Fouling and corrosion of bed nozzles in a bubbling fluidized-bed power boiler

  • R. Prescott
  • J. R. Kish
  • D. L. Singbeil
Peer Reviewed Articles

Abstract

An inspection of the floor in a bubbling fluidized-bed power boiler during a planned shutdown revealed significant corrosion of the type 310H stainless steel (UNS S31009) bed nozzles. One severely corroded bed nozzle was removed, along with samples of the deposit encasing the surface of the bed nozzle, for a subsequent failure analysis. The deposit covering the external (fireside) surface of the bed nozzle was almost entirely sodium and potassium chlorides, which covered a thick layer of corrosion product on the bed nozzle surface. The corrosion product was predominantly oxides of chromium, nickel, and iron. Chlorides were also found interspersed through the layer of corrosion product. It is concluded that the fireside corrosion was predominantly caused by chlorine-containing compounds (active oxidation). Overheating induced by the fouling, particularly within the air holes, is believed to be a major factor influencing corrosion.

Keywords

active oxidation bed nozzle corrosion fluidized bed fouling power boiler sodium chloride stainless steel sulfur dioxide 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    R.J. Bishop: “The Formation of Alkali-Rich Deposits by a High-Chlorine Coal,” J. Inst. Fuel, 1968, 41, p. 51.Google Scholar
  2. 2.
    R.J. Bishop and K.F. Cliffe: “Condensation Behaviour of Sodium Chloride during Convective Heat Transfer,” J. Inst. Fuel, 1970, 43, p. 441.Google Scholar
  3. 3.
    D.W. McKee, D.A. Shores, and K.L. Lurthra: “The Effects of SO2 and NaCl on High Temperature Hot Corrosion,” J. Electrochem. Soc., 1978, 125(3), p. 411.CrossRefGoogle Scholar
  4. 4.
    K. Iisa, Y. Lu, and K. Samenoja: “Sulfation of Potassium Chloride at Combustion Conditions,” Energy Fuels, 1999, 13(6), p. 1184.CrossRefGoogle Scholar
  5. 5.
    M. Orjala, R. Ingalsuo, K. Paakkinen, J. Hämäläinen, M. Mäkipää, M. Oksa, T. Malkow, R.J. Fordham, and D. Baxter: “How to Control Superheater Tube Corrosion in FB Boilers Which Use Wood and Wood Waste as Fuel,” Proceedings of the Tenth International Symposium on Corrosion in the Pulp and Paper Industry, vol. 1, T. Hakkarainen, ed., VTT, Espoo, Finland, 2001, p. 117.Google Scholar
  6. 6.
    H.J. Grabke, E. Reese, and M. Spiegel: “The Effects of Chlorine, Hydrogen Chloride and Sulphur Dioxide in the Oxidation of Steels below Deposits,” Corros. Sci., 1995, 37, p. 1023.CrossRefGoogle Scholar
  7. 7.
    Y. Shinata, F. Takahashi, and K. Hashiura: “NaCl-Induced Hot Corrosion of Stainless Steels,” Mater. Sci. Eng., 1987, 87, p. 399.CrossRefGoogle Scholar
  8. 8.
    A.J.B. Cutler, W.D. Halstead, J.W. Laxton, and C.G. Stevens: “The Role of Chloride in the Corrosion Caused by Flue Gas and Their Deposits,” J. Eng. Power (Trans. ASME), 1971, 93(7), p. 307.Google Scholar
  9. 9.
    N. Hiramatsu, Y. Uematsu, T. Tanaka, and M. Kinugasa: “Effects of Alloying Elements on NaCl-Induced Hot Corrosion of Stainless Steels,” Mater. Sci. Eng., 1989, A120, p. 319.Google Scholar

Copyright information

© ASM International 2006

Authors and Affiliations

  • R. Prescott
    • 1
  • J. R. Kish
    • 2
  • D. L. Singbeil
    • 2
  1. 1.School of MaterialsUniversity of ManchesterManchesterU.K.
  2. 2.PapricanVancouverCanada

Personalised recommendations