Abstract
In order to obtain essential information on the formation process of the high-Tc phase in the Bi, Pb-Sr-Ca-Cu-O system, phase equilibria in the system PbO-CaO-CuO have been studied, mainly by x-ray diffraction analysis and thermal analysis. Temperature versus composition diagrams were established for the systems PbO-CuO(Cu2O) and PbO(PbO2)–CaO in air. Three invariant points were detected in these systems: a eutectic reaction (PbO + Ca2PbO4 = L) at 847 ± 6°C, a peritectic reaction (Ca2PbO4 = L + CaO) at 980 ± 2°C, and a eutectic reaction (PbO + CuO = L) at 789 ± 3°C. For the system PbO(PbO2)-CaO-CuO, subsolidus phase equilibrium in air was established. The liquidus was also examined at 780, 800, and 820°C, and a ternary (PbO-Ca2PbO4-CuO) eutectic point was detected at 772 ± 6°C.
Similar content being viewed by others
References
M. Takano, J. Takada, K. Oda, H. Kitaguchi, Y. Miura, Y. Ikeda, Y. Tomii, and H. Mazaki, Jpn. J. Appl. Phys. 27, L1041 (1988).
Y. Ikeda, M. Takano, Z. Hiroi, K. Oda, H. Kitaguchi, J. Takada, Y. Miura, Y. Takeda, O. Yamamoto, and H. Mazaki, Jpn. J. Appl. Phys. 27, L2067 (1988).
K. Oda, H. Kitaguchi, J. Takada, A. Osaka, Y. Miura, Y. Ikeda, M. Takano, Y. Bando, N. Yamamoto, Y. Oka, Y. Tomii, T. Unezaki, Y. Takeda, and H. Mazaki, J. Jpn. Soc. Powder and Powder Metallurgy 35, 424 (1988) (in Japanese).
J. Takada, H. Kitaguchi, K. Oda, A. Osaka, Y. Miura, Y Ikeda, M. Takano, Y. Oka, N. Yamamoto, Y. Tomii, and Y. Takeda, J. Jpn. Soc. Powder and Powder Metallurgy 35, 1003 (1988) (in Japanese).
Y. Ikeda, H. Ito, Z. Hiroi, M. Takano, H. Kitaguchi, J. Takada, K. Oda, Y Miura, Y. Takeda, and H. Mazaki, J. Jpn. Soc. Powder and Powder Metallurgy 35, 965 (1988) (in Japanese).
T. Hatano, K. Aota, S. Ikeda, K. Nakamura, and K. Ogawa, Jpn. J. Appl. Phys. 27, L2055 (1988).
N. Kijima, H. Endo, J. Tsuchiya, A. Sumiyama, M. Mizuno, and Y. Oguri, Jpn. J. Appl. Phys. 27, L1852 (1988).
T. Uzumaki, K. Yamanaka, N. Kamehara, and K. Niwa, Jpn. J. Appl. Phys. 28, L75 (1989).
P. Conflant, J. C. Boibin, and D. Thomas, J. Solid State Chem. 18, 133 (1976).
J. Cassedanne and C. P. Campelo, An. Acad. Brasil. Cienc. 38, 35 (1966).
R. M. Biefield and S. S. White, J. Am. Ceram. Soc. 64, 182 (1981).
U. Kuxmann and P. Fischer, Erzmetall 27, 533 (1974).
Cl. Levy-Clement and A. Michel, Ann. Chim. 2, 63 (1975).
Cl. Levy-Clement, I. Morgenstern-Badarau, and A. Michel, Mater. Res. Bull. 7, 35 (1972).
E. Gebhardt and W. Obrowski, Z. Metallkd. 45, 332 (1954).
A. M. M. Gadalla and J. White, Trans. Brit. Ceram. Soc. 65, 181 (1966).
C. L. Teske and H-K. Miiller-Buschbaum, Z. Anorg. Allg. Chem. 379, 234 (1970).
Y. Ikeda, Y. Oue, K. Inaba, Y. Bando, and M. Takano, J. Jpn. Soc. Powder and Powder Metallurgy 35, 405 (1988) (in Japanese).
Y. Ikeda, H. Ito, S. Shimomura, Y. Oue, K. Inaba, Z. Hiroi, and M. Takano, Physica C 159, 93 (1989).
J. Takada, M. Ohno, H. Kitaguchi, K. Oda, A. Osaka, Y. Miura, Y. Ikeda, M. Takano, and Y. Bando, J. Jpn. Soc. Powder and Powder Metallurgy 35, 952 (1988) (in Japanese).
J. Takada, H. Kitaguchi, H. Kuniya, K. Sato, K. Oda, A. Osaka, Y. Miura, Y. Ikeda, M. Takano, Y. Bando, R. Kanno, and Y. Takeda, J. Jpn. Soc. Powder and Powder Metallurgy 36, 533 (1989) (in Japanese).
C. L. Teske and H-K. Miiller-Buschbaum, Z. Anorg. Allg. Chem. 370, 134 (1969).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kitaguchi, H., Takada, J., Oda, K. et al. Equilibrium phase diagram for the system PbO-CaO-CuO. Journal of Materials Research 5, 929–931 (1990). https://doi.org/10.1557/JMR.1990.0929
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1990.0929