The Influence of Aluminum on the Formation of Iron Oxides. IV. The Influence of [Al], [OH], and Temperature

  • D. G. Lewis
  • U. Schwertmann
Article

Abstract

Ferrihydrite was transformed to goethite and/or hematite at various temperatures, [OH], and [Al]. Increasing temperature and [Al] favored hematite, increasing [OH] favored goethite. A given [Al] induces hematite more effectively at lower [OH]. Al substitution in goethites increased linearly with log[Al], but was independent of temperature. At a given [Al], substitution increased with decreasing [OH]. In a plot of Al/Fe in the goethite against [Al]/[Fe(OH)4] in solution a straight line was obtained for all preparations independent of [OH].

Key Words

Aluminum Ferrihydrite Goethite Hematite Iron oxides 

Резюме

Ферригидрит был преобразован в гетит и/или гематит при разных температурах, [Аl] и [ОН]. Повышение температуры и [Аl] благоприятствует гематиту, а повышенное [ОН] благоприятно для гетита. При данном [Аl] образование гематита происходит эффективно при низком [ОН]. Замещение Аl в гетите возрастало линейно с log[Al], но не зависело от температуры. При данном [Аl] замещение возрастало с убыванием [ОН]. На графике соотношения Al/Fe в гетите и [Al]/[Fe(OH)4] в растворе была получена прямая линия для всех препаратов независимо от [ОН].

Resümee

Ferrihydrit wurde bei verschiedener Temperatur, [OH], und [Al] in Goethit und/oder Hämatit umgewandelt. Hämatit wurde durch steigende Temperatur und [Al], Goethit durch steigendes [OH] gefördert. Bei gegebenem [Al] wird Hämatit daher umso stärker gefördert, je niedriger [OH] ist. Der isomorphe Al-Ersatz in Goethit steigt linear mit log [Al] und war unabhängig von der Temperatur. Bei gegebenem [Al] steigt der Ersatz mit abnehmendem [OH], Bei Auftragung von Al/Fe in Goethit gegen [Al]/[Fe(OH)4] in der Lösung ergibt sich eine Gerade für alle Produkte unabhängig von [OH].

Résumé

De la ferrihydrite a été transformée en goethite et/ou en hématite à des températures, [OH], et [Al] variés. Une augmentation de température et de [Al] a favorisé l’hématite, une augmentation d’ [OH] a favorisé la goethite. Un [Al] donné induit l’hématite plus effectivement à un bas [OH], La substitution d’Al dans les goethites a augmenté linéairement avec log [Al], mais était indépendant de la température. A un [Al] donné, la substitution a augmenté avec la diminution d’ [OH]. Dans un graphe représentant Al/Fe dans la goethite par rapport à [Al]/[Fe(OH)4] en solution, une droite a été obtenue pour toutes les préparations indépendantes d’ [OH].

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. Fischer, W. R. and Schwertmann, U. (1975) The formation of hematite from amorphous Fe(III)hydroxide: Clays & Clay Minerals 23, 33–37.CrossRefGoogle Scholar
  2. Gastuche, M. C., Bruggenwert, T., and Mortland, M. M. (1964) Crystallization of mixed iron and aluminum gels: Soil Sei. 98, 281–289.CrossRefGoogle Scholar
  3. Lengweiler, H., Buser, W., and Feitknecht, W. (1961) Die Ermittlung der Löslichkeit von Eisen(III)-hydroxiden mit 59Fe. I. Fällungs- und Auflösungsversuche: Helv. Chim. Acta 44, 796–805.CrossRefGoogle Scholar
  4. Lewis, D. G. and Schwertmann, U. (1979) The influence of Al on the formation of iron oxides. Part III. Preparation of Al goethites in M KOH: submitted to Clay Minerals.Google Scholar
  5. Schwertmann, U. (1964) Differenzierung der Eisenoxide des Bodens durch photochemische Extraktion mit saurer Ammoniumoxalat-Lösung: Z. Pflanzenernaehr. Dueng. Bodenkd. 105, 194–202.CrossRefGoogle Scholar
  6. Schwertmann, U. and Taylor, R. M. (1972) The influence of silicate on the transformation of lepidocrocite to goethite: Clays & Clay Minerals 20, 159–164.CrossRefGoogle Scholar
  7. Schwertmann, U., Fitzpatrick, R. W., and Le Roux, J. (1977) Al substitution and differential disorder in soil hematites: Clays & Clay Minerals 25, 373–374.CrossRefGoogle Scholar
  8. Schwertmann, U., Fitzpatrick, R. W., Taylor, R. M., and Lewis, D. G. (1979) The influence of aluminum on iron oxides. Part II. Preparation and properties of Al-substituted hematites: Clays & Clay Minerals 27, 105–112.CrossRefGoogle Scholar
  9. Vegard, L. (1921) Die Konstitution der Mischkristalle und die Raumerfüllung der Atome: Z. Phys. 5, 17–29.CrossRefGoogle Scholar
  10. Wolska, E. (1976) Über die Koexistenz der Aluminium-und Eisen(III)-hydroxide und Oxide: Monatsh. Chem. 107, 349–357.CrossRefGoogle Scholar

Copyright information

© The Clay Minerals Society 1979

Authors and Affiliations

  • D. G. Lewis
    • 1
    • 2
  • U. Schwertmann
    • 1
  1. 1.Institut für BodenkundeTechnische Universität MünchenFreising-WeihenstephanBRD
  2. 2.Department of Soil Science, Waite Agricultural Research InstituteUniversity of AdelaideGlen OsmondAustralia

Personalised recommendations