Abstract
Preliminary results of producing Cu–Y–Ba metallic precursors to high Tc superconductors by high energy ball milling are reported. Mechanical alloying of Cu, Y, and Ba powders (various stoichiometries) produced either amorphous, mixed crystalline/amorphous, or fine grained crystalline powders, as shown by their x-ray spectra. None of the powders exhibited flux exclusion down to a temperature of 1.4 K. The YBa2Cu3 precursor consisted of a mixture of crystalline phases. After being pressed into a pellet and sintered, it was found to be superconducting at liquid nitrogen temperatures.
Similar content being viewed by others
References
M. K. Wu, J. R. Ashburn, C. J. Torng, P. H. Hor, R. L. Meng, L. Gao, Z. J. Huang, Y. Q. Wang, and C. W. Chu, Phys. Rev. Lett. 58, 908 (1987).
L. T. Romano, P. R. Wilshaw, N. J. Long, and C. R. M. Grovenor, Supercon. Sci. Technol. 1, 285 (1989).
S. Jin, R. C. Sherwood, R. B. van Dover, T. H. Tiefel, and D. W. Johnson, Jr., Appl. Phys. Lett. 51, 203 (1987).
M. A. Lusk, J. A. Lund, A. C. D. Chaklader, M. Burbank, A. A. Fife, S. Lee, B. Taylor, and J. Vrba, Supercon. Sci. Technol. 1, 137 (1988).
G. J. Yurek, J. B. Vander Sande, W-X. Wang, D. A. Rudman, Y. Zhang, and M. M. Matthiesen, Metall. Trans. A 18A, 1813 (1987).
T. Kogure, R. Kontra, and J. B. Vander Sande, Physica C 156, 35 (1988).
A. W. Weeber and H. Bakker, Physica B 153, 93 (1988).
L. Schultz, J. Wecker, and E. Hellstern, J. Appl. Phys. 61, 3583 (1987).
P. J. Yvon, R. B. Schwarz, C. B. Pierce, L. Bernardez, A. Connors, and R. Meisenheimer, Phys. Rev. B 39, 6690 (1989).
Powder Diffraction File, Editor-in-Chief William Frank McClune (International Center for Diffraction Data, Swarthmore, PA, 1988).
D. J. Chakrabarti and D. E. Laughlin, Bull. Alloy Phase Diagrams 2, 315 (1981).
K. Jansson and M. Nygren, J. Less-Common Metals 128, 319 (1987).
L. Schultz, Mater. Sci. Eng. 97, 15 (1988).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Batalla, E., Zwartz, E.G. Preparation of Cu–Y–Ba alloys by mechanical alloying. Journal of Materials Research 5, 1802–1805 (1990). https://doi.org/10.1557/JMR.1990.1802
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1990.1802