Microstructural analysis of the brass seat of a valve from the 1907 steam tug “Hercules”

  • C. R. Brooks
  • D. Monday
Peer Reviewed Articles
  • 71 Downloads

Abstract

The steam tug Hercules was an ocean-going and bay tug for 55 years before being retired. It is now being restored by the National Park Service (as of 1993 printing of this article). A broken steam valve was obtained for microstructural examination. The body was gray cast iron, and the stem and seat were brass. The examination centered on corrosion of the brass components. The seat and shaft were α brass, with a hardness of 64 and 79 DPH, respectively. A nut held the shaft onto the seat and was α-β brass with a hardness of 197 DPH. Welded on the end of the shaft was a ring of hard (DPH 294) α-β brass, which seated against the nut. The brass seat and stem showed little corrosion. However, the α-β brass nut and welded tip show extensive dezincification. This process of removal of Zn and the retention of Cu began in the high Zn β phase, but eventually both phases were attacked. The depth of penetration was consistent with dezincification rates reported in the literature for such brasses in salt water if the valve had been in service about 55 years.

Keywords

brass alloy dezincification failure analysis gate valve gray cast iron naval brass steam valve 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    “The Steam Tug Hercules,” pamphlet, National Maritime Museum, San Francisco, CA, 1991Google Scholar
  2. 2.
    G.F. Vander Voort, Metallographic Laboratory Practices, McGraw-Hill, New York, 1986Google Scholar
  3. 3.
    F.W. Fink and W.K. Boyd, “The Corrosion of Metals in Marine Environments,” Report 245, Defense Metals Information Center, Battelle, Columbus, OH, 1970Google Scholar
  4. 4.
    H. Leidheiser, The Corrosion of Copper, Tin, and Their Alloys, Wiley, New York, 1971Google Scholar
  5. 5.
    Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, Vol 2, 10th ed., Metals Handbook, ASM International, Materials Park, OH, 1990Google Scholar
  6. 6.
    Corrosion, Vol 13, 9th ed., Metals Handbook, ASM International, 1987, p 614Google Scholar
  7. 7.
    C.R. Brooks, Heat Treatment, Structure and Properties of Non-Ferrous Alloys, American Society for Metals, Metals Park, OH, 1982Google Scholar
  8. 8.
    D.A. Jones, Principles and Prevention of Corrosion, Macmillan Publishing, New York, 1992Google Scholar
  9. 9.
    R. Steigerwald, Metallurgically Influenced Corrosion, Corrosion, Vol 13, 9th ed., Metals Handbook, ASM International, Materials Park, OH, 1987, p 131Google Scholar
  10. 10.
    U.R. Evans, An Introduction to Metallic Corrosion, 3rd ed., American Society for Metals, Metals, Park, OH, 1981Google Scholar
  11. 11.
    H.H. Uhlig, Corrosion and Corrosion Control; An Introduction to Corrosion Science and Engineering, Wiley, New York, 1971Google Scholar
  12. 12.
    M.G. Fontana, Corrosion Engineering, McGraw-Hill, New York, 1978Google Scholar
  13. 13.
    C.W. Hummer, Jr., The Corrosion of Metals in Tropical Environments—Copper and Wrought Copper Alloys, Mater. Prot., Vol 7, 1968, p 41Google Scholar

Copyright information

© ASM International 2004

Authors and Affiliations

  • C. R. Brooks
  • D. Monday

There are no affiliations available

Personalised recommendations