Abstract
The high temperature equilibrium conductivity (950 °C–1050 °C) of congruent LiNbO3 can be resolved into two components: an electronic portion that is dependent on the oxygen partial pressure and an ionic portion that is pressure independent. It is shown that the two components can be obtained from an analysis of the total equilibrium conductivity measured as a function of oxygen partial pressure. The ionic transport number (fractional ionic conductivity) thus obtained is compared with that obtained from an oxygen concentration cell measurement. The two techniques are found to be in excellent agreement, confirming the experimental validity of the defect chemistry method. From the temperature dependence of the ionic conductivity, the activation energy (138 kJ/mol [1.43 eV]) for the ionic transport is obtained. The results are in good agreement with the value previously obtained for the oxygen chemical diffusivity.
Similar content being viewed by others
References
H. Fay, W. J. Alford, and H. M. Dess, Appl. Phys. Lett. 12, 89 (1968).
P. Lerner, C. Legras, and J. P. Duman, J. Cryst. Growth 3/4, 231 (1968).
S. C. Abrahams and P. Marsh, Acta Crystallogr. B42, 61–68 (1986).
E. K. Chang, A. Mehta, and D. M. Smyth, Adv. in Ceram. 23, 351 (1987).
D. M. Smyth, Proceedings of the Sixth IEEE Int. Symp. on Application of Ferroelectrics, ISAF ‘86, 115 (1986).
P. J. Jorgensen and R.W. Bartlett, J. Phys. Chem. Solids 30, 2639 (1969).
G. Bergmann, Solid State Commun. 6, 77 (1968).
Y. Limb, K.W. Cheng, and D. M. Smyth, Ferroelectrics 38, 813 (1981).
E. K. Chang, A. Mehta, and D. M. Smyth, Proc. of the Symp. on Electro-ceramics and Solid-state Ionics, edited by Harry L. Tuller and Donald M. Smyth (The Electrochemical Society Proceedings, 1988), Vol. 88-3, p. 35.
L. Heyne, Proceedings of a Symposium, Oct. 22–25, 1967, NBS special publication #296.
H. M. Chan, Z. Zhuang, and D. M. Smyth, in Defect Properties and Processing of High-Technology Nonmetallic Materials, edited by Y. Chen, W. D. Kingery, and R. J. Stokes (Mater. Res. Soc. Symp. Proc. 60, Pittsburgh, PA, 1986), p. 95.
G.E. Peterson and A. Carnevale, J. Chem. Phys. 56, 4848 (1972).
R. J. Holmes and D. M. Smyth, J. Appl. Phys. 55 (10), 3531 (1984).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mehta, A., Chang, E.K. & Smyth, D.M. Ionic transport in LiNbO3. Journal of Materials Research 6, 851–854 (1991). https://doi.org/10.1557/JMR.1991.0851
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1991.0851