X-Ray Powder Diffraction Rietveld Characterization of Synthetic Aluminum-Substituted Goethite

  • P. G. Fazey
  • B. H. O’Connor
  • L. C. Hammond
Article

Abstract

Riet veld X-ray powder diffraction (XRD) analysis has been evaluated as a procedure for characterizing Al-substituted goethite according to the Rietveld scale factor, unit-cell parameters, and atom positional parameters. The study was conducted with three synthetic goethite samples for which the degree of Al substitution for Fe determined by chemical analysis was 8.0 ± 0.4, 12.0 ± 0.4, and 20.1 ± 0.4 mole %. The weight fractions of crystalline material (WFCM) in the specimens, determined from the Rietveld scale factors after correcting for adsorbed water and impurities, were 0.878 (esd = 0.014), 0.919 (0.014), and 0.965 (0.015), respectively. The Al mole % substitutions, inferred from the Rietveld cell parameters according to the method of Schulze (1984), were 10.4 ± 2.5, 16.5 ± 2.6, and 17.1 ± 2.6, respectively. The cause of the significant difference between the second value and the chemical analysis result is not known. The atom positional parameters did not differ significantly within the sample suite and agreed satisfactorily with literature values. The results have demonstrated the value of using Rietveld XRD analysis to determine simultaneously the WFCM and Al mole % substitutions, as well as to confirm the non-hydrogen atom positions.

Key Words

Aluminum Crystallinity Goethite Rietveld refinement X-ray powder diffraction 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. Bish, D. L. and Howard S. A. (1988) Quantitative phase analysis using the Rietveld method: J. Appl. Crystallogr. 21, 86–91.CrossRefGoogle Scholar
  2. Busing, W. R. and Levy, H.A. (1958) A single crystal neuron diffraction study of diaspore, AlO(OH): Acta Crystallogr. 11, 798–803.CrossRefGoogle Scholar
  3. Cambier, P. (1986) Infrared study of goethites of varying crystallinity and particle size: II. Crystallographic and morphological changes in series of synthetic goethites: Clay Miner. 21, 201–210.CrossRefGoogle Scholar
  4. Cornell, R. M., Mann, S., and Skarnulis, A. J. (1983) A high resolution electron microscopy examination of domain boundaries in crystals of synthetic goethite: J. Chem. Soc. Faraday Trans. 1 79, 2679–2684.CrossRefGoogle Scholar
  5. Dollase, W. A. (1986) Correction of intensities for preferred orientation in powder diffractometry: Application of the March model: J. Appl. Crystallogr. 19, 267–272.CrossRefGoogle Scholar
  6. Forsyth, J. B., Hedley, I. G., and Johnson, C. E. (1968) The magnetic structure and hyperfine field of goethite (α-Fe-OOH): Proc. Phys. Soc. London, sect. C 1, 179–188.Google Scholar
  7. Golden, D. C. (1978) Physical and chemical properties of aluminum-substituted goethite: Ph.D. thesis, North Carolina State University, Raleigh, North Carolina, 74 pp. (University Microfilms Inc., 78/20029).Google Scholar
  8. Hill, R. J. (1979) Crystal structure refinement and electron density distribution in diaspore: Phys. Chem. Minerals 5, 179–200.CrossRefGoogle Scholar
  9. Hill, R. J. and Howard, C. J. (1986) A computer program for Rietveld analysis of fixed wavelength X-ray and neutron powder diffraction patterns: Version LHPM1: Australian Atomic Energy Commission Research Establishment, Lucas Heights, New South Wales, Australia.Google Scholar
  10. Hill, R. J. and Howard, C. J. (1987) Quantitative phase analysis from neutron powder diffraction data using the Rietveld method: J. Appl. Crystallogr. 20, 467–474.CrossRefGoogle Scholar
  11. Hubbell, J. H., McMaster, W. H., Del Grande, N. K., and Mallett, J. H. (1974) International Tables for X-ray Crystallography (1974), Vol. IV: Kynoch Press, Birmingham, United Kingdom, 47–70.Google Scholar
  12. Jordan, B., O’Connor, B. H., and Li Dey. (1990) Use of Rietveld pattern-fitting to determine the weight fraction of crystalline material in natural low-quartz specimens: Powder Diffraction 5, 64–69.CrossRefGoogle Scholar
  13. Klug, A. and Farkas, L. (1981) Structural investigations of polycrystalline diaspore samples by X-ray powder diffraction: Phys. Chem. Minerals 7, 138–140.CrossRefGoogle Scholar
  14. March, A. (1932) Mathematische Theorie der Regelung nach der Korngestalt bei affiner Deformation: Zeit. Kristallogr. 81, 285–297.Google Scholar
  15. Megaw, H. D. (1973) Crystal Structures—A Working Approach: W. B. Sanders Co., Philadelphia, 356–359.Google Scholar
  16. O’Connor, B. H. and Raven M. D. (1988) Application of the Rietveld refinement procedure in assaying powdered mixtures: Powder Diffraction 3, 2–6.CrossRefGoogle Scholar
  17. Reynolds, R. C. (1968) Effect of particle size on apparent lattice spacings: Acta Crystallogr. A24, 319–320.CrossRefGoogle Scholar
  18. Reitveld, H. M. (1969) A profile refinement method for nuclear and magnetic structures: J. Appl. Crystallogr. 2, 65–71.CrossRefGoogle Scholar
  19. Schulze, D. G. (1984) The influence of aluminum on iron oxides, VIII. Unit-cell dimensions of Al-substituted goethites and estimation of Al from them: Clays & Clay Minerals 32, 36–44.CrossRefGoogle Scholar
  20. Schulze, D. G. and Schwertmann, U. (1987) The influence of aluminum on iron oxides: XIII. Properties of goethites synthesised in 0.3 M KOH at 25°: Clay Miner. 22, 83–92.CrossRefGoogle Scholar
  21. Shannon, R. D. and Prewitt, C. T. (1969) Effective ionic radii in oxides and fluorides: Acta Crystallogr. B25, 925–946.CrossRefGoogle Scholar
  22. Trunz, V. (1976) Influence of crystallite size on the apparent basal spacings of kaolinite: Clays & Clay Minerals 24, 84–87.CrossRefGoogle Scholar
  23. Wiles, D. B. and Young, R. A. (1981) A new computer program for Rietveld analysis of X-ray powder diffraction patterns: J. Appl. Crystallogr. 14, 149–151.CrossRefGoogle Scholar

Copyright information

© The Clay Minerals Society 1991

Authors and Affiliations

  • P. G. Fazey
    • 1
  • B. H. O’Connor
    • 1
  • L. C. Hammond
    • 1
  1. 1.Department of Applied PhysicsCurtin University of TechnologyBentleyAustralia

Personalised recommendations