Abstract
The Bi-Pd and Ni-Bi binary phase equilibria at 235 °C were investigated. It was concluded that Bi2Pd, BiPd, Bi3Pd5, and BiPd3 are stable intermetallics in the Bi-Pd system and NiBi and NiBi3 are stable in the Ni-Bi system at this temperature. An isothermal cross section of the ternary Ni-Bi-Pd system at the same temperature was established experimentally. No ternary compound has been found. However, the Pd-rich corner of the phase diagram cannot be determined due to the sluggishness of the kinetics involved.
Similar content being viewed by others
References
P. Feschotte and J.-M. Rosset: J. Less-Common Met., 1988, vol. 143, pp. 31–37.
Binary Phase Diagrams, T.B. Massalski, J.I. Murray, L.H. Bennett, and H. Baker, eds., Metals Park, OH, 1986.
D.C. Abbott, R.M. Brook, N. McLelland, and J.S. Wiley: IEEE Trans. CMTH 14, 1991, p. 567.
V.I. Dybkov and O.V. Duchenko: J. Alloy Compounds, 1996, vol. 234, p. 297.
I. Oomen: Graduation Report, Technical University of Eindhoven, 1997, pp. 44–50.
R. Brandt, S. Knarren, G. Manders, M. Meuwissen, C. Moonemans, and B. Tilborghs: “Lead-Free Solders for Electronic Applications,” Internal Report, MDP Group “Lead-Free Soldering,” Technical University of Eindhoven, Eindhoven, The Netherlands, 1999.
G. Ghosh: J. Electron. Mater., 99, vol. 28 (11), p. 1238.
M. Mathon, M. Gambino, E. Hayer, M. Gaune-Escard, and J.P. Bros: J. Alloys. Compounds, 1999, vol. 285, p. 123.
H. Tanaka, M. Tanimoto, A. Matsuda, T. Uno, M. Kurihara, and S. Shiga: J. Electron. Mater., 1999, vol. 28 (11), p. 1216.
P.J.T.L. Oberndorff, M.G.A. van Vinken, A.A. Kodentsov, and F.J.J. van Loo: Proc. DIMAT 2000, Paris, 2000.
W. Peng, K. Zeng, and J. Kivilahti: “Formation of Intermetallic Compounds in Solder Joints and Its Effect on Joint Reliability,” Report HUT-EPT-2, Helsinki University of Technology, Helsinki, Finland, 2000.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Oberndorff, P.J.T.L., van Vinken, M.G.A., Kodentsov, A.A. et al. Phase relations in the Bi-Ni-Pd system at 235 °C. JPE 22, 265–268 (2001). https://doi.org/10.1361/105497101770338752
Received:
Issue Date:
DOI: https://doi.org/10.1361/105497101770338752