chill-casting technique. Journal of Materials Research 8, 985–988 (1993). https://doi.org/10.1557/JMR.1993.0985
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1993.0985