One factor that affects the suitability of tungsten carbide (WC) coatings for wear and corrosion control applications is the fatigue life of the coated part. Coatings, whether anodized or thermal spray coated, can reduce the fatigue life of a part compared to an uncoated part. This study compares the fatigue life of uncoated and thermal spray coated 6061 Al specimens. The relation between the residual stress level in the coating and the fatigue life of the specimen is investigated.
Cyclic bending tests were performed on flat, cantilever beam specimens. Applied loads placed the coating in tension. Residual stress levels for each of the coating types were determined experimentally using the modified layer removal method.
Test results show that the fatigue life of WC coated specimens is directly related to the level of compressive residual stress in the coating. In some cases, the fatigue life can be increased by a factor of 35 by increasing the compressive residual stress in the coating.
Similar content being viewed by others
References
J.M. Quets, “High Cycle Fatigue Properties of Chrome Plated 7075-T73 Aluminum and 4340 Steel,” Union Carbide, Technical Note No. 91-03, 1991
R.W. Landgraf and R.A. Chernenkoff, Residual Stress Effects on Fatigue of Surface Processed Steels, Analytical and Experimental Methods for Residual Stress Effects in Fatigue, STP 1004, ASTM, 1988, p 1–12
S.K. Koh and R.I. Stephens, Mean Stress Effects on Low Cycle Fatigue for a High Strength Steel, Fatigue Fract. Eng. Mater. Struct., Vol 14 (No. 4), 1991, p 413–428
D.J. Greving, E.F. Rybicki, and J.R. Shadley, Through-Thickness Residual Stress Evaluations for Several Industrial Thermal Spray Coatings Using a Modified Layer-Removal Method, J. Therm. Spray Technol., Vol 3 (No. 4), 1994, p 379–388
E.F. Rybicki, J.R. Shadley, Y. Xiong, and D.J. Greving, A Cantilever Beam Method for Evaluating Young’s Modulus and Poisson’s Ratio of Thermal Spray Coatings, J. Therm. Spray Technol., Vol 4 (No. 4), 1995, p 377–383
Y. Xiong, “A Cantilever Beam Method for Evaluating Young’s Modulus and Poisson’s Ratio of Thermal Spray Coatings,” Master of Science thesis, The University of Tulsa, 1994
R.T.R. McGrann, J.R. Shadley, E.F. Rybicki, B.E. Bodger, and W.A. Emery, Thermal Spray Coatings for Aircraft Landing Gear Components, Proc. of the AESF 1998 Aerospace/Airline Plating Forum, p 39–46
D.J. Greving, “Residual Stress and Thermal Spray Coating Performance,” Ph.D. dissertation, The University of Tulsa, 1995
ASM, Vol 1, Metals Handbook, 8th ed., American Society for Metals, 1961, p 946
F.P. Beer and E.R. Johnston, Jr., Mechanics of Materials, 2nd ed., p 204–207
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
McGrann, R.T.R., Greving, D.J., Shadley, J.R. et al. The effect of residual stress in HVOF tungsten carbide coatings on the fatigue life in bending of thermal spray coated aluminum. J Therm Spray Tech 7, 546–552 (1998). https://doi.org/10.1361/105996398770350774
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1361/105996398770350774